Formula of straw compound real wood imitated wires

A technology of imitating solid wood and formula, which is applied in the field of formula of straw composite solid wood wire, can solve the problems of violating the concept of ecological protection, secondary pollution of the environment, and consumption of trees, and achieve the goals of improving strength, preventing secondary pollution, and prolonging service life. Effect

Inactive Publication Date: 2010-09-29
CHONGQING SHUAIZHIDUN DOOR IND
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Composite imitation solid wood wire is one of the building materials widely used in modern home decoration and construction engineering. As a result, the current extensive market demand leads to a large demand for wood chips, resulting in the annual consumption of a large number of trees, causing great damage to vegetation, which violates the current concept of ecological protection
At the same time, most of the existing formulas contain toxic and harmful substances such as formaldehyde, causing secondary pollution to the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Embodiment 1. The formula for taking materials is: 5 kg of straw with a particle size of 80 mesh, 20 kg of limestone with a particle size of 150 mesh, 20 kg of PVC resin, 0.1 kg of polyethylene wax, 1.0 kg of composite lead salt stabilizer, 0.2 kg of AC foaming agent, and 0.05 kg of paraffin wax. kg, pour the above-mentioned material into the mixer and mix it well, then pour the mixture into the hopper of the extruder, form it through the high-temperature hard mold of the extruder, pass the blank out of the extruder through the vacuum setting mold, and then enter the traction , followed by soaking in cold water to set the shape, and finally vacuum dehumidification to complete the manufacture of the straw composite imitation solid wood wire of the present invention.

Embodiment 2

[0013] Embodiment 2. The formula for taking materials is: 6 kg of straw with a particle size of 200 mesh, 25 kg of limestone with a particle size of 350 mesh, 25 kg of PVC resin, 0.15 kg of polyethylene wax, 1.2 kg of composite lead salt stabilizer, 0.3 kg of AC foaming agent, and 0.1 kg of paraffin wax. kg, pour the above-mentioned material into the mixer and mix it well, then pour the mixture into the hopper of the extruder, form it through the high-temperature hard mold of the extruder, pass the blank out of the extruder through the vacuum setting mold, and then enter the traction , followed by soaking in cold water to set the shape, and finally vacuum dehumidification to complete the manufacture of the straw composite imitation solid wood wire of the present invention.

Embodiment 3

[0014] Embodiment 3. The formula for taking materials is: 8 kg of straw with a particle size of 300 mesh, 30 kg of limestone with a particle size of 500 mesh, 30 kg of PVC resin, 0.2 kg of polyethylene wax, 1.5 kg of composite lead salt stabilizer, 0.5 kg of AC foaming agent, and 0.15 kg of paraffin wax. kg, pour the above-mentioned material into the mixer and mix it well, then pour the mixture into the hopper of the extruder, form it through the high-temperature hard mold of the extruder, pass the blank out of the extruder through the vacuum setting mold, and then enter the traction , followed by soaking in cold water to set the shape, and finally vacuum dehumidification to complete the manufacture of the straw composite imitation solid wood wire of the present invention.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Granularityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a formula of straw compound real wood imitated wires. The formula comprises the following components in part by weight: 5 to 8 parts of straws with granularity of 80 to 300 meshes, 20 to 30 parts of limestone with granularity of 150 to 500 meshes, 20 to 30 parts of PVC resin, 0.1 to 0.2 part of polyethylene wax, 1.0 to 1.5 parts of stabilizer, 0.2 to 0.5 part of AC foaming agent and 0.05 to 0.15 part of paraffin. The formula realizes recycle and reutilization of wastes, is economic and environment-friendly and avoids damage to the ecology by adopting the straws to replace sawdust; meanwhile, the strength of the real wood imitated wires formed through a high-temperature hard die by using the formula is greatly improved and fully accords with even exceeds the national standard so as to prolong the service life; the real wood imitated wires prepared by adopting multiple chemical reagents and chemical raw materials can prevent mildew and moisture, insulate heat and retard flame, and are quite safe to use; and the formula does not adopt toxic and harmful substances such as formaldehyde and the like so as to prevent secondary pollution to the environment.

Description

technical field [0001] The invention relates to a formula of building materials, in particular to a formula of straw composite solid wood wire. Background technique [0002] Composite imitation solid wood wire is one of the building materials widely used in modern home decoration and construction engineering. As a result, the current extensive market demand leads to a large demand for wood chips, resulting in the annual consumption of a large number of trees, causing great damage to vegetation, which violates the current concept of ecological protection. At the same time, most of the existing formulas contain toxic and harmful substances such as formaldehyde, which has caused secondary pollution to the environment. [0003] In view of the above shortcomings, it is necessary to provide an improved compound imitation solid wood wire material formula, which can fully protect the environment while meeting the current broad market demand. Contents of the invention [0004] In...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08L97/02C08K13/02C08K3/26C08K5/01E04F19/02
Inventor 陶泊汛陶沿竹王亚涂九宏王梦娜陶红均
Owner CHONGQING SHUAIZHIDUN DOOR IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com