Spectrum generator, preparation method thereof and preparation method of far-infrared radiant coating

A far-infrared radiation and generator technology, applied in the field of material engineering, can solve the problems of complex structure, complex production process and low radiation rate of spectrum generators, and achieve the effect of simple structure, simple production process and high radiation rate

Active Publication Date: 2011-04-27
GUANGDONG JUNFENG BFS TECH
View PDF0 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a spectrum generator and its preparation method and the preparation method of the far-infrared radiation paint, which solves the problems of complex structure of the existing spectrum generator and the need for the existing far-infrared radiation material to be prepared by high-temperature calcination. Due to the technical problems of complex process defects, poor match between the radiation wavelength and the best absorption wavelength of the human body, and low emissivity, the structure of the spectrum generator is simple, the preparation process of the far-infrared radiation coating is simple, and the radiation wavelength can match the human body. The purpose of the best absorption wavelength and relatively high radiation rate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Spectrum generator, preparation method thereof and preparation method of far-infrared radiant coating
  • Spectrum generator, preparation method thereof and preparation method of far-infrared radiant coating
  • Spectrum generator, preparation method thereof and preparation method of far-infrared radiant coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] The technical solutions of the present invention will be described in further detail below with reference to the accompanying drawings and embodiments.

[0019] figure 1 It is a flow chart of the preparation method of the far-infrared radiation coating of the present invention. Such as figure 1 As shown, the preparation of the far-infrared radiation coating of the present embodiment needs mixed slurry and water-based epoxy film-forming agent, wherein the water-based epoxy film-forming agent includes water-based epoxy film-forming agent A component and water-based epoxy film-forming agent B group Further, the preparation method steps of the far-infrared radiation coating of the present embodiment specifically include:

[0020] Step 11, put the mixed slurry into a stirring ball mill and grind it for 2-4 hours, then put it into an ultra-fine grinding mill and grind it for 1-2 hours to generate a mixed slurry of micro-nano particles. The mixed slurry in this embodiment in...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a spectrum generator, a preparation method thereof and a preparation method of a far-infrared radiant coating. The preparation method of the far-infrared radiant coating comprises the following steps: putting a mixed slurry into a ball-stirring mill, grinding for 2-4 hours, then putting the slurry into an ultra-fine grinding machine, and grinding for 1-2 hours, so as to generate a mixed slurry of micro-nano particles; putting the mixed slurry of micro-nano particles and 12-30% of a component B of a water borne epoxy film-forming agent into a high-function stirrer for mixing, and putting the mixture into a three-roll grinder for kneading 2-3 times, so as to generate a hybrid mixed solution, wherein the component B of the water borne epoxy film-forming agent is a water borne epoxy curing agent; stirring and mixing the generated hybrid mixed solution and 10-25% of a component A of the water borne epoxy film-forming agent thoroughly and uniformly, so as to prepare the far-infrared radiant coating, wherein the component A of the water borne epoxy film-forming agent is epoxy resin or a epoxy resin mixture. By utilizing the method provided by the invention, the aims that the far-infrared radiant coating is prepared with a simple process and the radiant wavelength of the coating matches well with the best absorption wavelength of human body are realized.

Description

technical field [0001] The invention relates to material engineering technology, in particular to a spectrum generator, a preparation method thereof, and a preparation method of far-infrared radiation paint. Background technique [0002] With the continuous improvement of people's living standards, spectrum generators with health care functions are more and more popular. [0003] In the prior art, there is a spectrum generator with a relatively advanced structure, which includes an electrothermal film heating layer, a PET insulating layer is arranged above the electrothermal film heating layer, and a spectrum generating layer is arranged above the PET insulating layer. A protective quilt cover is arranged under the heating layer. However, the spectrum generator with multi-layer structure makes its own manufacturing process relatively complicated. [0004] Furthermore, there is still a typical preparation method of a spectrum generator at present: it uses an insulating mate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D7/12C09D5/00H05B3/20A61N5/06
Inventor 范广宏任明伟赵春英陈险峰陈俊岭
Owner GUANGDONG JUNFENG BFS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products