Imitation electroplating coating

An imitation electroplating and coating technology, applied in the field of imitation electroplating coatings, can solve problems such as skin allergies, carcinogenicity, air and water pollution, and achieve strong adhesion, good environmental protection, and good brightness

Inactive Publication Date: 2009-11-18
HANGZHOU LIWEI CHEM INDAL PAINT
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Traditional electroplating products pollute air and water very seriously. Improper use of sodium cyanide, a raw material required for production, can easily cause disability. Nickel electroplating can cause skin allergies and carcinogenic effects, seriously threatening health
The wastewater discharge of electroplating products is large and the pollution is serious

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Imitation electroplating coating
  • Imitation electroplating coating
  • Imitation electroplating coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0106] The present embodiment is the optimal formula, and its first component by weight is composed as follows:

[0107] Floating silver pigment 3 parts

[0108] 27 parts of xylene;

[0109] The second component in parts by weight is composed as follows:

[0110] Amino resin 5 parts

[0111] 23 parts of low acid value acrylic resin

[0112] Butyl acetate 0.6 part

[0113] 0.6 part of xylene

[0114] Low acid value adhesion promoter 0.2 part

[0115] Low acid value conductive agent 0.15 parts.

[0116] The production process, inspection requirements, usage methods and other related content are as described above.

Embodiment 2

[0118] The first component of the present embodiment in parts by weight is composed as follows:

[0119] Floating silver pigment 3 parts

[0120] 27 parts of xylene;

[0121] The second component in parts by weight is composed as follows:

[0122] 4 parts of amino resin

[0123] 24 parts of low acid acrylic resin

[0124] Butyl acetate 0.6 part

[0125] 0.6 part of xylene

[0126] Low acid value adhesion promoter 0.2 part

[0127] Low acid value conductive agent 0.15 parts.

[0128] The production process, inspection requirements, usage methods and other related content are as described above.

Embodiment 3

[0130] The first component of the present embodiment in parts by weight is composed as follows:

[0131] Floating silver pigment 3 parts

[0132] 27 parts of xylene;

[0133] The second component in parts by weight is composed as follows:

[0134] Amino resin 6 parts

[0135] 22 parts of low acid value acrylic resin

[0136] Butyl acetate 0.6 part

[0137] 0.6 part of xylene

[0138] Low acid value adhesion promoter 0.2 part

[0139] Low acid value conductive agent 0.15 parts.

[0140] The production process, inspection requirements, usage methods and other related content are as described above.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lusteraaaaaaaaaa
Login to View More

Abstract

The invention relates to an imitation electroplating coating which can be applied to the products such as a bicycle, a motorcycle, an electric motor car, resin crafts, Buddha tool, ceramics, light fitting, shells, glass, hardware, electric appliances, plastics, etc. The imitation electroplating coating comprises a first component and a second component; wherein, the first component consists of floating silver paint and dimethylbenzene, and the second component consists of amine resin, acrylic resin, butylacetate, dimethylbenzene, adhesion promoter and conductive agent. The invention is energy-saving and environment-friendly, and can be used for replacing electroplating technology.

Description

technical field [0001] The invention relates to an imitation electroplating coating, which is mainly applied to bicycles, motorcycles, electric vehicles, resin handicrafts, Buddhist furniture, ceramics, lamps, shells, glass, hardware, electrical appliances, plastics and other products. Background technique [0002] Traditional electroplating products pollute the air and water quite seriously. Improper use of sodium cyanide, the raw material required for production, can easily cause disability. Electroplating nickel can cause skin allergies and carcinogenic effects, which seriously threatens health. Electroplating products discharge a large amount of wastewater and cause serious pollution. SUMMARY OF THE INVENTION [0003] The technical problem to be solved by the present invention is to overcome the above-mentioned shortcomings existing in the prior art, and to provide a kind of imitation electroplating paint that is energy-saving and environmentally friendly, and can repl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D161/20C09D7/12C09D5/24C09D5/29
CPCY02P20/10
Inventor 柳彩虹
Owner HANGZHOU LIWEI CHEM INDAL PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products