Fine denier light terylene short fine with luminous function

A bright polyester, functional technology, applied in the field of polyester staple fiber, can solve the problem of no polyester bright staple fiber, etc., and achieve the effect of uniform shrinkage, good dimensional stability, and good gloss

Inactive Publication Date: 2008-06-11
SHENGHONG GRP CO LTD
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Ordinary polyester staple fiber, although there are many differentiated or functional varieties, but after our understanding and search, there is no polyester staple staple fiber with luminous function and fine denier.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment

[0012] The production process is as follows: Intrinsic viscosity IV of ultra-bright polyester chips is 0.64dl / g, add fluorescent agent to the slices at the mixing bin at a ratio of 0.15%, send them to the wet slice bin through pulse conveying, and enter after drying In the screw extruder, the set temperature of the extruder is 270-285 ° C, the melt pressure is > 10 MPa, and the melt temperature is 290 ° C. It is measured by a frequency conversion metering pump. The melt pressure after the pump is 15 MPa and mixed by a high-efficiency static mixer. , into the spinning box for spinning, the melt passes through the circular spinneret, the resulting tow is cooled by ring blowing, oiled, wound and dropped into the barrel to obtain primary fibers, and then bundled, drawn, crimped, relaxed and heat-set , cutting, packing, producing the polyester staple fiber described in the present embodiment.

[0013] In the above process, the ring blowing temperature is 23°C, the wind speed is 0.6...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention aims to provide fine denier (1 to 33 dtex) bright polyester staple fiber with luminescence function. The invention adopts the technical proposal that the supper bright PET sliced sheet is adopted as the spinning raw material; before the sliced sheet being transmitted, the fluorescence luminescence agent with the mass percentage concentration of 0.15% is added and mixed with the sliced sheet; the high temperature tension hot-setting technology condition is adopted to reduce the boiling water shrinkage ratio (or the dry heat shrinkage ratio) of the fiber. The product of the invention has the function of emitting fluorescence under normal conditions, the function can not be lost after coloring, and on the contrary, can realize the function of foiling essential color. Simultaneously, because the supper bright PET sliced sheet is adopted during the production, the glossiness of the product itself is good. The unique technical conditions ensure the product shrinkage to be concordant and uniform, the yarn weaved by utilizing the fiber has the advantages that the shrinkage is small and the dimensional stability is good. The invention can be commonly used for producing the computer metallic yarn and the sewing thread.

Description

technical field [0001] The invention relates to a polyester staple fiber and belongs to the technical field of chemical fibers. Background technique [0002] The production of differentiated fibers and colored fibers is a new technology in chemical fiber production. With the rapid development of the chemical fiber industry, the production technology of differential fiber and colored fiber has been paid more and more attention, and the development and application of new production technology has become one of the development trends of the chemical fiber industry. The domestic production of functional polyester fibers generally adopts the blend spinning method. The blend spinning method is to add modifiers to the polymer and spin with conventional spinning equipment to obtain functional fibers. [0003] Ordinary polyester staple fiber, although there are many differentiated or functional varieties, but after our understanding and search, there has not been a polyester staple ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01F6/92D01F1/10
Inventor 辛婷芬
Owner SHENGHONG GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products