High heat resistance low density high performance auto polypropylene composite and preparation method thereof

A polypropylene composition and low-density technology, which is applied in the field of high-heat-resistant and low-density high-performance polypropylene composition and its preparation, can solve the problems of incompatibility of high heat resistance and high toughness, achieve excellent comprehensive performance, reduce Emissions, Density Reduction Effects

Active Publication Date: 2011-05-25
KINGFA SCI & TECH CO LTD +2
View PDF13 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] The purpose of the present invention is to overcome the disadvantages of high heat resistance and high toughness of polypropylene materials for vehicles, and to provide a high heat resistance low density high performance polypropylene composition

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High heat resistance low density high performance auto polypropylene composite and preparation method thereof
  • High heat resistance low density high performance auto polypropylene composite and preparation method thereof
  • High heat resistance low density high performance auto polypropylene composite and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0065] Table 1 Formula content

[0066] components

Example 1

Comparative example 1

Comparative example 2

Comparative example 3

PP

84.5%

85%

84.5%

84.5%

POE

5%

5%

5%

5%

Al 2 o 3 whiskers

5%

5%

10%

-

coupling agent

0.5%

-

0.5%

0.5%

talcum powder

5%

5%

-

10%

[0067] Put the above raw materials into a high-speed mixer with a rotation speed of about 1000rpm and mix them according to the weight percentage, and then put them into a twin-screw extruder. Get granulated. Wherein the coupling agent used is the mixture of epoxy resin, hydrogenated butadiene and monoglyceride, 50% by weight of epoxy resin, 25% by weight of hydrogenated butadiene, and 25% by weight of monoglyceride.

[0068] The properties of the prepared samples are as follows:

[0069] Table 2 Performance table

[0070]

[0071] Comparing Example 1 and Comparative Example 2 from Table 2...

Embodiment 2~ Embodiment 5

[0074] Table 3 Formula content

[0075] components

Example 2

Example 3

Example 4

Example 5

Comparative example 4

PP

64%

64%

65%

58%

58%

POE

15%

15%

10%

15%

10%

Al 2 o 3 whiskers

3%

10%

13%

15%

-

coupling agent

1%

1%

2%

2%

2%

talcum powder

17%

10%

10%

15%

30%

[0076] Put the above raw materials into a high-speed mixer with a rotation speed of about 1000rpm and mix for 3 minutes. See Example 1 for the extrusion granulation process. Wherein the coupling agent used is the mixture of epoxy resin, hydrogenated butadiene and monoglyceride, 30% by weight of epoxy resin, 40% by weight of hydrogenated butadiene, and 30% by weight of monoglyceride.

[0077] The properties of the prepared samples are as follows:

[0078] Table 4 Performance table

[0079]

[0080] Comparing Examples 2 to 5, it is found that the compounded talcum powde...

Embodiment 6~ Embodiment 9

[0082] Table 5 Formula content

[0083] components

Example 6

Example 7

Example 8

Example 9

PP

64%

64%

64%

64%

POE

15%

15%

15%

15%

Al 2 o 3 whiskers

3%

5%

8%

-

ZnO whiskers

-

-

-

10%

talcum powder

17%

15%

12%

10%

coupling agent

1%

1%

1%

1%

[0084] Put the above raw materials into a high-speed mixer with a rotation speed of about 1000rpm and mix for 3 minutes. See Example 1 for the extrusion granulation process. Wherein the coupling agent used is the mixture of epoxy resin, hydrogenated butadiene and monoglyceride, 50% by weight of epoxy resin, 25% by weight of hydrogenated butadiene, and 25% by weight of monoglyceride.

[0085] The properties of the prepared samples are as follows:

[0086] Table 6 Performance table

[0087]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high heat resistance low density high performance auto polypropylene composite and a preparation method thereof. The polypropylene composite comprises the following components in percentage by weight: 50 to 84.5 percent of PP, 5 to 20 percent of flexibilizer, 5 to 15 percent of crystal whisker, 5 to 15 percent of talcpowder, and 0.5 to 2 percent of coupling agent. The preparation method comprises the following steps of: pre-mixing the components of PP and crystal whisker in a high speed mixer; transporting the mixed raw material into a twin screw extruder; and feeding material at the crystal whisker side into the twin screw extruder and performing fusion, extrusion and granulation to obtain the product. The product is characterized in high heat resistance, low density and high performance, and does not produce environmental pollution during manufacturing and use, thereby reducing the pressure on sewage treatment, and reducing energy consumption. Moreover, the composite neither produces the migration of toxic substance nor contains heavy metals. And the product completely meets the ROSH standard.

Description

technical field [0001] The invention belongs to the technical field of modified materials, and in particular relates to a high-heat-resistant, low-density, high-performance polypropylene composition and a preparation method thereof. Background technique [0002] Plastic plays an irreplaceable role for other materials in terms of car aesthetics, comfort, safety, anti-corrosion, light weight and large design freedom. Among the many plastic varieties used in automobiles, the development and application of modified PP materials in automobiles has always been the focus of attention of the automobile industry and the plastics industry. Modified PP materials that meet the different functional requirements of various automotive parts can be obtained through various modification processing methods. In addition to its excellent cost performance, various toughened, filled and reinforced PP materials have been obtained in the major assembly systems of automobiles. widely used. With pe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/14C08L63/00C08K13/04C08K7/08C08K3/34C08K5/01C08K5/103B29B9/06B29C47/92B29C48/92
CPCB29C48/04B29C48/40B29C48/92B29C2948/9259B29C2948/92704B29C2948/92885B29C2948/92895
Inventor 杨燕李永华罗忠富王灿耀陈瑶杨波黄达
Owner KINGFA SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap