Solid wood composite coining door panel and production technology thereof

A solid wood composite and molding technology, which is applied to wood processing appliances, wooden veneer joints, manufacturing tools, etc., can solve the problems of high cost, inability to form batches, easy to open glue, etc. texture real effect

Inactive Publication Date: 2008-02-06
桦甸市城市基础设施开发建设投资有限公司
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because it is a manual workshop production, the efficiency is low, it is impossible to form batches, the product quality is unstable, the glue is easy to open, and the cost is high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Solid wood composite coining door panel and production technology thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] 1. Take the high-density molded door panel 3 with two panels, the surface is smooth, and the size is 3.2*2150*860mm. The surface is evenly sprayed with ammonia water with a concentration of 5%, and placed at room temperature for 8 to 24 hours to achieve the purpose of rewetting and softening the molded door panel.

[0024] 2. Take a natural solid wood veneer 1 with a thickness of 0.2 mm and a non-woven fabric 2 on the back (the wood species is oak wood). The upper and lower studs and other parts are cut into seven solid wood veneer components in sequence. The principle is that the door studs and stud head veneer components are cut according to the actual size of the door panel or according to the shape and size of the door studs and studs. The solid wood veneer components of the panel part should be appropriately enlarged and cut according to the actual shape and size of the door panel panel, so as to prepare for the stretching and filling of the groove part.

[0025] ...

Embodiment 2

[0029] 1. Take the high-density molded door panel 3 without any shape, the surface is smooth, and the size is 3.2*2150*9200mm. The surface is evenly sprayed with ammonia water with a concentration of 5%, and placed at room temperature for 8 to 24 hours to achieve the purpose of rewetting and softening the molded door panel.

[0030] 2. Take several technical wood veneers 1 (the wood type is teak) with a thickness of 0.2 mm and a thickness of 0.2 mm on the back, and cut them to a certain length according to the length of the molded door panel.

[0031] 3. Evenly spray the modified urea-aldehyde resin on the surface of the softened molded door panel 3 and the back of the cut technical wood veneer 1 component (the side with the non-woven fabric), and dry it in a drying oven or dry it naturally at room temperature Dry.

[0032] 4. Put glue-dried high-tech wood veneer 1 specifications in sequence on the molded door panel after glue-spraying and drying.

[0033] 5. Put the molded ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a solid wood composite molded door board, belonging to a three-layer composite structure. The structure material of the first layer is natural solid wood single board or technical wood single board, the structure of the second layer is non-woven cloth and the structure of the third layer is molded door board (fiberboard). The invention also provided the manufacturing technique which is applicable to industrialized scale production and has stable quality. The invention overcomes the disadvantage of the solid wood single board which has no transverse pulling resistance strength without any material backing and is easy to break transversely; the solid wood composite molded door is a right integration of the solid wood composite door and the molded door, which not only has the advantages of the solid wood composite door that the wood surface texture true and natural, but also has the advantages of the molded door which does not craze or deform.

Description

Technical field: [0001] The invention relates to a novel molded door panel, in particular discloses a solid wood composite molded door panel and its production process, belonging to the technical field of wood processing. technical background: [0002] At present, as far as wooden interior doors are concerned, there are mainly two series of products, solid wood composite doors and molded doors. The so-called solid wood composite door is similar in structure to the traditional solid wood tenon and tenon door. It uses cheap wood, economical fast-growing wood or density board that is not suitable for surface materials to replace the original wood that can be used as surface materials to make structural components. , and then attach wood veneers that can be used as surface materials on the outside of the structural components, and then splice them into doors. This kind of door has the texture of natural wood, which is real, natural, and close to natural solid wood doors. The co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B27D1/04B27D1/08
Inventor 王海洲曹绪英
Owner 桦甸市城市基础设施开发建设投资有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com