Raw materials formulation and method for preparing concrete encaustic tile by using gallet

A technology for concrete and colored tiles, which is applied to the raw material formulation and field of producing concrete colored tiles by using stone chips, can solve problems such as the unsuitable production of filter-pressed colored tiles, achieve excellent squareness and flatness, reduce production costs, and protect The effect of the environment

Inactive Publication Date: 2006-09-27
QUNFENG INTELLIGENT MACHINERY
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The technology provided by this patent is only applicable to roll-pressed colored tiles, and not suitable for the production of filter-pressed colored tiles that require higher raw materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Embodiment 1: Utilize stone chip to produce the raw material formula of concrete colored tile, proportion by weight:

[0028] Stone chips with a particle diameter of 1 to 5 mm 53

[0029] Cement (P.O 42.5#) 33

[0030] Admixture (TW-3 superplasticizer) 1

[0031] water 13.

[0032] The method for utilizing stone chips to produce concrete colored tiles comprises the following steps:

[0033] a. Concrete preparation:

[0034] a) First sieve the stone chip waste residue with a 1mm / hole sieve to remove the fine powder smaller than 1mm; then use a 5mm / hole sieve to remove the coarse slag larger than 5mm, and take the remaining stone chips in the middle sieve;

[0035] b) Put a predetermined amount of stone chips after sieving into the concrete mixer, and start mixing for 4 to 5 minutes;

[0036] c) Put a predetermined amount of cement into the stone chips after stirring, and start stirring for 1 to 2 minutes;

[0037] d) Add a predetermined amount of water dissolved wi...

Embodiment 2

[0044] Embodiment 2: Utilize stone chip to produce the raw material formula of concrete color tile, proportion by weight:

[0045] Stone chips with a particle diameter of 1-5mm 55

[0046] Cement (P.O 42.5#) 31

[0047] Admixture (TW-3 superplasticizer) 0.8

[0048] water 13.2.

[0049] Its production method is identical with embodiment 1.

[0050] Embodiment 2: Utilize stone chip to produce the raw material formula of concrete color tile, proportion by weight:

[0051] Stone chips with a particle diameter of 1-5mm 55

[0052] Cement (P.O 42.5#) 31

[0053] Admixture (TW-3 superplasticizer) 0.8

[0054] water 13.2.

[0055] Its production method is identical with embodiment 1.

Embodiment 3

[0056] Embodiment 3: Utilize stone chip to produce the raw material formula of concrete color tile, proportion by weight:

[0057] Particle diameter 1 ~ 5mm stone chips 58

[0058] Cement (P.O 42.5#) 29

[0059] Admixture (TW-3 superplasticizer) 0.5

[0060] water 12.5.

[0061] Its production method is identical with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides the formulation and method for preparing encaustic concrete tile by using attle, wherein the formula of the raw material include (by weight parts): attle 53-58, cement (P.O 42.5#) 29-33, additive (TW-3 high efficiency water reducing agent) 0.5-1, and balancing water.

Description

technical field [0001] The invention relates to a raw material formula and method for producing concrete colored tiles from stone chips. Background technique [0002] With the rapid development of my country's construction industry, people put forward higher requirements for housing construction. Not only should there be neat streets, beautiful squares, and large green areas, but also a colorful roof to make the buildings colorful and beautify the environment and life. According to the national policy, sloping roofs and colored roofs will be vigorously developed. The Ministry of Construction has already clearly stipulated that in the future, at least 30% of urban buildings must use sloping roofs to improve the waterproof, heat insulation, and heat preservation functions of buildings and beautify the environment. [0003] Colored concrete tiles not only have high strength, light weight, waterproof, drainage and other functions, but also have the advantages of low production ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B14/04C04B28/00
Inventor 张建海周志宏陈勋
Owner QUNFENG INTELLIGENT MACHINERY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com