A kind of preparation method of colored superhydrophobic bamboo wood

A production method and wood technology, applied in wood impregnation, wood treatment, impregnated wood, etc., can solve the problems of increasing the added value of bamboo and wood products, single color, and monotonous decorative effect, so as to improve superhydrophobic stability, simple operation, Easy to scale up the effect of production

Active Publication Date: 2022-03-04
ZHEJIANG FORESTRY UNIVERSITY
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, due to the monotonous decorative effect of bamboo wood, if synchronous coloring is achieved while making super-hydrophobic bamboo wood, the added value of bamboo wood product applications will be significantly increased

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Example 1: At 40KN / m 2 Under pressure, use 320 mesh sandpaper to polish the surface of the moso bamboo board that needs to be processed, and use a vacuum cleaner to remove the powder on the surface to obtain a clean surface;

[0027] Spray 3wt% hydrogen peroxide on the clean surface, the spraying amount is 100g / m 2 , After spraying, leave it at room temperature for 1.5 hours, rinse it with deionized water for 3 times, and use a 100°C heat gun to quickly dry it to obtain a surface-pretreated moso bamboo board;

[0028] The edge of the surface of the obtained moso bamboo board to be treated is sealed with a detachable silica gel strip to form a pool-shaped frame; an equal volume of 12g / L cobalt nitrate hexahydrate solution and 27g / L 2-methylimidazole aqueous solution are quickly mixed and poured into the pool-shaped frame , the total amount of mixed solution is 0.6L / m 2 . After standing at room temperature for 6 hours, pour out the liquid in the pool-like frame, quickl...

Embodiment 2

[0031] Example 2: At 40KN / m 2 Under pressure, use 320-grit sandpaper to polish the surface of the fir board that needs to be processed, and use a vacuum cleaner to remove the powder on the surface to obtain a clean surface;

[0032] Spray 7wt% hydrogen peroxide on the clean surface, the spray amount is 30g / m 2 , After spraying, leave it at room temperature for 2 hours, rinse it with deionized water for 3 times, and quickly dry it with an 80°C hot air gun to obtain a surface-pretreated fir board;

[0033] Seal the edge of the obtained fir board surface to be treated with a detachable silicone strip to form a pool-like frame; quickly mix an equal volume of 16g / L cobalt nitrate hexahydrate solution and 36g / L 2-methylimidazole aqueous solution and pour it into the pool-like frame , the total amount of mixed solution is 0.4L / m 2 . After standing at room temperature for 4 hours, the liquid in the pool-like frame was poured out, the surface of the fir board was quickly rinsed 3 ti...

Embodiment 3

[0036] Example 3: At 40KN / m 2 Under pressure, use 320-grit sandpaper to polish the surface of the pine board that needs to be processed, and use a vacuum cleaner to remove the powder on the surface to obtain a clean surface;

[0037] Spray 5wt% hydrogen peroxide on the clean surface, the spraying amount is 60g / m 2 , After spraying, leave it at room temperature for 2 hours, rinse it with deionized water for 3 times, and use a 120°C hot air gun to quickly dry it to obtain a surface-pretreated pine board;

[0038] Seal the edge of the surface of the obtained pine board to be treated with a detachable silicone strip to form a pool-like frame; quickly mix an equal volume of 14g / L cobalt nitrate hexahydrate solution and 30g / L 2-methylimidazole aqueous solution and pour it into the pool-like frame , the total amount of mixed solution is 0.5L / m 2 . After standing at room temperature for 5 hours, pour out the liquid in the pool-like frame, quickly rinse the surface of the pine board...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for producing colored superhydrophobic bamboo wood. The whole production process is carried out in an open environment at room temperature, without the need for organic solvents and reaction devices, and is simple to operate, so it is easy to scale up and produce; at the same time, it can be grown on the surface of bamboo wood. The metal organic framework material is used as a precursor, and the metal hydroxide prepared by in situ conversion has a good binding force on the surface of bamboo wood, which is conducive to improving the adhesion of the superhydrophobic coating and improving its superhydrophobic stability; and through Changing the type of metal salt used in the in-situ conversion of double metal hydroxides can regulate the color of the prepared hydroxides, thereby realizing the production of colored superhydrophobic bamboo wood.

Description

technical field [0001] The invention relates to the field of bamboo wood production, in particular to a production method of colored superhydrophobic bamboo wood. Background technique [0002] With the pursuit of low-carbon life, bamboo and wood materials are increasingly being used in outdoor landscape architecture, furniture, flooring, decoration materials, and large-scale structural engineering materials. With the expansion of product use, people put forward more and higher requirements for product functions. At present, the functions of bamboo and wood materials are single, and the product functions are far behind the market's great demand for multi-functional products. Thereby develop the bamboo-wood plank with different functions, improve the added value of product, expand its use, satisfy the consumption demand of people's increasing day by day, just seem very urgent. In addition, due to the nutrients such as sugar, starch, protein and fat, bamboo wood is prone to m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B27K3/02B27K3/52B27K3/16B27K5/04C01G51/04C01G53/04C09D5/00
CPCB27K3/02B27K3/0207B27K3/52B27K3/16B27K5/04C01G51/04C01G53/04C09D5/00
Inventor 庞亚俊陈浩沈哲红卢英卓
Owner ZHEJIANG FORESTRY UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com