Super-yellowing-resistant high-rigidity UV fully-bright transparent finishing coat and preparation method thereof

A transparent topcoat and high hardness technology, applied in the field of UV paint, can solve the problems of being easily damaged, affecting the use of dining tables and tea tables, and affecting the color of 3D printing patterns, etc.

Active Publication Date: 2020-11-24
东莞大宝化工制品有限公司 +1
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the existing UV paint has poor yellowing resistance, which will affect the color of these 3D printing patterns, and then affect the decorative effect of the 3D printing patterns. Moreover, the paint film hardness of the existing UV paint is generally only about 2H. Under the action of external force, it is easy to be damaged, and these 3D printing patterns cannot be firmly protected, which will affect the use of dining tables, coffee tables, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Super-yellowing-resistant high-rigidity UV fully-bright transparent finishing coat and preparation method thereof
  • Super-yellowing-resistant high-rigidity UV fully-bright transparent finishing coat and preparation method thereof
  • Super-yellowing-resistant high-rigidity UV fully-bright transparent finishing coat and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] A kind of super-yellowing-resistant high-hardness UV full-bright transparent topcoat of the present embodiment is made up of the following raw materials in parts by weight:

[0042] 20 parts of bisphenol A epoxy acrylate;

[0043] 10 parts of amino-modified epoxy acrylate;

[0044] 0.65 parts of isobornyl acrylate;

[0045] 6.5 parts of neopentyl glycol diacrylate;

[0046] 13 parts of three (2-hydroxyethyl) isocyanuric acid triacrylates;

[0047] 3 parts of photoinitiator;

[0048] 0.2 part of defoamer;

[0049] 0.3 parts of anti-settling agent;

[0050] Among them, the amino-modified epoxy acrylate is 6100D-80 produced by Jiangmen Hengguang New Material Co., Ltd.;

[0051] Wherein, the photoinitiator is 2-hydroxyl-methylphenylpropane-1-one.

[0052] The preparation method of the super-yellowing-resistant high-hardness UV full-bright transparent topcoat of the present embodiment comprises the following steps:

[0053] Step 1: adding the bisphenol A epoxy acryla...

Embodiment 2

[0057] A kind of super-yellowing-resistant high-hardness UV full-bright transparent topcoat of the present embodiment is made up of the following raw materials in parts by weight:

[0058] 25 parts of bisphenol A epoxy acrylate;

[0059]16 parts of amino-modified epoxy acrylate;

[0060] 3.6 parts of isobornyl acrylate;

[0061] 9 parts of neopentyl glycol diacrylate;

[0062] 13.4 parts of three (2-hydroxyethyl) isocyanuric acid triacrylates;

[0063] 3.6 parts of photoinitiator;

[0064] 0.3 part of defoamer;

[0065] Wetting agent 0.4 parts;

[0066] Dispersant 0.5 part.

[0067] Among them, the amino-modified epoxy acrylate is 6100D-80 produced by Jiangmen Hengguang New Material Co., Ltd.;

[0068] Wherein, the photoinitiator is composed of 2-hydroxy-methylphenylpropan-1-one and 2,4,6-trimethylbenzoyl-diphenylphosphine oxide in a mass ratio of 1:0.2.

[0069] Refer to Example 1 for the preparation method of the super-yellowing-resistant high-hardness UV full-bright...

Embodiment 3

[0071] A kind of super-yellowing-resistant high-hardness UV full-bright transparent topcoat of the present embodiment is made up of the following raw materials in parts by weight:

[0072] 30 parts of bisphenol A epoxy acrylate;

[0073] 18 parts of amino-modified epoxy acrylate;

[0074] 2.7 parts of isobornyl acrylate;

[0075] 13.5 parts of neopentyl glycol diacrylate;

[0076] 13.8 parts of three (2-hydroxyethyl) isocyanuric acid triacrylates;

[0077] 4 parts of photoinitiator;

[0078] 0.3 part of defoamer;

[0079] Wetting agent 0.4 parts;

[0080] Dispersant 0.8 parts.

[0081] Among them, the amine-modified epoxy acrylate is Yatumei YTM2087 produced by Guangdong Libang Changrunfa Technology Materials Co., Ltd.;

[0082] Wherein, the photoinitiator is composed of 2-hydroxy-methylphenylpropane-1-one and 1-hydroxy-cyclohexyl-phenyl ketone in a mass ratio of 1:0.5.

[0083] Refer to Example 1 for the preparation method of the super-yellowing-resistant high-hardnes...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of UV paints, and provides a super-yellowing-resistant high-rigidity UV fully-bright transparent finishing coat and a preparation method thereof. The super-yellowing-resistant high-rigidity UV fully-bright transparent finishing coat consists of the following raw materials in parts by weight: 20-40 parts of bisphenol A epoxy acrylate, 10-20 parts of amino-modified epoxy acrylate, 20-40 parts of an acrylate monomer, 3-5 parts of a photoinitiator and 0.5-2 parts of additives, wherein the acrylate monomer consists of isobornyl acrylate, neopentyl glycoldiacrylate and tri(2-hydroxyethyl)isocyanurate triacrylate in a mass ratio of (0.1-0.6) to 1 to (0.8-2); and the additives are one or more of a defoamer, a wetting agent, a dispersing agent and an anti-settling agent. The super-yellowing-resistant high-rigidity UV fully-bright transparent finishing coat has good plumpness, adhesive force and pollution resistance, excellent yellowing resistance and high rigidity and can be applied to 3D printing patterns on dining tables, tea tables and the like.

Description

technical field [0001] The invention relates to the technical field of UV paint, in particular to a super-yellowing-resistant high-hardness UV full-bright transparent topcoat and a preparation method thereof. Background technique [0002] With the improvement of people's awareness of environmental protection, the use of non-renewable raw materials such as wood and stone is less and less. Therefore, the countertops of dining tables and coffee tables are increasingly replaced with renewable raw materials such as glass and synthetic stone. . At present, young people have become the mainstream consumer group, and they prefer products such as dining tables and coffee tables with simple patterns and single colors. The use of 3D printing technology to prepare patterns on dining tables, coffee tables, etc. has the advantages of environmental protection, high efficiency, uniform color, etc., and can meet the consumption needs of young people, so it is widely used. [0003] In order...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D163/10C09D5/16
CPCC09D163/10C09D5/1662C08L2205/025C08L2201/10C08L63/10
Inventor 鲁宁林进辉
Owner 东莞大宝化工制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products