A lead-free multiferroic material with relaxor ferroelectric properties and its preparation method

A technology of multiferroic materials and ferroelectric properties, applied in the field of lead-free multiferroic materials Ca3CoMn1-xCrxO6 and its preparation, can solve problems such as lead environment and human health hazards, achieve strong magnetoelectric coupling effect, simple preparation process, and realize large-scale production. The effect of mass production

Active Publication Date: 2022-05-10
ZHENGZHOU UNIVERSITY OF LIGHT INDUSTRY
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, most of the relaxor ferroelectric materials currently used are lead-based single crystals or ceramics. Because the toxicity of lead will bring great harm to the environment and human health, it is of great significance to find new lead-free relaxor ferroelectric materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A lead-free multiferroic material with relaxor ferroelectric properties and its preparation method
  • A lead-free multiferroic material with relaxor ferroelectric properties and its preparation method
  • A lead-free multiferroic material with relaxor ferroelectric properties and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] The present invention will be further described below in conjunction with specific embodiments. It should be understood that the following examples are only used to illustrate the present invention rather than limit the scope of the present invention, and those skilled in the art can make some non-essential improvements and adjustments based on the content of the above invention.

[0027] The lead-free multiferroic material Ca with relaxation ferroelectric properties in this embodiment 3 CoMn 1-x Cr x o 6 (0.05≤ x ≤0.15) is prepared as follows:

[0028] In the first step, at a temperature of 25°C, the CaCO 3 、C 4 h 6 COO 4 4H 2 O, C 4 h 6 MnO 4 4H 2 O, CrN 3 o 9 According to 3:1:1- x : x ( x =0.05, 0.1, 0.15) stoichiometric ratio for accurate weighing, and at the same time, weigh citric acid twice the amount of metal cations and dissolve it in deionized water (the principle is that each gram of citric acid corresponds to 1-2ml of deionized water) ;

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a lead-free multiferroic material with relaxor ferroelectric properties and a preparation method thereof. The chemical formula is Ca 3 CoMn 1‑ x Cr x o 6 , where 0.05≤ x ≤0.15, the crystal is orthorhombic structure, space group R‑3c. The weighed CaCO 3 、C 4 h 6 CoO 4 4H 2 O, C 4 h 6 MnO 4 4H 2 O, CrN 3 o 9 Dissolve in citric acid solution, add ethylene glycol to enhance the solution viscosity, then adjust the pH of the mixed solution to 3‑5, put it into a water bath and heat it to make the solution a jelly-like wet gel; dry the wet gel to obtain dry gel; and then through grinding, pre-sintering, secondary grinding, tableting, and sintering to obtain the lead-free multiferroic material. The particle size of the sample is uniform, and it not only has multiferroic characteristics, but also has obvious relaxation characteristics in its ferroelectric phase transition, and its electric dipole moment can be regulated by a magnetic field to promote its application in multifunctional devices.

Description

technical field [0001] The invention relates to the field of relaxor ferroelectric materials and multiferroic materials, in particular to a lead-free multiferroic material Ca with relaxor ferroelectric properties 3 CoMn 1-x Cr x o 6 (0.05≤ x ≤0.15) and preparation method. Background technique [0002] Multiferroic materials refer to materials with two or more iron orders at the same time. This kind of materials can have both spontaneous polarization order and spin order at a certain temperature, and the magnetoelectric coupling effect caused makes multiferroics Materials have certain special physical properties. The characteristic of ferroelectric materials is that they have spontaneous polarization when no external electric field is applied, and the direction of their spontaneous polarization can be reversed or reoriented by an external electric field. Among the ferroelectrics, there is a class called relaxor ferroelectrics, which have a high dielectric constant and a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/26C04B35/622
CPCC04B35/2633C04B35/622C04B2235/3208C04B2235/3262C04B2235/3275C04B2235/3241C04B2235/656C04B2235/6567C04B2235/602C04B2235/76
Inventor 龚高尚周进段亚然王永强苏玉玲
Owner ZHENGZHOU UNIVERSITY OF LIGHT INDUSTRY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap