Initial magnetic-inductive capacity 60 (+12) (-12) nickel-zinc ferrite material and preparation method

A technology of nickel-zinc ferrite and initial magnetic permeability, applied in the direction of magnetism of inorganic materials, can solve the problems of ferrite eddy current loss increase, reduce lamp efficiency, increase production cost, etc., and achieve low electromagnetic loss and good electromagnetic loss characteristics, the effect of broadband and low electromagnetic loss

Inactive Publication Date: 2010-06-23
TONGXIANG TELIYOU ELECTRONICS SCI & TECH
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, 3F4 power manganese zinc ferrite is generally used abroad to prepare power couplers in high frequency electrodeless lamps, but due to the existence of Such a conductive pair usually has a low resistivity, and since the operating frequency of the high-frequency electrodeless lamp is usually 2.5MHz to 3MHz, this leads to a sharp increase in the eddy current loss of the ferrite, which greatly reduces the efficiency of the lamp
In addition, because the eddy current loss of manganese zinc ferrite is very large, and the eddy current loss is mainly converted into heat, which causes the temperature of the ferrite to reach above 100°C during the working process, so that the 3F4 power manganese zinc ferrite can be assembled In the power coupler, special insulation treatment and skeleton support must be carried out, which leads to a more complicated process and increases the production cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Initial magnetic-inductive capacity 60 (+12) (-12) nickel-zinc ferrite material and preparation method
  • Initial magnetic-inductive capacity 60 (+12) (-12) nickel-zinc ferrite material and preparation method
  • Initial magnetic-inductive capacity 60 (+12) (-12) nickel-zinc ferrite material and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] 1) Selection of raw materials: a kind of nickel-zinc ferrite material with an initial magnetic permeability of 68 and its preparation method provided in this embodiment, its raw material is selected industrially pure Fe 2 o 3 , ZnO, MnCO 3 , NiO and CoO.

[0030] 2) Composition design and weighing: according to Fe 2 o 3 49mol%, ZnO 14mol%, MnCO 3 1 mol%, NiO 35.7 mol%, and CoO 0.3 mol%.

[0031] 3) Mixing of raw materials: Put the weighed raw materials into a sand mill, add deionized water, the weight of deionized water is 1.2 times of the total weight of raw materials, and the ball milling time is 2 hours.

[0032] 4) Pre-burning: Dry the raw materials that have been ball-milled once, and put them into an electric furnace for pre-burning. The pre-burning temperature is 950°C, and the pre-burning time is 3.5 hours. After pre-burning, it is cooled with the furnace. After pre-burning, XRD phase analysis was carried out on the pre-fired material, and it was confirmed...

Embodiment 2

[0042] 1) Selection of raw material: a kind of nickel-zinc ferrite material and preparation method with an initial magnetic permeability of 61 provided in this embodiment, its raw material selects industrially pure Fe 2 o 3 , ZnO, MnCO 3 , NiO and CoO.

[0043] 2) Composition design and weighing: according to Fe 2 o 3 46mol%, ZnO 10.4mol%, MnCO 3 0.1 mol%, NiO 42 mol%, and CoO 1.5 mol%.

[0044] 3) Mixing of raw materials: Put the weighed raw materials into a sand mill, add deionized water, the weight of deionized water is 1.2 times of the total weight of raw materials, and the ball milling time is 1 hour.

[0045] 4) Pre-burning: Dry the raw materials that have been ball-milled once, and put them into an electric furnace for pre-burning. The pre-burning temperature is 1100°C, and the pre-burning time is 1.5 hours. After pre-burning, it is cooled with the furnace. After pre-burning, XRD phase analysis was carried out on the pre-fired material, and it was confirmed that o...

Embodiment 3

[0055] 1) Selection of raw material: a kind of nickel-zinc ferrite material and preparation method with an initial magnetic permeability of 52 provided in this embodiment, its raw material selects industrially pure Fe 2 o 3 , ZnO, MnCO 3 , NiO and CoO.

[0056] 2) Composition design and weighing: according to Fe 2 o 3 49mol%, ZnO 8mol%, MnCO 3 0.4 mol%, NiO 42 mol%, and CoO 0.6 mol%.

[0057] 3) Mixing of raw materials: Put the weighed raw materials into a sand mill, add deionized water, the weight of deionized water is 1.2 times of the total weight of raw materials, and the ball milling time is 1.5 hours.

[0058] 4) Pre-burning: Dry the raw materials that have been ball-milled once, and put them into an electric furnace for pre-burning. The pre-burning temperature is 1000°C, and the pre-burning time is 2 hours. After pre-burning, it is cooled with the furnace. After pre-burning, XRD phase analysis was carried out on the pre-fired material, and it was confirmed that onl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Curie pointaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses an oxygen body material of nickel, zinc and ferrum with initial permeability being 60<-12><+12> and a preparation method thereof. The main phase of the material is spinel structure, and the material essentially consists of Fe2O3, ZnO, MnO, NiO and CoO, and the contents of composition calculated by oxide are: 46mol percent to 49mol percent of Fe2O3, 8mol percent to 14mol percent of ZnO, 0.1mol percent to 1.0mol percent of MnO, 35.7mol percent to 42mol percent of NiO and 0.3mol percent to 1.5mol percent of CoO; the oxygen body material of nickel, zinc and ferrum with initial permeability being 60<-12><+12> has broadband, low electromagnetic consumption and good stability in larger working current and can be used for producing various power couplers of high-frequency electroless lamps with the working frequency in range of 2.5MHz to 3MHz; the material has extremely low electromagnetic consumption in high frequency ranging from 2.5MHz to 3MHz; when the frequency isin the range of 2.5MHz to 3MHz, the quality factor Q is more than 240, and the material has extremely high Curie temperature which is more than 300DEG C; due to such high Curie temperature, the material can ensure that the electroless lamp can work smoothly even if the temperature is higher, thus being beneficial to the miniaturization of the electroless lamp.

Description

technical field [0001] The invention relates to a nickel-zinc ferrite material that can be used to make various high-frequency electrodeless lamp power couplers with an operating frequency within 80MHz, especially a kind of nickel-zinc ferrite material with an initial magnetic permeability of 60 -12 +12 Nickel zinc ferrite material and preparation method thereof. Background technique [0002] High Frequency Electronic Discharge Lamp (High Frequency Electronic Discharge Lamp) is a high-tech new light source that integrates the latest electronic power-saving technology and electric light source technology. It does not use a filament, but uses a magnetic field to stimulate gas discharge and light emission. It is highly efficient, energy-saving, and environmentally friendly. , long life and many other advantages. The high-frequency electrodeless lamp is composed of three parts: the excitation power supply, the power coupler and the bulb. The excitation source generates an elec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01F1/11B22F9/04C04B35/622C04B35/26
Inventor 胡军顾晔华
Owner TONGXIANG TELIYOU ELECTRONICS SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com