Compound near-infrared light photocatalyst as well as preparation method and application thereof

A near-infrared light and photocatalyst technology, which is applied in the field of photocatalytic degradation of pollutants, can solve the problems of low efficiency of organic pollutants, and achieve the effects of simple preparation method, promotion of carrier separation, and improvement of efficiency and rate

Active Publication Date: 2021-09-21
浙江省科创新材料研究院
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Highly oxygen-doped cerium fluoride (CeF 3 -O) is a photocatalyst with a unique intermediate energy band structure. The two band gaps are 1.7eV and 2.9eV respectively. , to carry out photocatalytic reactions of visible light and near-infrared light respectively, but the efficiency of near-infrared photocatalytic degradation of organic pollutants is much lower than that under visible light

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Compound near-infrared light photocatalyst as well as preparation method and application thereof
  • Compound near-infrared light photocatalyst as well as preparation method and application thereof
  • Compound near-infrared light photocatalyst as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] 20mg CeF 3 -O and 0.85 mg AgNO 3 Mix evenly to obtain a compound near-infrared photocatalyst, and store it away from light for future use.

[0033] Dissolve the prepared compound near-infrared photocatalyst in 50ml of tetracycline hydrochloride (20mg / L) solution by ultrasonic dispersion, react in dark for 30min, and then illuminate under 300w xenon lamp (filter: λ>680nm) , Sampling and testing every 30 minutes.

[0034] It was found that, if figure 1 Shown are the degradation efficiency (a) and rate (b) curves of the composite near-infrared photocatalyst under near-infrared light for the degradation of tetracycline hydrochloride. It can be seen from the figure that the compound near-infrared photocatalyst has a degradation efficiency of 73.1% for tetracycline hydrochloride within 180 min, and the kinetic reaction rate k of the first order reaction is 4.5×10 -3 min -1 .

Embodiment 2

[0036] 20mg CeF 3 -O and 0.5mg EDTA-2Na are evenly mixed to obtain a compound near-infrared photocatalyst, which can be stored in the dark for future use.

[0037] Dissolve the prepared compound near-infrared photocatalyst in 50ml of tetracycline hydrochloride (20mg / L) solution by ultrasonic dispersion, react in dark for 30min, and then illuminate under 300w xenon lamp (filter: λ>680nm) , Sampling and testing every 30 minutes.

[0038] It was found that, if figure 2 Shown are the degradation efficiency (a) and rate (b) curves of the composite near-infrared photocatalyst under near-infrared light for the degradation of tetracycline hydrochloride. It can be seen from the figure that the compound near-infrared light photocatalyst has a degradation efficiency of 70.4% for tetracycline hydrochloride within 120 min, and the kinetic reaction rate k of the first order reaction is 9.3×10 -3 min -1 .

Embodiment 3

[0040] 20mg CeF 3 -O and 1.02mg AgNO3 Mix evenly to obtain a compound near-infrared photocatalyst, and store it away from light for future use.

[0041] Dissolve the prepared compound near-infrared photocatalyst in 50ml of tetracycline hydrochloride (20mg / L) solution by ultrasonic dispersion, react in dark for 30min, and then illuminate under 300w xenon lamp (filter: λ>680nm) , Sampling and testing every 30 minutes.

[0042] It was found that the degradation efficiency of the compound near-infrared photocatalyst to tetracycline hydrochloride was 72.8% within 180 min, and the reaction rate k of the first-order reaction kinetics was 4.5×10 -3 min -1 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a compound near-infrared light photocatalyst and a preparation method and application thereof. CeF3-O serving as a main catalyst and silver nitrate serving as a cocatalyst are compounded according to a certain proportion, Ag nano-particles are deposited on the surface of CeF3-O under near-infrared light illumination, carrier separation is promoted through the surface plasma resonance effect, and meanwhile, tetracycline hydrochloride is efficiently degraded. The CeF3-O serves as a main catalyst, has a unique intermediate energy level structure, can directly absorb near-infrared light to generate photo-induced electron-hole pairs, and is essentially different from a composite catalyst which performs near-infrared catalysis through hot electron injection by utilizing the surface plasma resonance effect of Ag nanoparticles. In addition, the CeF3-O is used as a main catalyst, ethylene diamine tetraacetic acid is used as a cocatalyst, and the near-infrared light catalyst compounded according to a certain proportion can also efficiently degrade tetracycline hydrochloride. The process is simple, the compound photocatalyst is good in near-infrared light response, and the tetracycline hydrochloride degradation efficiency is effectively improved.

Description

technical field [0001] The invention belongs to the technical field of photocatalytic degradation of pollutants, and in particular relates to a composite near-infrared light photocatalyst and its preparation method and application. Background technique [0002] Semiconductor photocatalysis is a technology that can effectively use solar energy for photoelectric conversion to treat environmental organic pollutants, and plays an important role as a bridge between modern industrial development and environmental protection. Rare earth semiconductor materials have been widely used as catalysts in many important industrial waste gas treatment processes. [0003] Highly oxygen-doped cerium fluoride (CeF 3 -O) is a photocatalyst with a unique intermediate energy band structure. The two band gaps are 1.7eV and 2.9eV respectively. , to perform photocatalytic reactions under visible light and near-infrared light, respectively, but the efficiency of near-infrared photocatalytic degrada...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J27/25B01J27/06B01J31/26C01F17/265C01F17/10C02F1/30C02F101/38C02F101/34C02F101/36
CPCB01J27/25B01J27/06B01J31/26C01F17/265C01F17/10C02F1/30C02F2305/10C02F2101/34C02F2101/36C02F2101/38B01J35/39
Inventor 王智宇韩冰
Owner 浙江省科创新材料研究院
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com