Waterproof cubic three-dimensional tweed
A cubic and three-dimensional technology, applied in the field of textile fabrics, can solve the problems of easy wrinkling, no three-dimensional effect, and no recovery, and achieve good waterproof and oil-proof effects.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0023] Raw material: Wool / Lycra=93.78 / 6.22 (wool is 80S Australian wool, Lycra is 40D / 1 DuPont Lycra). Yarn count: 70 / 2*70 / 2, twist coefficient: 145 / 145, drafting speed ratio of wool and Lycra: 1:2.5, warp density: 287 threads / 10cm, weft density: 260 threads / 10cm, total tightness Degree: 92.5, meter weight: 310g, finished product width: 150cm.
[0024] Specific production steps: top dyeing-spinning-weaving-repair-singeing-flat washing-drying-heat setting-mud washing-double cooking-drying-cooking-brush cutting-waterproof, oil-proof finishing-baking- Intermediate inspection - wet - dry - finished product.
[0025] Among them, heat setting temperature: 190°C, speed ratio: 40m / min; waterproof, oil-proof: speed: 8m / min; temperature: 170°C, additive SL-NEW (manufactured by Ciba Essence China Co., Ltd.): added The amount is 5% of the weight of the fabric per meter. The parameters used in other steps can be realized according to the production parameters of conventional wool spinni...
Embodiment 2
[0031] Raw material: Wool / Lycra=92 / 8 (the wool is 80S Australian wool, and the Lycra is 40D / 1 DuPont Lycra). Yarn count: 70 / 2*70 / 2, twist coefficient: 145 / 145, drafting speed ratio of wool and Lycra: 1:2.5, warp density: 287 threads / 10cm, weft density: 260 threads / 10cm, total tightness Degree: 92.5, meter weight: 310g, finished product width: 151cm.
[0032] Specific production steps: top dyeing-spinning-weaving-repair-singeing-flat washing-drying-heat setting-mud washing-double boiling-drying-cooked repair-brush cutting-waterproof and oil-proof finishing-baking-middle Check-wet-dry-finished product.
[0033] Heat setting temperature: 195°C, speed ratio: 45m / min; waterproof, oil-proof: speed: 8m / min, temperature: 160°C, additive SL-NEW (manufactured by Ciba Essence China Co., Ltd.): adding amount is 5% of fabric weight per meter. The parameters used in other steps can be realized according to the production parameters of conventional wool spinning fabrics.
[0034] In the ...
Embodiment 3
[0039] Raw material: Wool / Lycra=95 / 5 (wool is 80S Australian wool, Lycra is 40D / 1 DuPont Lycra). Yarn count: 70 / 2*70 / 2, twist coefficient: 145 / 145, drafting speed ratio of wool and Lycra: 1:2.5, warp density: 285 threads / 10cm, weft density: 265 threads / 10cm, total tightness Degree: 95, meter weight: 315g, finished product width: 152cm.
[0040]Specific production steps: top dyeing-spinning-weaving-repair-singeing-flat washing-drying-heat setting-mud washing-double boiling-drying-cooked repair-brush shearing-waterproof, oil-proof finishing-baking- Intermediate inspection - wet - dry - finished product.
[0041] Among them, heat setting temperature: 190°C, speed ratio: 40m / min; waterproof, oil-proof: speed: 10m / min; temperature: 165°C, additive SL-NEW (produced by Ciba Essence China Co., Ltd.): add The amount is 4% of the weight of the fabric per meter. The parameters used in other steps can be realized according to the production parameters of conventional wool spinning fabr...
PUM
![No PUM](https://static-eureka-patsnap-com.libproxy1.nus.edu.sg/ssr/23.2.0/_nuxt/noPUMSmall.5c5f49c7.png)
Abstract
Description
Claims
Application Information
![application no application](https://static-eureka-patsnap-com.libproxy1.nus.edu.sg/ssr/23.2.0/_nuxt/application.06fe782c.png)
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com