PVC composite material based on self-drying water-based aluminum powder coating as well as preparation method and application thereof

A PVC material, self-drying technology, applied in the field of composite materials, can solve the problems that cannot be cleaned with water or other detergents, reduce the use time of the screen, and the polarization contrast is easy to weaken, etc., to achieve convenient packaging, transportation and installation, and good stretching effect , the effect of reducing pollution

Active Publication Date: 2020-12-11
SUZHOU BETELY POLYMER MATERIALS CO LTD +1
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, oil-based coatings have inherent defects, such as dangerous storage, non-volatile, and harmful to the environment and human body. Water-based coatings are gradually being developed, but aluminum powder coatings are different from other existing water-based coatings, and their application fields require different properties to meet It is required for film projection, but after the existing aluminum powder water-based screen coating dries, the aluminum powder on the coating is easy to be touched off, and blackening occurs. When dust is occupied, it cannot be cleaned with water or other detergents, and the floating aluminum Powder is the easiest to oxidize, and the polarization contrast is easily weakened, which greatly reduces the use time of the screen

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PVC composite material based on self-drying water-based aluminum powder coating as well as preparation method and application thereof
  • PVC composite material based on self-drying water-based aluminum powder coating as well as preparation method and application thereof
  • PVC composite material based on self-drying water-based aluminum powder coating as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0021] The preparation method of PVC composite material based on self-drying water-based aluminum powder coating is as follows: adding water-based additives into water, adding water-based aluminum powder after stirring, adding water-based resin under stirring, and stirring to obtain self-drying water-based aluminum powder coating; The self-drying water-based aluminum powder coating is routinely coated on the surface of the PVC material to obtain a PVC composite material based on the self-drying water-based aluminum powder coating; after conventional natural drying or heating drying, a screen is obtained. Specifically, the above-mentioned water-based leveling agent, water-based anti-settling agent, and water-based wax slurry were added to water at a stirring rate of 1000 rpm, stirred for 15 minutes, and then added with a water-based defoamer and water-based dispersant, and stirred at a stirring speed of 1200 rpm for 5 minutes, Then add water-based aluminum powder, stir at 800 rp...

Embodiment 1

[0026] In Example 1, Comparative Example 2 and Comparative Example 3, the water-based resin is composed of water-based anionic aliphatic polyurethane SP-3106, water-based polycarbon polyurethane PU3461, water-based acrylic resin Crysol 6319, water-based alcohol with a weight ratio of 75:10:5:10. Acid resin 6070 composition; in Comparative Example 1, the water-based resin is water-based anionic aliphatic polyurethane SP-3106. In Example 1, Comparative Example 1 and Comparative Example 3, the water-based aluminum powder is composed of large aluminum powder and small aluminum powder, wherein the particle size D50 of the large aluminum powder is 25-35 microns, and the particle size D50 of the small aluminum powder is 8- 15 microns, the mass percentage of large aluminum powder is 35%, and the rest is small aluminum powder; in Comparative Example 2, the particle size D50 of the water-based aluminum powder is all 8-15 microns.

[0027] In the examples and comparative examples, the wa...

Embodiment 2

[0036] The water-based resin is composed of water-based anionic aliphatic polyurethane SP-3106, water-based polycarbonate polyurethane PU3461, water-based acrylic resin Crysol 6319, and water-based alkyd resin 6070 with a weight ratio of 75:10:5:10; the water-based aluminum powder is composed of large aluminum powder, It is composed of small aluminum powder, wherein the particle size D50 of the large aluminum powder is 25-35 microns, the particle size D50 of the small aluminum powder is 8-15 microns, the mass percentage of the large aluminum powder is 35%, and the rest is the small aluminum powder; water dispersion The wetting and leveling agent is BYK-346 and Tego 270 with a weight ratio of 1:1; the water-based defoamer is Tego810 and DAPRO DF 677 with a weight ratio of 1:1; the water-based anti-settling agent is AQ-633E ; Water-based wax slurry is LUBA-print 725.

[0037] In the weight parts of Example 1, the water-based resin was adjusted to 58 parts, and the water-based al...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a PVC composite material based on a self-drying water-based aluminum powder coating as well as a preparation method and application thereof. The PVC composite material comprises a PVC material and the self-drying water-based aluminum powder coating, and the coating comprises the following components in percentage by mass: 50-60% of water-based resin, 20-25% of water-based aluminum powder and 5-15% of a water-based additive. The water-based coating is used for replacing oil-based coating, water is used as a solvent, the cost is reduced, safety and environmental protection are achieved, and environmental protection and physical health of constructors are greatly reduced; and a dry film has good transparency, water resistance, weather resistance and yellowing resistance, the coating can be cleaned with water or a cleaning agent after being used for a long time, the corrosion of water to the dry film is avoided, and the influence of humidity in air on the weather resistance and yellowing resistance of the dry film is also avoided.

Description

technical field [0001] The invention belongs to composite material technology, and particularly relates to a PVC composite material based on self-drying water-based aluminum powder coating, a preparation method and application thereof. Background technique [0002] PVC material is currently widely used in cinemas showing 3D movie effects. Its initial form is soft white PVC with holes. The surface is sprayed with a silver coating to protect the PVC substrate and enhance the 3D effect. The coating must have 3 An important performance index: gain brightness, scattering angle, polarization contrast; the gain brightness is the ratio of the screen reflection brightness in the 5° angle direction under the same lighting strip to the brightness of the ideal diffuse screen under the same conditions, which is reflected in the viewing angle. The degree of visual stimulation to the eyes during filming, according to national standards and industry standards, the general gain brightness is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/14D06N3/04D06N3/12D06N3/00G03B21/56
CPCD06N3/14D06N3/042D06N3/121D06N3/0015D06N3/0063G03B21/56D06N2209/0861D06N2209/142D06N2209/1692
Inventor 张涛花魁昌汪小峰徐宏赵奔王全欧阳旭频
Owner SUZHOU BETELY POLYMER MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap