Method of screening laminated ceramic capacitor

A technology of ceramic capacitors and screening methods, applied in the direction of multilayer capacitors, capacitors, capacitor manufacturing, etc., can solve problems such as deterioration of insulation resistance

Inactive Publication Date: 2001-05-02
MURATA MFG CO LTD
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, in order to ensure that the multilayer ceramic capacitor has high insulation resistance characteristics, a voltage exceeding the rated voltage is applied to the multilayer ceramic capacitor judged as a good product by the conventional screening method in a high-temperature and high-humidity environment. However, when such an accelerated test is performed, there is a problem that the insulation resistance deteriorates.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method of screening laminated ceramic capacitor
  • Method of screening laminated ceramic capacitor
  • Method of screening laminated ceramic capacitor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] First, prepare a laminated ceramic capacitor with a length of 1.6 mm, a width of 0.8 mm, a thickness of 0.8 mm, an electrostatic capacitance of 0.22 μF, and a rated voltage of 16 V according to the known manufacturing method of the laminated ceramic capacitor 1. A capacitor manufactured by using Ni as the inner electrode 7, Cu as the outer electrode 6, and using a ceramic material with B characteristics on the active layer 8.

[0025] Next, a description will be given of a process in which a direct current 4 is applied superimposedly to the manufactured multilayer ceramic capacitor, and when a voltage is generated between the external electrodes 6, the multilayer ceramic capacitor achieves dielectric breakdown. In addition, the DC constant current 4 that has been energized by superimposition does not leak due to the humidity attached to the surface of the multilayer ceramic capacitor 1, and a voltage is generated between the external electrodes 6. In order to apply this ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A method is provided for accurately screening monolithic ceramic capacitors to reject those having internal defects. A constant direct current is supplied between the external electrodes (6) of a monolithic ceramic capacitor (1) having defects (12) in its effective dielectric layer (8). When the voltage between the external electrodes (6) is increased and a voltage curve (11) becomes flat, the constant direct current (4) is further supplied for a predetermined time. If the voltage between the external electrodes (6) abruptly falls during the predetermined time, the capacitor is rejected as defective.

Description

technical field [0001] The invention relates to a screening method for laminated ceramic capacitors which ensures the insulation resistance characteristics of laminated ceramic capacitors. Background technique [0002] In the past, as a screening method for multilayer ceramic capacitors to ensure the insulation characteristics of multilayer ceramic capacitors, a direct voltage exceeding the rated voltage was repeatedly applied between the external electrodes of multilayer ceramic capacitors, and the defective part of the dielectric ceramic layer was electrically destroyed and removed. The withstand voltage test method of capacitors whose insulation resistance value has deteriorated; the insulation resistance measurement test method of measuring the insulation resistance after a certain period of time after applying a DC voltage, and removing capacitors that cannot return to the reference value; measuring the leakage current value after a certain period of time after applying ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G01R31/00G01R31/01H01G4/30H01G13/00
CPCG01R31/016
Inventor 山下由起人大参智饭野猛稻垣茂树菊池立郎富田义纪
Owner MURATA MFG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com