Method for adding reducing agent for promoting carbonization smelting of molten titanium-containing slag

A technology of reducing agent and slag, which is applied in the field of metallurgy, can solve the problems of the pre-mixed reducing agent addition method for molten materials, slow heating rate of the molten pool, and long heating time, so as to achieve the advancement of carbonization reaction and reduce energy consumption , Improve the effect of poor electrical conductivity

Pending Publication Date: 2022-02-25
PANGANG GRP PANZHIHUA STEEL & VANADIUM
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing reports are only explained by technological means, and there are no related reports on the way of adding reducing agent to pre-mixed molten materials
[0003] Secondly, in the carbonization smelting process of molten titanium-containing slag, the electrical conductivity of the titanium-containing slag itself is poor, so there is a problem of slow heating rate of the early molten pool, which leads to long heating time and high cost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for adding reducing agent for promoting carbonization smelting of molten titanium-containing slag

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] The present invention will be further described below in combination with specific embodiments.

[0015] It should be noted that if there are directional indicating terms in the present invention, such as up, down, left, right, front, back direction and orientation terms, they are for the convenience of describing the relative positional relationship between components, not for related components and positions between components The absolute position of the relationship is specified, and it is only used to explain the relative positional relationship, movement conditions, etc. between the components in a specific posture. If the specific posture changes, the directional indication will also change accordingly. If there are terms related to quantity in the present invention, such as "many", "multiple", "several", etc., it specifically refers to two or more.

[0016] A method for adding a reducing agent to promote the carbonization and smelting of molten titanium-containi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for adding a reducing agent for promoting carbonization smelting of molten titanium-containing slag, and belongs to the technical field of metallurgy. The method for adding the reducing agent for promoting carbonization smelting of the molten titanium-containing slag comprises the following steps: 1, after discharging of a previous furnace and before charging of the furnace, adding a reducing agent accounting for 10%-40% of the total reducing agent adding amount required by the furnace into the reaction furnace in advance through a furnace top feeding system; and 2, putting molten titanium-containing slag with the initial temperature larger than or equal to 1280 DEG C into the reaction furnace, then electrifying the reaction furnace to be heated to the smelting temperature, and then supplementing and adding the residual reducing agent needed by the furnace. According to the method, a conductive medium-C can be provided for a molten pool in an early reaction furnace by pre-adding part of the reducing agent so that the condition of poor conductivity of the titanium-containing slag can be remarkably improved, the temperature rise speed of the molten pool can be increased in the early smelting stage, the original defect of slow temperature rise is overcome, the smelting time is shortened, the energy consumption is reduced, and unexpected technical effects are further brought.

Description

technical field [0001] The invention relates to the technical field of metallurgy, in particular to a method for adding a reducing agent for promoting the carbonization and smelting of molten titanium-containing slag. Background technique [0002] Pre-prepared reducing agent technology is mostly used in the field of mixing reducing agent and solid minerals to make pre-reduced pellets and lump ore and then entering the smelting furnace for deep smelting, but this technology is rarely reported in the process of reducing molten materials. Existing reports only illustrate it by technological means, and there are no related reports on the way of adding reducing agent in pre-mixed molten materials. [0003] Secondly, in the carbonization smelting process of molten titanium-containing slag, the conductivity of the titanium-containing slag itself is poor, so there is a problem of slow heating rate of the early molten pool, which leads to long heating time and high cost. Contents o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22B7/04C22B34/12
CPCC22B7/04C22B7/001C22B34/1218Y02P10/20
Inventor 郭文明龙飞虎
Owner PANGANG GRP PANZHIHUA STEEL & VANADIUM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products