Coating method of nickel cobalt lithium manganese oxide ternary cathode material

A technology of nickel-cobalt lithium manganese oxide and positive electrode materials, which is applied in the direction of positive electrodes, electrical components, battery electrodes, etc., can solve problems such as poor performance and uneven coating, and achieve reduced usage and cost, short process time, The effect of improving coating efficiency

Active Publication Date: 2022-04-15
HAIKE GRP RES INST OF INNOVATION & TECH
View PDF14 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention aims at the technical problems of uneven coating and poor performance after coating when coating nickel-cobalt lithium manganese oxide ternary positive electrode material in the above-mentioned background technology, and provides a coating of nickel-cobalt lithium manganese oxide ternary positive electrode material. method, uniform coating, good cycle performance after coating, simple operation, and easy industrial production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Coating method of nickel cobalt lithium manganese oxide ternary cathode material
  • Coating method of nickel cobalt lithium manganese oxide ternary cathode material
  • Coating method of nickel cobalt lithium manganese oxide ternary cathode material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] Fluidization of matrix material:

[0049] LiN with a particle size of 3 μm 0.50 co 0.20 mn 0.30 o 2 The finished material (produced by Peking University Xianxing Company) is added into the fluidized bed cavity through the upper feed fluidization port of the fluidized bed, and the frequency of the main air inlet fan of the blower, the auxiliary air inlet fan of the blower and the induced draft fan are set to 40Hz in turn , 50Hz and 20Hz, set the air inlet temperature of the blower to 200°C, so as to quickly dry the coated material. Both the motor frequency of the horizontal stirring paddle and the vertical stirring paddle are set to 50HZ. Set the fluidization time of the matrix material to 20 minutes, and the matrix material realizes disordered and uniform fluidization in the chamber under the multiple effects of the main air inlet of the blower and the auxiliary air inlet of the blower, its own gravity, horizontal stirring and vertical stirring.

[0050] Configure ...

Embodiment 2

[0056] Fluidization of matrix material:

[0057] LiNi with a particle size of 5 μm 0.60 co 0.20 mn 0.20 o 2 The finished material (produced by Peking University Xianxing Company) is added into the fluidized bed cavity through the upper feed fluidization port of the fluidized bed, and the frequency of the main air inlet fan of the blower, the auxiliary air inlet fan of the blower and the induced draft fan are set to 40Hz in turn , 50Hz and 20Hz, set the air inlet temperature of the blower to 180°C to quickly dry the coated material. Both the motor frequency of the horizontal stirring paddle and the vertical stirring paddle are set to 50HZ. Set the fluidization time of the matrix material to 40 minutes, and the matrix material realizes disordered and uniform fluidization in the cavity under the multiple actions of the main air inlet of the blower and the auxiliary air inlet of the blower, its own gravity, horizontal stirring and vertical stirring.

[0058] Configure coating...

Embodiment 3

[0070] The fluidization process of the matrix material and the process of configuring the coating solution are the same as in Example 2.

[0071] Coating and Drying:

[0072] The coating solution was fed into the cavity from the top and middle atomization ports of the fluidized bed by a top-middle common atomization method through a peristaltic pump, and the feeding rate was 25 mL / min. The coating solution is atomized to coat the matrix material, and the coating solution is completely atomized and dried at 80° C. for 20 minutes. Stop the blower, induced draft fan, and vertical paddle motor successively, and set the frequency of the horizontal paddle motor to discharge frequency 15Hz. Open the discharge port, take out the dry coating material and turn off the horizontal stirring paddle motor.

[0073] The coated material was sintered at 750° C. for 7 hours in an air atmosphere, and the sintered material was crushed to obtain a coated nickel-cobalt-lithium-manganese-oxide tern...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a coating method for a nickel-cobalt lithium manganate ternary positive electrode material, and belongs to the technical field of lithium-ion battery electrode material preparation. The method includes: 1) adding a nickel-cobalt lithium manganate ternary positive electrode material into a cavity of a fluidized bed for fluidization to obtain a fluidized nickel-cobalt lithium manganate ternary positive electrode material; 2) coating the The solution is atomized at the atomization port of the fluidized bed to obtain the coating solution after the atomization; 3) the coating solution after the atomization is added to the cavity of the fluidized bed to convect the nickel-cobalt lithium manganate in the fluidized state. The element positive electrode material is spray-coated and dried to obtain a coated nickel-cobalt lithium manganate ternary positive electrode material. The catalyst prepared by the invention has high activity, the catalyst is easy to separate after the reaction, can be reused, and has simple preparation process and low cost.

Description

technical field [0001] The invention relates to the technical field of preparation of lithium-ion battery electrode materials, in particular to a coating method for nickel-cobalt-lithium-manganese-oxide ternary positive electrode materials. Background technique [0002] Lithium-ion batteries are composed of positive electrode materials, negative electrode materials, electrolytes, separators, casings, etc., and the performance of positive electrode materials directly determines the energy density of lithium-ion batteries. Nickel-cobalt lithium manganate ternary cathode material, as the "dark horse" of lithium battery cathode materials that has emerged in recent years, has attracted extensive research due to its incomparable advantages such as high energy density and power density, and excellent cycle performance. And has been successfully applied in the field of electric vehicle passenger vehicles. However, due to the characteristics of the ternary material's own structure, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/36H01M4/505H01M4/525H01M4/62H01M10/0525
CPCH01M4/366H01M4/505H01M4/525H01M4/62H01M4/628H01M10/0525H01M2004/021H01M2004/028Y02E60/10
Inventor 崔云龙苗力孝牛庆荣魏志凯谢芳鞠署元
Owner HAIKE GRP RES INST OF INNOVATION & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com