Metal plate shearing edge rolling strengthening method and plate-shaped part manufactured through same

A metal sheet, rolling technology, applied in the field of mechanical engineering, can solve problems such as cracks cannot be prevented

Active Publication Date: 2020-12-08
DONGFENG COMML VEHICLE CO LTD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Embodiments of the present invention provide a metal plate rolling strengthening method and the plate-shaped part produced therefrom, so as to solve the problem in the related art that cracks cannot be prevented from originating from the tear zone of the shearing edge

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metal plate shearing edge rolling strengthening method and plate-shaped part manufactured through same
  • Metal plate shearing edge rolling strengthening method and plate-shaped part manufactured through same
  • Metal plate shearing edge rolling strengthening method and plate-shaped part manufactured through same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] In order to make the purpose, technical solutions and advantages of the embodiments of the present invention clearer, the technical solutions in the embodiments of the present invention will be clearly and completely described below in conjunction with the drawings in the embodiments of the present invention. Obviously, the described embodiments It is a part of embodiments of the present invention, but not all embodiments. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0029] Embodiments of the present invention provide a shear edge rolling strengthening method of a metal sheet and a plate-shaped part produced therefrom, which can solve the problem in the related art that cracks cannot be prevented from originating from the shear edge tear zone.

[0030] see figure 1 As shown, a metal sheet shear edge roll...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a metal plate shearing edge rolling strengthening method and a plate-shaped part manufactured through the same. The method comprises the steps that a rolling wheel is installed on rolling equipment, the rolling wheel is driven to move to make contact with a shearing edge of a metal plate, and the rolling wheel is enabled to keep thrust F in the moving direction of the rolling wheel; and the metal plate is driven to move close to the rolling wheel in the direction perpendicular to the thrust F, meanwhile, the rolling wheel rolls the edge of the shearing edge to form a chamfer, and the included angle between the rolling face of the rolling wheel and the plate face of the metal plate ranges from 30 degrees to 45 degrees. According to the metal plate shearing edge rolling strengthening method and the plate-shaped part manufactured through the same, burrs on the edge of the shearing edge can be removed, the shearing edge can be thinned in the thickness direction, residual pressure stress is formed on the whole shearing edge, and therefore the fatigue strength of the shearing edge of the plate-shaped part is greatly improved.

Description

technical field [0001] The invention relates to the field of mechanical engineering, in particular to a metal plate shearing edge rolling strengthening method and a plate-shaped part produced therefrom. Background technique [0002] Shear edge cracking of high-strength steel plates can occur in two situations. First, in the stamping process, the so-called steel plate flange elongation or hole expansion rate detection is to reflect the cracking tendency of the shear edge in the stamping process; Cutting edge cracking can also occur during the service of the part, which is generally a fatigue fracture mode at this time. [0003] Under service conditions, the fatigue life or fatigue strength of stamping parts originating from the shearing edge will be significantly lower than that of the smooth edge, which is related to the microscopic morphology and stress state of the shearing edge burr and shearing edge tear zone, and is also related to the material Generally, the higher t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23P9/02
CPCB23P9/02
Inventor 高亮庆李少兵李栋炎张先国莫莉赵策杨亮波欧阳可居刘成虎梁立新
Owner DONGFENG COMML VEHICLE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap