Luminous automotive coating wheel hub paint and preparation method thereof

A paint and wheel hub technology, applied in the field of luminous automotive paint, wheel hub paint and its preparation, can solve the problems that the car cannot attract enough attention from personnel, no luminous effect, hidden safety hazards, etc., and achieve excellent leveling and good electrostatic coating operations performance, excellent resistance to salt spray

Inactive Publication Date: 2009-12-30
王长光
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the wheel coatings of automobiles on the market have no luminous effect, so that the automobile cannot attract enough attention of personnel when driving at night, which has certain potential safety hazards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A luminescent automotive paint wheel hub paint, containing green luminescent powder, acrylic resin, amino resin, DISPARLON 6900-20X wax liquid, BL-3175 resin, EP-1001 resin, dispersant, S-100 solvent oil, leveling agent, ES -80 conductive additive, n-butanol, toluene;

[0031] The percentage by weight of each component in the described luminescent automobile paint wheel hub paint is:

[0032] Luminous powder 5%-20%

[0033] Toluene 5%-20%

[0034] Acrylic resin 40%-50%

[0035] Amino resin 10%-15%

[0036] DISPARLON 6900-20X wax solution 5%-15%

[0037] EP-1001 resin 2%-6%

[0038] BL-3175 resin 2%-6%

[0039] Dispersant 0.05%-0.5%

[0040] S-100 solvent oil 1%-3%

[0041] Leveling agent 0.05%-0.5%

[0042] ES-80 conductive additive 0.5%-2%

[0043] Butanol 5%-15%

[0044] The unit of weight described in this embodiment is kilogram, also can be ton;

[0045] The preparation steps of the luminous automotive coating wheel hub paint described in this embodiment...

Embodiment 2

[0055] The present embodiment is a preferred scheme based on embodiment 1, and the quality of raw materials (components) used is the same as that of embodiment 1, and the weight percentage of described luminous automobile coating wheel hub paint is:

[0056] Green Glow Powder 8.2%

[0057] Toluene 8.2%

[0058]Acrylic resin 47.4%

[0059] Amino resin 11.4%

[0060] DISPARLON 6900-20X Wax 10%

[0061] EP-1011 resin 3%

[0062] BL-3175 resin 3%

[0063] Dispersant 0.18%

[0064] S-100 mineral spirits 1.4%

[0065] Leveling agent 0.12%

[0066] ES-80 conductive additive 1%

[0067] n-Butanol 6.1%

[0068] The unit of weight described in this embodiment is kilogram, also can be ton;

[0069] The preparation steps of the luminous automotive coating wheel hub paint described in the present embodiment are the same as in Example 1;

[0070] In this example, the various components and equipment used are conventional products and can be purchased in the market.

Embodiment 3

[0072] The present embodiment is a preferred scheme based on embodiment 1, and the quality of raw materials (components) used is the same as that of embodiment 1, and the weight percentage of described luminous automobile coating wheel hub paint is:

[0073] Red Glow Powder 9.5%

[0074] Toluene 9%

[0075] Acrylic resin 47.1%

[0076] Amino resin 10.6%

[0077] DISPARLON 6900-20X Wax 9.2%

[0078] EP-1001 resin 3.05%

[0079] BL-3175 resin 3.05%

[0080] Dispersant 0.15%

[0081] S-100 mineral spirits 1.6%

[0082] Leveling agent 0.15%

[0083] ES-80 conductive additive 1%

[0084] n-Butanol 5.6%

[0085] The unit of weight described in this embodiment is kilogram, also can be ton;

[0086] The preparation steps of the luminous automotive coating wheel hub paint described in the present embodiment are the same as in Example 1;

[0087] In this example, the various components and equipment used are conventional products and can be purchased in the market.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention aims to provide a luminous automotive coating wheel hub paint and a preparation method thereof. The wheel hub paint contains luminous powder, methylbenzene, acrylic resin, amino resin, DISPARLON 6900-20X wax liquid, EP-1001 resin, BL-3175 resin, dispersant, S-100 solvent oil, flatting agent, ES-80 conduction accessory ingredient and n-butyl alcohol. The invention has abundant color and special noctilucence effect, has favourable levelling property, film coating property, interlayer mating property and mark covering ability, and can be directly sprayed on aluminum material to obtain favourable salt-resistant mist, CASS and the like; in addition, the invention can adapt to environment without temperature control devices, has favourable electrostatic coating property, environment protection and no radioactivity and can repeatedly glow for a long time.

Description

technical field [0001] The invention relates to the field of chemical coatings, in particular to a luminous automotive paint wheel paint and a preparation method thereof. The invention contains components such as luminescent powder, toluene, acrylic resin, amino resin, etc.; the luminous automotive paint wheel paint has rich colors, The visual effect is obvious and beautiful, which can improve the safety of driving at night. technical background [0002] The safety of automobile driving at night is an important issue related to drivers and their members; automobiles driving at night need obvious signs to attract the attention of personnel, so as to ensure traffic safety. At present, the wheel coatings of automobiles on the market have no luminous effect, so that the automobile cannot attract enough attention of personnel when driving at night, which has certain potential safety hazards. Therefore, there is a need for a luminescent coating for automobile wheels on the market...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D161/20C09D7/12C09D5/22
Inventor 王长光
Owner 王长光
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com