Maintenance method for manufacturing foam concrete member

A technology of foam concrete and components, which is applied in the field of maintenance when making concrete components by self-heating, which can solve problems such as melting of insulation pipes, high curing temperature, product cracks, etc., and achieves the effects of easy operation, low energy consumption, and low investment

Inactive Publication Date: 2021-01-08
烟台三力轻质混凝土科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This kind of production method has a higher curing temperature, which can easily melt the insulation pipe in the board, and the finished product is also prone to cracks due to dehydration. Not only that, in order to increase the curing temperature, it is necessary to increase the mold foam. The temperature of the concrete slurry needs to be increased, which is difficult in the cold weather in the north, and the energy consumption is also high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0009] Add the foamed concrete slurry with a temperature of 40°C into the thermal insulation mold. At this time, the temperature of the foamed concrete slurry in the thermal insulation mold is continuously increased, and the initial setting time and final setting time of the cement in the foamed concrete slurry are controlled. The temperature of the foamed concrete slurry and the components formed by the foamed concrete slurry is kept within 69°C during the period from 0.5 hours before the final setting time of the cement to 4 hours after the final setting time of the cement, and the temperature is maintained for about 11 hours. Complete the maintenance process.

specific Embodiment 2

[0011] Add the foamed concrete slurry with a temperature of 36°C into the thermal insulation mold. At this time, the temperature of the foamed concrete slurry in the thermal insulation mold is continuously increased, and the initial setting time and final setting time of the cement in the foamed concrete slurry are controlled. The temperature of the foamed concrete slurry and the components formed by the foamed concrete slurry is kept within 60°C during the period from 0.5 hours before the final setting time of the cement to 5 hours after the final setting time of the cement, and the temperature is maintained for about 11 hours. Complete the maintenance process.

specific Embodiment 3

[0013] Add the foamed concrete slurry with a temperature of 32°C into the thermal insulation mold. At this time, the temperature of the foamed concrete slurry in the thermal insulation mold is continuously increased, and the initial setting time and final setting time of the cement in the foamed concrete slurry are controlled. The temperature of the foamed concrete slurry and the components formed by the foamed concrete slurry is kept within 50°C during the period from 0.5 hours before the final setting time of the cement to 5 hours after the final setting time of the cement, and the temperature is maintained for about 12 hours. Complete the maintenance process.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a maintenance method for manufacturing a foam concrete member, which adopts a thermal insulation mold and is characterized in that the initial setting time and the final setting time temperature of cement in foam concrete slurry in the thermal insulation mold are controlled; wherein the temperature t of the foam concrete slurry and the member formed by the foam concrete slurry is controlled to be 30 DEG C<=t<70 DEG C within the time period from 0.5 hour before the final setting time to 5 hours after the final setting time. The method is suitable for manufacturing foam concrete members which are high in using amount of cement and other active materials, small in coarse and fine aggregate content and suitable for temperature rise, has the advantages of being easy to operate, low in manufacturing cost, small in investment, reliable in quality, low in energy consumption, easy to popularize and the like, and provides powerful technical support for building energy conservation and fabricated buildings.

Description

technical field [0001] The invention relates to a maintenance method for making foam concrete components, in particular to a maintenance method for self-heating concrete components. Background technique [0002] Concrete components, especially foam concrete components, often require steam curing or autoclaving curing to improve the mechanical performance indicators of the components. Steam curing requires large investment, energy consumption, and high cost, which does not meet the current building energy-saving requirements. A patent with the patent number "2017100094981" and "a method for manufacturing high-strength foam concrete products" is disclosed in the prior art. The manufacturing method is as follows: Step 1: making foam concrete slurry; Mold maintenance; step 3, demoulding, watering and moisturizing maintenance, and the finished product step. The main technical characteristics are as follows: ①In the production process, the temperature of the foamed concrete slurry...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B40/02
CPCC04B40/025
Inventor 牟世宁林振伟孙茂川陈秋宇赵新于鹏卫德恩
Owner 烟台三力轻质混凝土科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products