Heat preservation and sound absorption paste for roof and preparation method of heat preservation and sound absorption paste

A paste and sound-absorbing technology, which is applied in the field of thermal insulation and sound-absorbing spray paste and its preparation on the roof, can solve the problems that cannot meet the requirements of buildings

Active Publication Date: 2022-03-18
上海三棵树防水技术有限公司
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it cannot meet the existing building requirements and is only suitable for self-built houses in remote areas

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heat preservation and sound absorption paste for roof and preparation method of heat preservation and sound absorption paste
  • Heat preservation and sound absorption paste for roof and preparation method of heat preservation and sound absorption paste
  • Heat preservation and sound absorption paste for roof and preparation method of heat preservation and sound absorption paste

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A heat-insulating and sound-absorbing paste for roofs is prepared from the following components according to the following ratios in parts by mass:

[0039]

[0040] The preparation method of the heat-insulating and sound-absorbing paste for the roof of the present embodiment comprises the following steps:

[0041] 1) Add water to the reaction kettle, then add organic gelling material, fiber, silicate solution and additives, disperse and stir at 500r / min for 10min;

[0042] 2) Pre-mix coarse Poraver beads, fine Poraver beads, hollow glass beads, filling powder and additives until no obvious powder accumulation is formed into mixed powder;

[0043] 3) Then pour the mixed powder prepared in step 2) into the liquid material prepared in step 1) at a stirring rate of 40r / min at a constant speed;

[0044] 4) Finally, stir at 60 r / min for 15 minutes to prepare the heat-insulating and sound-absorbing paste for the roof.

[0045] The bulk density of the thick Poraver beads ...

Embodiment 2

[0058] A heat-insulating and sound-absorbing paste for roofs is prepared from the following components according to the following ratios in parts by mass:

[0059]

[0060]

[0061] The preparation method of the heat-insulating and sound-absorbing paste for the roof of the present embodiment comprises the following steps:

[0062] 1) Add water to the reaction kettle, then add organic gelling material, fiber, silicate solution and additives, disperse and stir at 700r / min for 5min;

[0063] 2) Pre-mix coarse Poraver beads, fine Poraver beads, hollow glass beads, filling powder and additives until no obvious powder accumulation is formed into mixed powder;

[0064] 3) Then pour the mixed powder prepared in step 2) into the liquid material prepared in step 1) at a stirring rate of 100r / min;

[0065] 4) Finally, stir at 120r / min for 10min to prepare the heat-insulating and sound-absorbing paste for the roof.

[0066] The bulk density of the thick Poraver beads is 110~150kg / ...

Embodiment 3

[0078] A heat-insulating and sound-absorbing paste for roofs is prepared from the following components according to the following ratios in parts by mass:

[0079]

[0080] The preparation method of the heat-insulating and sound-absorbing paste for the roof of the present embodiment comprises the following steps:

[0081] 1) Add water to the reaction kettle, then add organic gelling material, fiber, silicate solution and additives, disperse and stir at (600) r / min for 6 minutes;

[0082] 2) Pre-mix coarse Poraver beads, fine Poraver beads, hollow glass beads, filling powder and additives until no obvious powder accumulation is formed into mixed powder;

[0083] 3) Then pour the mixed powder prepared in step 2) into the liquid material prepared in step 1) at a stirring rate of 60r / min at a constant speed;

[0084] 4) Finally, stir at (100) r / min for 10-15 minutes to prepare the heat-insulating and sound-absorbing paste for the roof.

[0085] The bulk density of the thick P...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Bulk densityaaaaaaaaaa
Particle sizeaaaaaaaaaa
Bulk densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a heat-preservation and sound-absorption paste material for a roof and a preparation method thereof. The heat-preservation and sound-absorption paste material is prepared from the following components in parts by mass: 50-60 parts of water, 2-5 parts of an organic cementing material, 1-3 parts of a silicate solution, 3-5 parts of an auxiliary agent, 5-20 parts of coarse Poraver beads, 5-10 parts of fine Poraver beads, 5-25 parts of hollow glass beads, 1-15 parts of fibers, 2-6 parts of filling powder and 1-3 parts of an additive, the bulk density of the coarse Poraver beads is 110-150kg / m < 3 >, and the particle size D90 of the coarse Poraver beads is less than or equal to 2mm; the bulk density of the fine Poraver beads is 180-220 kg / m < 3 >, and the particle size D90 of the fine Poraver beads is 0.3 mm. The invention has the advantages of high sound absorption coefficient, wide sound absorption frequency band, fast construction, seamless surface, safety, environmental protection and the like.

Description

technical field [0001] The invention relates to the field of building thermal insulation and sound absorption materials, in particular to a thermal insulation and sound absorption spray paste for roofs and a preparation method thereof. Background technique [0002] With the advancement of science and technology, the creation and use of various mechanical equipment has brought prosperity and progress to human beings, but also produced more and more noise. Noise will not only cause hearing damage, but also induce a variety of cancer-causing and fatal diseases, harm the human cardiovascular system, affect the human nervous system, make people irritable, irritable, affect sleep, cause fatigue, and interfere with people's mental health. Life and work affect people's quality of life. The indoor surface of the building includes the ground, wall and roof. If only hard and dense stone, plaster, and wood are used for decoration, it will produce strong reflection of sound waves, which...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D1/00C09D5/29C09D7/61C09D7/65C09D7/80
CPCC09D1/00C09D5/29C09D7/61C09D7/65C09D7/70C09D7/80Y02W30/91
Inventor 李文彦汤婷婷王文建夏军
Owner 上海三棵树防水技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com