Rocky sand crystal

A technology of rock sand and weight percentage, which is applied in the field of rock sand crystals, can solve the problems of reducing the plastic strength of mortar, and achieve the effects of easy operation, reduction of ground ash, and excellent technical indicators

Inactive Publication Date: 2005-06-08
黄海滨
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the 1990s, China began to study the admixture called "micro-membrane agent" to replace lime. After being used in construction mixed mortar to replace lime, the workability was improved and the use effect was ideal. However, as time went by, "micro-membrane" "Agent" can reduce the plastic strength of mortar

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The rock sand crystal is characterized in that it contains the following components (weight percentage):

[0020] Sodium fatty alcohol polyethylene sulfonate 10%;

[0021] Sodium Rosinate 8%;

[0022] Triisopropanolamine 5%;

[0023] Polyacrylate 12%;

[0024] Sodium sulfate 8%;

[0025] Fly ash 57%;

Embodiment 2

[0027] The rock sand crystal is characterized in that it contains the following components (weight percentage):

[0028] Sodium fatty alcohol polyethylene sulfonate 12%;

[0029] Sodium Rosinate 7%;

[0030] Triisopropanolamine 8%;

[0031] Polyacrylate 10%;

[0032] Sodium sulfate 5%;

[0033] Fly ash 58%;

Embodiment 3

[0035] The rock sand crystal is characterized in that it contains the following components (weight percentage):

[0036] Sodium fatty alcohol polyethylene sulfonate 11%;

[0037] Sodium Rosinate 7%;

[0038] Triisopropanolamine 5%;

[0039] Polyacrylate 8%;

[0040] Sodium sulfate 4%;

[0041] Fly Ash 65%

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A rock sand crystal instead of lime or cement in mortar is prepared from emtrol sodium polyvinylsulfonate, sodium abietate, triisopropanol amine, polyacrylate, sodium sulfate and powdered coal ash.

Description

technical field [0001] The invention belongs to the field of building material admixtures, in particular to a rock sand crystal used for mixing mortar. Background technique [0002] In the history of Chinese architecture, the use of lime has a history of thousands of years. As the world's awareness of environmental protection increases, it is recognized that the use of lime destroys the ecological environment, and sintering of lime causes environmental pollution. In the 1990s, China began to study the admixture called "micro-membrane agent" to replace lime. After being used in construction mixed mortar to replace lime, the workability was improved and the use effect was ideal. However, as time went by, "micro-membrane" "Agent" can reduce the plastic strength of mortar. Practice has proved that "micro-membrane agent" is not the best white ash substitute product. In 2000, the use of "micro-membrane agent" has been stopped in this part of the area. And during this period, so...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B18/08C04B26/22
CPCY02W30/91
Inventor 黄海滨黄海忠马长全
Owner 黄海滨
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products