Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Polyvinyl alcohol color coating art canvas without filler and its producing process

A technology of polyvinyl alcohol and color coating, applied in the painting field of painters and artists, can solve problems such as oil absorption, back seepage, coating cracking, etc., and achieve the effect of tight coating film, stable performance and good color

Inactive Publication Date: 2010-05-12
宋健 +2
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The defect of this white-coated art canvas is that the compactness of the coating film is not ideal, and back seepage and oil absorption are often prone to occur during painting; because it contains more solid powder without fillers, it is prone to cracking and cracking of the coating and flaking; white coating tends to yellow
These defects affect the performance and shelf life of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The production process steps of polyvinyl alcohol-free composite color coated art oil canvas of the present invention are as follows:

[0032] 1. Preparation of coating materials for bottom, middle and overcoat coatings:

[0033] (1) Undercoat material: take polyvinyl alcohol solution: 50%, styrene-acrylate copolymer emulsion: 18%, ethylene-vinyl acetate copolymer emulsion: 16%, pigment paste: 0.1 %, emulsifying wax: 0.15%, glycerin: 0.2%, sodium benzoate: 0.1%, water: 15.45%; heat the polyvinyl alcohol solution to 75°C, add emulsifying wax and mix evenly to make polyvinyl alcohol emulsion; Then add styrene-acrylate copolymer emulsion and ethylene-vinyl acetate copolymer emulsion and mix evenly; then dissolve sodium benzoate in water, add pigment paste, glycerin and the above mixture, stir and mix evenly at room temperature, and set aside.

[0034] (2), intermediate coating coating material: take polyvinyl alcohol solution: 45%, styrene-acrylate copolymer emulsion: 15%...

Embodiment 2

[0041] The production process steps of the present invention are as follows:

[0042] 1. Preparation of coating materials for bottom, middle and overcoat coatings:

[0043] (1) Undercoat material: take polyvinyl alcohol solution: 45%, styrene-acrylate copolymer emulsion: 25%, ethylene-vinyl acetate copolymer emulsion: 12%, pigment paste: 0.15% %, emulsifying wax: 0.1%, glycerin: 0.3%, sodium benzoate: 0.05%, water: 17.40%; heat the polyvinyl alcohol solution to 80°C, add emulsifying wax and mix evenly to make polyvinyl alcohol emulsion; Then add styrene-acrylate copolymer emulsion and ethylene-vinyl acetate copolymer emulsion and mix evenly; then dissolve sodium benzoate in water, add pigment paste, glycerin and the above mixture, stir and mix evenly at room temperature, and set aside.

[0044] (2), intermediate coating coating material: take polyvinyl alcohol solution: 50%, styrene-acrylate copolymer emulsion: 16%, ethylene-vinyl acetate copolymer emulsion: 16%, pigment slur...

Embodiment 3

[0051] The production process steps of polyvinyl alcohol compounded color coated art oil canvas in the embodiment of the present invention are as follows:

[0052] 1. Preparation of coating materials for bottom, middle and overcoat coatings:

[0053] (1) Undercoat material: take polyvinyl alcohol solution: 40%, styrene-acrylate copolymer emulsion: 20%, ethylene-vinyl acetate copolymer emulsion: 20%, pigment slurry: 0.05 %, emulsifying wax: 0.2%, glycerin: 0.25%, sodium benzoate: 0.15%, water: 19.35%; heat the polyvinyl alcohol solution to 85°C, add emulsifying wax and mix evenly to make polyvinyl alcohol emulsion; Then add styrene-acrylate copolymer emulsion and ethylene-vinyl acetate copolymer emulsion and mix evenly; then dissolve sodium benzoate in water, add pigment slurry, glycerin and the above mixture, stir and mix evenly at room temperature, and set aside;

[0054] (2), intermediate coating coating material: take polyvinyl alcohol solution: 55%, styrene-acrylate copol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention belongs to the field of drawing article technology, and is especially one kind of artists' color canvas with coating of PVA and no filler suitable for oil painting, propylene drawing, gouache and decoration and its production process. The artists' canvas producing process includes compounding the coating materials with PVA solution, styrene-acrylate copolymer emulsion, vinylacetate-ethylene copolymer emulsion, pigment slurry, etc for the bottom layer, the middle layer and facing layer; painting the bottom coating and stoving; painting 1-3 middle coating and stoving; andpainting 1 or 2 facing coating and stoving to obtain the product. The present invention adopts sandwiched structure coating technique, and the artists' canvas has stable performance, good color, highcoating strength, no oil permeation and other advantages.

Description

technical field [0001] The invention relates to a non-filler polyvinyl alcohol compounded color-coated art oil canvas and its production process, specifically for painting artists, suitable for oil painting, acrylic painting, and gouache painting, and can also be used for decoration and decoration The invention belongs to the technical field of painting supplies. Background technique [0002] Before the present invention was made, in prior art, artist's painting usually adopts traditional white coated canvas. It is mainly to apply white coating material directly on the base fabric. White coating materials use polymer emulsions such as polyvinyl alcohol, ethylene acetic acid homopolymer emulsions, styrene-acrylate copolymer emulsions, and acrylate copolymer emulsions with one-component or two-component emulsions as coating gum bases. Made with a mix of multiple fillings. Then apply the coating material on the base cloth to make art oil canvas. The defect of this kind of w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06N3/18D06N7/04B44D2/00
Inventor 宋健宋奇宋磊
Owner 宋健
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More