Ramie bone nanocrystalline cellulose aerogel and preparation method thereof

A technology of nanocrystalline cellulose and ramie bone, applied in the field of thermal insulation materials, can solve the problems of large pore structure, poor thermal insulation effect, high thermal conductivity, etc.

Inactive Publication Date: 2020-10-20
WUHAN TEXTILE UNIV
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, bioaerogels prepared by supercritical drying method have low thermal conductivity and good thermal insulation effect, but special supercritical drying equipment is required, and the cost is high
However, bioaerogels prepared by the traditional vacuum freeze-drying method have larger pore structure, higher thermal conductivity, and poor thermal insulation effect.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ramie bone nanocrystalline cellulose aerogel and preparation method thereof
  • Ramie bone nanocrystalline cellulose aerogel and preparation method thereof
  • Ramie bone nanocrystalline cellulose aerogel and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0023] The invention provides a preparation method of ramie bone nanocrystalline cellulose airgel, comprising the following steps:

[0024] 1) osmotically concentrating the ramie bone nanocrystalline cellulose suspension to obtain ramie bone nanocrystalline cellulose hydrogel;

[0025] 2) The ramie bone nanocrystalline cellulose hydrogel obtained in the step 1) is sequentially subjected to spray freezing and vacuum freeze drying to obtain the ramie bone nanocrystalline cellulose aerogel.

[0026] The invention osmotically concentrates the ramie bone nanocrystalline cellulose suspension to obtain the ramie bone nanocrystalline cellulose hydrogel. The present invention uses ramie bone nanocrystalline cellulose suspension to prepare airgel, ramie bone resources are abundant, raw material resources are abundant, and the cost is cheap, which not only solves the problem of environmental pollution caused by ramie bone incineration, but also improves the comprehensive utilization valu...

Embodiment 1

[0046] Take 100g of ramie bone powder, add 500mL of distilled water, and steam-explode at 121°C for 20min; take 50g of pretreated ramie bone powder, add 1500mL of 10% NaOH solution, cook at 75°C for 6h, let it stand for 12h, and then filter it with suction. Soak the filter residue in 200mL distilled water for 2h, filter, repeat the operation 3 times, dry the filter residue to obtain ramie bone crude cellulose; take 30g ramie bone crude cellulose, add 750mL 5% H 2 o 2 React for 8 hours, then filter, rinse the filter residue with distilled water for 3 times, and dry the obtained ramie bone cellulose; take 2.0 g of ramie bone cellulose, add 20 mL of 68% sulfuric acid, and react with magnetic stirring at 55 ° C for 35 minutes, and control the stirring speed to 700 rpm. After cooling and standing for 5 hours, centrifuge at a speed of 5000 rpm for 10 minutes, remove the supernatant, wash the precipitate with an equal amount of distilled water, repeat the above centrifugation and was...

Embodiment 2

[0053] Get 20mL of the ramie bone nanocrystalline cellulose suspension prepared in Example 1 and place it in a 12kDa dialysis bag, immerse the dialysis bag in 15wt% dextran aqueous solution, replace the dextran aqueous solution once every 25h, until the ramie bone When the nanocrystalline cellulose concentration in the nanocrystalline cellulose suspension is 2.0 wt%, the osmotic concentration is completed, and the ramie bone nanocrystalline cellulose hydrogel is obtained;

[0054] The ramie bone nanocrystalline cellulose hydrogel was sprayed with a stainless steel nozzle with an inner diameter of 0.2 mm under a constant pressure of 1.3 bar and frozen in a liquid nitrogen freezing container at -80 ° C to obtain a frozen sample with a thickness of 1.2 cm. The sample was placed in a vacuum freeze dryer and dried for 24 hours at -55°C and a vacuum of less than 0.1 mbar to obtain ramie bone nanocrystalline cellulose airgel.

[0055] The measured density of ramie bone nanocrystallin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
pore sizeaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of ramie bone nanocrystalline cellulose aerogel, which comprises the following steps: carrying out osmotic concentration on a ramie bone nanocrystalline cellulose suspension, and sequentially carrying out spray freezing and vacuum freeze drying to obtain the ramie bone nanocrystalline cellulose aerogel. The ramie bone nanocrystalline cellulose suspensionliquid is used as a raw material; the osmotic concentration is carried out to obtain ramie bone nanocrystalline cellulose hydrogel; the hydrogel is instantly condensed into tiny frozen particles through spray freezing; ice crystal growth is prevented from damaging a gel structure, meanwhile, the pore diameter of the ramie bone nanocrystalline cellulose aerogel can be reduced to the nanoscale, thethermal conductivity of the aerogel is reduced, finally, the frozen particles are sublimated and dried through vacuum freeze drying, and then the ramie bone nanocrystalline cellulose aerogel with lowthermal conductivity is obtained. The results of the embodiment show that the ramie bone nanocrystalline cellulose aerogel prepared by the preparation method provided by the invention has a heat conductivity coefficient of 0.019 W / (m.K).

Description

technical field [0001] The invention relates to the technical field of thermal insulation materials, in particular to a ramie bone nanocrystalline cellulose airgel and a preparation method thereof. Background technique [0002] Cellulose has been widely used to make various materials due to its renewability, biocompatibility and biodegradability. Among them, the use of cellulose and its derivatives to prepare bioaerogels has also been widely studied. Some aerogels have low thermal conductivity and have great application potential as thermal insulation materials. [0003] In the prior art, common methods for preparing bioaerogels include supercritical drying and vacuum freeze-drying. Among them, bioaerogels prepared by supercritical drying method have low thermal conductivity and good thermal insulation effect, but special supercritical drying equipment is required, and the cost is high. However, bioaerogels prepared by the traditional vacuum freeze-drying method have a lar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08J9/28C08J3/075C08L1/04
CPCC08J9/28C08J3/075C08J2205/026C08J2201/0484C08J2301/04
Inventor 崔永明石从众赵逸飞王金凤唐彬陈悟董雄伟
Owner WUHAN TEXTILE UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com