Preparation of Mg alkali zeolite by vapor phase self crystallization

A vapor phase, zeolite technology, applied in the direction of crystalline aluminosilicate zeolite, can solve the problems of environmental pollution, irritating odor, serious problems, etc.

Inactive Publication Date: 2005-02-23
FUDAN UNIV
View PDF1 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As we all know, volatile amines have serious irritating odor and will cause serious pollution to the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 11

[0021] Example 11, the alkali used in the above examples is solid NaOH, and the water is distilled water.

Embodiment 1

[0022] Example 12, the FER zeolite synthesized in Example 1 was measured by low-temperature nitrogen adsorption method, and its Langmuir specific surface area was 410.2m 2 / g, the micropore volume is 0.13cm 3 / g.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
Login to View More

Abstract

A process for preparing the magnesium-alkali zeolite (FER) by vapor phase transfer (VPT) method includes such steps as preparing the gel from the mixture of alkali metal, oxide of. 3-valence element, oxide of 4-valence element and water, dewatering to obtain dried gel, and self crystallizing in Teflon / water vapor at 100-200 deg.C.

Description

technical field [0001] The invention belongs to the technical field of material synthesis, and in particular relates to a method for preparing ferrierite (FER) by self-rotating crystals in a vapor phase. Using THF / H 2 The O mixture is used as the vapor phase in the vapor phase transport method, the amount of template agent is small, the reaction temperature is low, and the crystallinity of the product is high. Background technique [0002] Zeolite molecular sieve is an inorganic aluminosilicate crystal. Its skeleton contains regular and orderly arranged pores or cages of molecular size (pore size 0.3-1.5nm). It has the functions of shape-selective catalysis, ion exchange and molecular sieving. Widely used in crude oil refining, petroleum catalytic cracking and petrochemical and other fields. [0003] FER (ZSM-35, ferrierite) is a zeolite with a mesopore structure, which contains ten-membered ring channels (0.42×0.54nm, along the [001] direction) and crossed eight-membered ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01B39/02
Inventor 程晓维龙英才
Owner FUDAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com