High-strength aluminum alloy isothermal direction-change open die forging method and device

An aluminum alloy, isothermal forging technology, applied in the field of high-strength aluminum alloy isothermal direction-changing free forging and devices, to achieve the effects of good deformation uniformity, uniform temperature, and uniform billet temperature

Active Publication Date: 2011-11-23
CENT SOUTH UNIV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the deficiencies in the existing high-strength aluminum alloy forging forming process, and provide a high-strength aluminum alloy isothermal direction free forging with simple process method, convenient operation, forging and forming always under isothermal conditions, and good forging structure and performance Method and device

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength aluminum alloy isothermal direction-change open die forging method and device
  • High-strength aluminum alloy isothermal direction-change open die forging method and device
  • High-strength aluminum alloy isothermal direction-change open die forging method and device

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] High-strength aluminum alloy isothermal direction change free forging method:

[0036] The first step: cut the head and tail of the alloy billet with a diameter of 80mm and the grade of 7085, and then use a lathe to flatten the two ends of the alloy billet, and make the two end faces of the alloy billet after the flattening be aligned with the alloy billet The axes are perpendicular to each other to ensure that the pressure direction is parallel to the axis of the alloy billet during upsetting, so as to avoid bending during upsetting, and obtain an alloy billet with a diameter of 70 mm and a length of 110 mm; put the processed billet into a resistance heating furnace Heating to 450°C in medium temperature, holding the temperature for one hour and keeping the furnace temperature constant;

[0037] Step 2: Start the press, upsetting the billet to a height of 60 mm and then elongating it to the original height; repeatedly upsetting and elongating; finally, forging and form...

Embodiment 2

[0049] High-strength aluminum alloy isothermal direction change free forging method:

[0050] The first step: cut the head and tail of the alloy billet with a diameter of 80mm and the grade of 7085, and then use a lathe to flatten the two ends of the alloy billet, and make the two end faces of the alloy billet after the flattening be aligned with the alloy billet The axes are perpendicular to each other to ensure that the pressure direction is parallel to the axis of the alloy billet during upsetting, so as to avoid bending during upsetting, and obtain an alloy billet with a diameter of 70 mm and a length of 110 mm; put the processed billet into a resistance heating furnace Heating to 420°C in medium temperature, holding the temperature for one hour and keeping the furnace temperature constant;

[0051] Step 2: Start the press, upsetting the billet to a height of 40 mm and then elongating it to the original height; repeatedly upsetting and elongating; finally, forging to obtai...

Embodiment 3

[0054] High-strength aluminum alloy isothermal direction change free forging method:

[0055] The first step: cut the head and tail of the alloy billet with a diameter of 80mm and the grade of 7085, and then use a lathe to flatten the two ends of the alloy billet, and make the two end faces of the alloy billet after the flattening be aligned with the alloy billet The axes are perpendicular to each other to ensure that the pressure direction is parallel to the axis of the alloy billet during upsetting, so as to avoid bending during upsetting, and obtain an alloy billet with a diameter of 70 mm and a length of 110 mm; put the processed billet into a resistance heating furnace Heating to 380°C in medium temperature, holding the temperature for one hour and keeping the furnace temperature constant;

[0056] Step 2: Start the press, upsetting the billet to a height of 40 mm and then elongating it to the original height; repeatedly upsetting and elongating; finally, forging to obtai...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-strength aluminum alloy isothermal direction-change open die forging method which comprises the following steps: heating preprocessed high-strength aluminum alloy blank in a direction-change isothermal forging heating holding furnace at the temperature of 350-450 DEG C, and keeping the furnace temperature unchanged; and according to the structure property indices required by the blank, repeatedly upsetting and drawing the blank in the direction-change isothermal forging heating holding furnace until the blank reaches the design size of the forge piece. The isothermal direction-change open die forging device comprises a heating furnace and a forging press, wherein the furnace body is installed on the forging platform of the forging press; the forging rammer of the forging press is installed in a through hole in the furnace bottom plate; and the forging head of the forging press is installed in a through hole in the furnace top plate. The invention has the advantages of simple technique, convenient operation, and low tendency to recrystallization, enables the high-strength aluminum alloy to be under isothermal conditions all through the direction-change open die forging process, does not need to heat the blank again in the forging process, improves the quality of the forge piece and enhances the forging efficiency; and the forge piece has the advantages of sufficient structure deformation, uniform deformation at each part, and low tendency of cracking. The forge piece has favorable structure properties, and is suitable for industrial production.

Description

technical field [0001] The invention discloses a high-strength aluminum alloy isothermal direction-changing free forging method and device, and belongs to the technical field of metallurgical forging techniques. Background technique [0002] Due to the advantages of low density, high specific strength and specific stiffness, high-strength aluminum alloys have been widely used in various industrial sectors. High-strength aluminum alloy forgings have become indispensable mechanical parts in various industrial sectors, but their quality depends largely on the forging process s Choice. When the unidirectional deformation of the billet is small, the refinement of the grain and the second phase is insufficient, which affects the performance improvement of the forging, but when the unidirectional deformation is too large, severe tearing is likely to occur inside and on the surface of the billet and the forging billet is scrapped. In order to increase the total deformation to ensur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B21J3/00B21J1/06B21J17/00
Inventor 陈康华梁信陈送义彭迪陈学海
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com