A technology of aromatic polyamide and wire-covered varnish, which is applied in the direction of coating, etc., can solve the problems of many bubbles, low heat resistance stability, and hairy appearance of the paint film, so as to improve the thermal shock performance and reduce the unevenness of solvent volatilization , good storage stability effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
example 1
[0019] Add 310 parts of N-methylpyrrolidone and 140 parts of dry xylene in a reaction flask equipped with a thermometer, a stirrer and a heater, and 135 parts of 4,4'-diphenylmethane diisocyanate and 95 parts of toluene diisocyanate Dissolve, stir and heat to 40°C, add 78 parts of isophthalic acid, 65 parts of adipic acid and 10 parts of trimethylolpropane, heat up to 80-90°C, keep warm for 1 hour, and then heat up to 100-110°C , keep warm for 1 hour, add 40 parts of cresol, then raise the temperature to 120°C and keep it warm for 0.5 hour, then cool down to 80°C, dilute with a mixed solvent composed of 57 parts of cresol and 70 parts of xylene, the viscosity of the obtained solution is at 25°C When it is 550cpa·s, it is the aromatic polyamide auxiliary agent of the present invention.
example 2~4
[0021] Except that formula uses the quantity shown in table 1 instead, all the other operations are the same as example 1.
[0022] Two, auxiliary agent performance test of the present invention
[0023] The wire enamel obtained after mixing the auxiliary agent of the present invention obtained in Example 1 and Example 3 with the commercially available polyesterimide wire enamel, and the commercially available polyesterimide wire enamel, polyesterimide with 5% nylon 66 resin added Comparison of viscosity of wire enamel (results in Table 2), paint film appearance and hot-shock performance (results in Table 3).
[0024] Table 2 Viscosity Comparison
[0025] sample
Rotational viscosity at 25°C, cpa·s
Commercially available polyesterimide wire enamel
130±20
Polyesterimide wire enamel with 5% nylon 66 resin added
170±20
Add the polyesterimide wire enamel of the auxiliary agent of 6% example 1
140±20
Add the polyester...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com