High-strength ferritic stainless steel band and manufacturing method thereof

A manufacturing method and technology of steel strip, applied in the field of stainless steel, can solve problems such as inability to meet

Inactive Publication Date: 2010-06-23
BAOSHAN IRON & STEEL CO LTD
View PDF3 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Adding elements such as V to improve the strength of stainless steel in this chromium stainless steel can increase the yield strength of stainless steel by about 100Mpa, reaching the level of 300-350Mpa, but it still cannot meet the needs of higher-strength thin strip materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength ferritic stainless steel band and manufacturing method thereof
  • High-strength ferritic stainless steel band and manufacturing method thereof
  • High-strength ferritic stainless steel band and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0035] The present invention will be described in more detail below with reference to the accompanying drawings. These examples are only descriptions of the best embodiments of the present invention, and do not limit the scope of the present invention in any way.

[0036] The chemical compositions of the steels involved in the examples of the present invention and the steels involved in the comparative examples are shown in Table 2, the main rolling processes are shown in Table 3, and the mechanical properties are shown in Table 4. The steel used in the comparative example is the vanadium-added ferritic stainless steel commonly used at present.

[0037] The chemical composition of the steel involved in the embodiment of the present invention and the steel involved in the comparative example in table 2

[0038]

[0039] Table 3 The main rolling process of the steel involved in the embodiment of the present invention and the steel involved in the comparative example

[0040...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
yield strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a high-strength ferritic stainless steel band, which comprises the following components in percentage by weight: less than or equal to 0.015 percent of C; less than or equal to 1.0 percent of Si; less than or equal to 1.0 percent of Mn; 10.5 to 17.0 percent of Cr; less than or equal to 0.03 percent of P; less than or equal to 0.01 percent of S; less than or equal to 0.1 percent of Ni; less than or equal to 0.015 percent of N; less than or equal to 0.03 percent of Al; less than or equal to 0.006 percent of O; less than or equal to 0.025 percent of C+N; 10(C+N) to 0.60 percent of Nb or 8(C+N) to 0.30 percent of Ti or more than or equal to 10(C+N) to 0.60 percent of Ti+0.5Nb, wherein the ratio of Nb to Ti is between 1.0 and 2.0; the balance of Fe and unavoidable impurities. The invention also provides a method for manufacturing the steel band, which comprises the steps of smelting, continuous casting, coping, hot rolling, annealing and pickling, cold rolling and pickling and bundling. The steel band has higher strength and lower cost and belongs to the environmental-friendly material.

Description

technical field [0001] The present invention relates to a stainless steel, in particular, the present invention relates to a high-strength ferritic stainless steel. Background technique [0002] With the continuous development of the electronics industry, the output of various electronic products such as televisions and computers continues to increase, and people's requirements for the appearance of products are also constantly improving. A large number of liquid crystal displays, mobile phone casings, etc. use special frames, resulting in a significant increase in the amount of ferritic stainless steel dedicated to liquid crystal display frames. At present, this ferritic stainless steel is mainly used to manufacture frames of electronic products such as TVs, computers, mobile phones, etc., which requires it to have high strength and good corrosion resistance. [0003] Ferritic stainless steel is produced by an ultra-low carbon and nitrogen process, and the corrosion resist...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/50C21D8/02B21B37/74B21B37/16
Inventor 毕洪运李鑫王宝森
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com