Cement sealing curing agent and preparation method thereof

A technology of sealing and curing agent and cement, which is applied in the field of cement sealing and curing agent and its preparation, which can solve the problems of penetration effect, curing time, hardness and strength to be improved, and achieve fine and uniform crystallization products with regular appearance and promote enrichment Effect

Active Publication Date: 2022-04-15
力特克新材料(广东)有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing sealing and curing agents are generally made of single-component materials, and their penetration effect, curing time, hardness, and strength still need to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Embodiment 1 of the present invention provides a kind of cement sealing curing agent, and this curing agent is prepared by mixing component A and component B in a ratio of 6:1,

[0035] In terms of mass percentage, the raw material formula of the component A consists of:

[0036] Sodium polysilicate 40%, lithium polysilicate 39%, hydroxyethyl cellulose 2%, zeolite 2%, metakaolin 4%, sodium dihydrogen phosphate 2%, wetting agent 2%, penetrant 2%, disinfectant Foaming agent 1%, surface modifier 2%, stabilizer 2%, deionized water 2%;

[0037] In terms of mass percentage, the raw material formula of the component B consists of:

[0038] Aliphatic urethane acrylate 60%, trimethylolpropane triacrylate 27%, nano-scale graphene oxide 2%, nano-iron 1%, aluminum hydroxide 4%, aluminum sulfate 2%, sodium hydroxide 2%, de Ionized water 2%.

[0039] The particle size of the sodium polysilicate is 5nm, and the particle size of the lithium polysilicate is 10nm.

[0040] The wettin...

Embodiment 2

[0051] Embodiment 2 of the present invention provides a kind of cement sealing curing agent, and this curing agent is prepared by mixing component A and component B in a ratio of 6:1,

[0052] In terms of mass percentage, the raw material formula of the component A consists of:

[0053] Sodium polysilicate 20%, lithium polysilicate 34%, hydroxyethyl cellulose 5%, zeolite 8%, metakaolin 8%, sodium dihydrogen phosphate 3%, wetting agent 3%, penetrant 5%, disinfectant Foaming agent 3%, surface modifier 4%, stabilizer 3%, deionized water 4%;

[0054] In terms of mass percentage, the raw material formula of the component B consists of:

[0055] Aliphatic urethane acrylate 42%, trimethylolpropane triacrylate 30%, nano-scale graphene oxide 4%, nano-iron 3%, aluminum hydroxide 8%, aluminum sulfate 4%, sodium hydroxide 4%, de Ionized water 5%.

[0056] The particle diameter of the sodium polysilicate is 8nm, and the particle diameter of the lithium polysilicate is 12nm.

[0057] The ...

Embodiment 3

[0064] Embodiment 3 of the present invention provides a kind of cement sealing curing agent, and this curing agent is prepared by mixing component A and component B in a ratio of 6:1,

[0065] In terms of mass percentage, the raw material formula of the component A consists of:

[0066] Sodium polysilicate 20%, lithium polysilicate 20%, hydroxyethyl cellulose 6%, zeolite 10%, metakaolin 6%, sodium dihydrogen phosphate 6%, wetting agent 5%, penetrant 4%, disinfectant Foaming agent 5%, surface modifier 6%, stabilizer 6%, deionized water 6%;

[0067] In terms of mass percentage, the raw material formula of the component B consists of:

[0068] Aliphatic urethane acrylate 39%, trimethylolpropane triacrylate 20%, nano-scale graphene oxide 6%, nano-iron 5%, aluminum hydroxide 10%, aluminum sulfate 6%, sodium hydroxide 6%, de Ionized water 8%.

[0069] The particle size of the sodium polysilicate is 10nm, and the particle size of the lithium polysilicate is 15nm.

[0070] The wet...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a cement sealing curing agent and a preparation method thereof. The curing agent is prepared by mixing component A and component B at a ratio of 6:1, and the raw material formula of component A includes sodium polysilicate, polysilicic acid Lithium, hydroxyethyl cellulose, zeolite, metakaolin, sodium dihydrogen phosphate, wetting agent, penetrant, defoamer, surface modifier, stabilizer, deionized water, the raw material formula of component B includes aliphatic Urethane Acrylate, Trimethylolpropane Triacrylate, Nano Graphene Oxide, Nano Iron, Aluminum Hydroxide, Aluminum Sulfate, Sodium Hydroxide, Deionized Water. The permeability of the present invention is stronger, which greatly improves the strength and wear resistance of the surface layer of the concrete structure, and prolongs the service life of the ground. Component A of the curing agent can be used alone, but under the action of component B, it will be greatly To shorten the curing time and increase its strength to a certain extent, component B plays a synergistic effect on component A.

Description

technical field [0001] The invention relates to the technical field of sealing and curing agents, in particular to a cement sealing and curing agent and a preparation method thereof. Background technique [0002] Sealing and curing agent, also known as liquid hardener or concrete (cement) sealant, can effectively penetrate into the concrete and react chemically with it, lock the pores inside, and have a permanent sealing effect on the concrete surface. The strength and hardness of the ground can control the ground from sand and dust, prevent chemical erosion and weathering. However, the existing sealing and curing agents are generally made of single-component materials, and their penetration effect, curing time, hardness and strength still need to be improved. Contents of the invention [0003] The object of the present invention is to overcome the above-mentioned defects in the prior art, and provide a cement seal curing agent and a preparation method thereof. [0004] ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/69
CPCC04B41/69C04B41/5144C04B41/5037C04B41/5024C04B41/5015C04B41/5014C04B41/50C04B41/5001C04B41/4884C04B41/4803C04B41/4896C04B41/46C04B41/48C04B41/4869C04B41/4539C04B41/4876C04B41/4961C04B41/483
Inventor 周享平
Owner 力特克新材料(广东)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com