A kind of volcanic flow rock effect glaze and its preparation method and application

A volcanic flow and volcano technology, applied in the field of glaze, volcanic flow rock effect glaze and its preparation, can solve the problems such as the inability to achieve the flow color effect, the inability to obtain the high brightness effect of the volcanic flow rock, etc., and achieves simple application method and high transparency. , The effect of high temperature resistance

Active Publication Date: 2022-07-01
亚细亚新材料科技股份公司 +1
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Although the above-mentioned high-brightness and colorful ceramic products can achieve colorful effects, they cannot achieve the flow-color effect, let alone the high-brightness effect of volcanic flow rocks.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of volcanic flow rock effect glaze and its preparation method and application
  • A kind of volcanic flow rock effect glaze and its preparation method and application
  • A kind of volcanic flow rock effect glaze and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0091] The present embodiment provides a preparation method of a volcanic flow rock effect glaze, and the preparation method includes the following steps:

[0092] (1) wet ball milling mixed raw materials according to the formula, adopt absolute ethanol to immerse the raw materials during wet ball milling, and obtain a mixed material with an average particle size of 40 μm;

[0093](2) the mixed material obtained in step (1) is divided into the first powder material and the second powder material, and the mass ratio of the first powder material and the second portion of material is 2:1; The two powders are respectively subjected to wet ball milling, and the raw materials are immersed in absolute ethanol during wet ball milling; the average particle size of the first ball abrasive obtained by ball milling of the first powder is 30 μm; the second ball mill obtained by ball milling of the second powder The average particle size of the material is 15 μm;

[0094] (3) uniformly mix...

Embodiment 2

[0097] The present embodiment provides a preparation method of volcanic flow rock effect glaze, and the preparation method includes the following steps:

[0098] (1) wet ball milling mixed raw materials according to the formula, adopt absolute ethanol to immerse the raw materials during wet ball milling, and obtain a mixed material with an average particle size of 30 μm;

[0099] (2) the mixed material obtained in step (1) is divided into the first powder material and the second powder material, and the mass ratio of the first powder material and the second portion of material is 3:1; The two powders are respectively subjected to wet ball milling, and the raw materials are immersed in absolute ethanol during wet ball milling; the average particle size of the first ball abrasive obtained by ball milling of the first powder is 20 μm; the second ball mill obtained by ball milling of the second powder The average particle size of the material is 10 μm;

[0100] (3) uniformly mixi...

Embodiment 3

[0103] The present embodiment provides a preparation method of volcanic flow rock effect glaze, and the preparation method includes the following steps:

[0104] (1) wet ball milling mixed raw materials according to the formula, adopt dehydrated alcohol to immerse raw materials during wet ball milling, and obtain a mixed material with an average particle size of 50 μm;

[0105] (2) the mixed material obtained in step (1) is divided into the first powder material and the second powder material, and the mass ratio of the first powder material and the second portion of material is 1:1; The two powders are respectively subjected to wet ball milling, and the raw materials are immersed in absolute ethanol during wet ball milling; the average particle size of the first ball abrasive obtained by ball milling of the first powder is 40 μm; the second ball mill obtained by ball milling of the second powder The average particle size of the material is 20 μm;

[0106] (3) uniformly mixing...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a volcanic flow rock glaze and a preparation method and application thereof. In parts by weight, the constituent raw materials of the volcanic flow rock effect glaze include: 15-20 parts of calcite plagioclase, 20-25 parts of quartz parts, 5-8 parts of barium carbonate, 6-9 parts of calcined talc, 5-7 parts of kaolin, 25-28 parts of wollastonite, 2-5 parts of calcined kaolin, 3-6 parts of zinc oxide and 1-3 parts of corundum, By adjusting the components of the glaze in the present invention, the prepared volcanic flow rock glaze has the effect of high radiance and color when used in slate, and has high transparency, high temperature resistance and wear resistance, and the gloss can reach 85 degree or more.

Description

technical field [0001] The invention belongs to the technical field of materials, and relates to a glaze, in particular to a volcanic flow rock effect glaze and a preparation method and application thereof. Background technique [0002] Ceramics have different artistic styles and different technical characteristics. During the development of ceramic technology, colorful and various colored glazes appeared. The blue ones include bean green, shadow blue, pink blue or Longquan azure, etc.; red and purple ones include sacrificial red, Langyao red, uniform red, rose purple, beauty drunk or underglaze red, etc; Others include crystalline glaze, crack glaze or golden sand glaze, etc. [0003] Among the above-mentioned color glazes, the ceramic products obtained by adopting the lighter color glaze are still bright and shiny, but the ceramic products obtained by adopting the darker color glaze are generally dull and have insufficient visual impact. [0004] CN 111517825A discloses ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/00
CPCC03C8/00
Inventor 林要军
Owner 亚细亚新材料科技股份公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com