High plasticity magnesium alloy and preparation method thereof

A high-plasticity, magnesium alloy technology, applied in the field of magnesium alloys, can solve the problems of no high-plasticity magnesium alloy system and limited improvement, and achieve the effects of improving plastic deformation capacity, alleviating stress concentration, and high room temperature plasticity.

Inactive Publication Date: 2009-03-25
NANJING UNIV OF INFORMATION SCI & TECH
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The above patents are based on the magnesium-zinc master alloy, adding a certain amount of rare earth elements and other elements to improve the plasticity of the magnesium alloy. The degree of improvement is limited by the parent alloy, and no independent high-plasticity magnesium alloy system has been formed.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High plasticity magnesium alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0014] Table 1 Plastic Alloys

[0015]

[0016]

[0017] Tin-lead-zirconium and magnesium form a complex compound. The dispersion distribution can adjust the orientation of the grains during deformation. At the same time, zirconium has the effect of refining the grains, which can significantly improve the plasticity of the material; The brittleness of the material is lower than the composition range of the alloy, and the effect of the elements is not enough to precipitate the necessary compounds. Therefore, under the action of a certain amount of Sn, Pb or Sn, Pb and Zr, the plasticity of magnesium is improved. As can be seen from the above table, when the content of each metal is lower than the minimum content of the present invention, the effect of improvement is not obvious, and when it is higher than the highest amount, the effect of improvement is not obvious, so only when the content of the present invention Better performance can be obtained within ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a magnesium alloy with high plasticity, which contains the following components by mass percent: 0.5 percent to 4 percent of Sn, 0.1 percent to 6 percent of Pb, 0.05 percent to 6 percent of Zr, and Mg as the rest. The preparation steps thereof are as follows: materials are proportioned according to the proportion of alloy components, metals proportioned are heated and melted in protective atmosphere of SF6, the mass percent of Zr in Mg-Zr hardener is 30 percent, and the magnesium alloy of high plasticity is obtained after the temperature reaches 700 DEG C to 730 DEG C and is maintained for 5 minutes to 10 minutes. Magnesium can form a compound with both tin and lead, coordinating with deformation and alleviating stress concentration, thus greatly improving the plastic deformation capacity of magnesium alloy, not only effectively enhancing the strength of the magnesium alloy but also increasing the plasticity of the alloy. Under the function of a certain amount of Zr, tin and lead can impose a more obvious effect on the increasing of the plasticity of magnesium. The magnesium alloy of high plasticity only uses general elements of common tin and lead, thereby avoiding the use of a large amount of rare and precious elements, and has simple production and preparation technique, quite low cost and high normal-temperature plasticity.

Description

1. Technical field [0001] The invention belongs to the technical field of magnesium alloys, in particular to a high-plasticity magnesium alloy and a preparation method thereof. 2. Background technology [0002] Magnesium alloys are widely used in the manufacture of industrial products because of their high specific strength and specific stiffness. However, the existing common magnesium alloys have poor plasticity. If such an alloy is used as the matrix of the composite material, the plasticity of the composite material will also be poor. There are currently some studies on high ductility magnesium alloys: [0003] 200610026842.X proposes a self-generated quasicrystal-reinforced high-plastic magnesium alloy, which belongs to the technical field of metal materials. The inventive components and their weight percentages are: 2-10% Zn, 0.5-6% Gd, 0-1.0% Zr, impurity elements Fe<0.005%, Ni<0.002%, and the rest is Mg. The alloy of the invention contains quasicrystalline ph...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C23/00C22C1/03
Inventor 赵浩峰王玲郭胜利刘斌吴红颜王维颜开
Owner NANJING UNIV OF INFORMATION SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products