Fly ash baked brick prepared by washed incineration fly ash of house refuse and preparation method thereof

A technology of domestic waste incineration and sintered bricks, which is applied to the production of clay products, ceramic materials, and the removal of solid waste, etc., to achieve good macro performance, reduce potential hazards, and simple manufacturing processes

Inactive Publication Date: 2012-11-21
SHANGHAI INST OF TECH
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At the same time, since the disposal of fly ash landfills cannot destroy dioxins, and the heavy metals in them cannot be degraded, once leakage occurs, it will cause great harm to society, so there are certain hidden dangers; fly ash landfills cannot be reused after they are closed. use, resulting in a large waste of resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fly ash baked brick prepared by washed incineration fly ash of house refuse and preparation method thereof
  • Fly ash baked brick prepared by washed incineration fly ash of house refuse and preparation method thereof
  • Fly ash baked brick prepared by washed incineration fly ash of house refuse and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] A fly ash sintered brick made by washing domestic waste incineration fly ash, the mass percentage of its raw materials is as follows:

[0048] Domestic waste incineration fly ash after washing 25%

[0049] Clay 60%

[0050] Feldspar 15%

[0051] A kind of fly ash sintered brick made of domestic waste incineration fly ash after washing. The main chemical components (mass percentage) in the washed fly ash, clay and feldspar are shown in Table 4.

[0052] Table 4 Chemical composition of washed fly ash, clay and feldspar (%)

[0053]

[0054] Among them, the washed fly ash is the domestic waste incineration fly ash taken from Shanghai Jiangqiao Domestic Waste Incineration Power Plant after washing;

[0055] Among them, clay is a kind of pottery clay that exists in nature, produced in Dingjiaqiao, Zhejiang;

[0056] Fe in clay 2 o 3 The content of clay is relatively high, and its iron oxide composition makes the finished product appear red. The photo of clay (a) XRD...

Embodiment 2

[0059] A kind of fly ash sintered brick made by washing domestic waste incineration fly ash, the mass percentage of its raw materials is composed of:

[0060] Domestic waste incineration fly ash after washing 30%

[0061] Clay 55%

[0062] Feldspar 15%

[0063] The fly ash sintered brick made of the washed domestic waste incineration fly ash, the main chemical components (mass percentage) in the washed fly ash, clay and feldspar are shown in Table 4 in Example 1.

Embodiment 3

[0065] A fly ash sintered brick made by washing domestic waste incineration fly ash, the mass percentage of its raw materials is as follows:

[0066] Domestic waste incineration fly ash after washing 35%

[0067] Clay 60%

[0068] Feldspar 5%

[0069] The fly ash sintered brick made of the washed domestic waste incineration fly ash, the main chemical components (mass percentage) in the washed fly ash, clay, and feldspar are shown in Table 4 in the examples.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses a fly ash baked brick prepared by washed incineration fly ash of house refuse and a preparation method thereof. The fly ash baked brick consists of 25-35% of washed incineration fly ash of house refuse, 45-70% of clay and 5-20% of feldspar in percentage by weigh. The preparation method comprises seven steps of washing treatment of incineration fly ash of house refuse, pretreatment before crushing materials, material crushing, aging of raw materials, forming of raw materials, green body drying and sintering to form brick. Finally, the fly ash baked brick prepared by washed incineration fly ash of house refuse is obtained. In the invention, the washed incineration fly ash of house refuse is used to prepare the baked brick; by calcining, dioxin in the incineration flyash can be destroyed thoroughly and heavy metals in the fly ash can be cured, thereby achieving the purpose of innocent treatment of incineration fly ash of house refuse and turning the waste into valuable. The manufacturing process of the fly ash baked brick is simple and the fly ash baked brick has good macroscopic properties and can be used for paving roads.

Description

technical field [0001] The invention relates to a method for preparing fly ash sintered bricks made of domestic waste incineration fly ash washed with water. Background technique [0002] With the rapid development of waste incineration technology, the amount of fly ash produced is increasing. Fly ash is a recognized hazard because it contains dioxins (polychlorinated dibenzodioxins, polychlorinated dibenzofurans) and a large amount of heavy metals. Waste, its dioxins and heavy metals are difficult to deal with. However, fly ash contains more silicates and aluminosilicates, which is a useful material and can be used as a resource. The development of sintered bricks with fly ash not only realizes the resource utilization of waste, but also can destroy the dioxins in the fly ash during the calcination process, and the dense structure of the finished product can solidify the heavy metals in the fly ash, so as to achieve the harmlessness of the fly ash It has certain theoreti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B09B3/00C04B33/00C04B33/135
CPCY02P40/60
Inventor 张海英
Owner SHANGHAI INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products