Bioactive filtering material for water treatment and baking technology thereof
A biological activity, water treatment technology, applied in biological water/sewage treatment, water/sludge/sewage treatment, sustainable biological treatment, etc., can solve the problem of limited application of aerated biological filter, intolerant of water scour, and large flow resistance and other problems, to achieve the effect of good film hanging performance, good water flow and large porosity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0017] According to the requirements of biological aerated filtration on the physical and chemical properties of ceramsite and the analysis results of clay, clay is used as the main raw material, 0.15‰ lignin and 0.15‰ sulfonate are added as plasticizers, and it is combined with 2‰ polyvinyl alcohol. The chemical composition of the raw materials is adjusted to have higher expansibility, while ensuring high wear resistance, strength and chemical stability of ceramsite products. The firing temperature of ceramsite needs to be strictly controlled during the roasting process. In the drying stage, the temperature is generally controlled at 60°C, and the drying time is preferably two hours; then the temperature is gradually raised to 600°C. The heating process should not be too fast, and the drying time is preferably 1.5 hours. should. In the preheating stage, the time can be shorter, generally 1 hour; then gradually increase the temperature to 1250 ° C, and after 1 hour of roasting...
Embodiment 2
[0018] Embodiment 2: As described in Embodiment 1, the difference is
[0019] Clay is used as the main raw material, 0.3‰ lignin and 0.3‰ sulfonate are added as plasticizers, and it is combined with 4‰ polyvinyl alcohol for roasting.
Embodiment 3
[0020] Embodiment 3: As described in Embodiment 1, the difference is
[0021] Clay is used as the main raw material, 0.1‰ lignin and 0.15‰ sulfonate are added as plasticizers, combined with 2.5‰ polyvinyl alcohol, and roasted.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com