A kind of in-situ synthesis aluminum carbide reinforced aluminum matrix composite material and preparation method thereof

A composite material and reinforced aluminum-based technology, which is applied in the field of in-situ synthesis of aluminum carbide Al4C3 reinforced aluminum-based composite materials and its preparation, can solve the problems of unspecified thermal stability and high-temperature mechanical properties of composite materials, and achieve improved interface wetness. Wet and interfacial bonding strength, broad application prospects, effects of high room temperature strength and high temperature mechanical properties

Active Publication Date: 2021-02-02
SHANGHAI JIAOTONG UNIV
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The Chinese patent with the publication number CN 109680188 A discloses an aluminum oxide layer-coated nano-aluminum carbide particle-reinforced aluminum-based composite material and its preparation method, using graphite powder and activated carbon as carbon sources to react to obtain composite reinforcement of alumina and aluminum carbide. The aluminum matrix composite material, this method does not give the thermal stability and high temperature mechanical properties of the composite material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of in-situ synthesis aluminum carbide reinforced aluminum matrix composite material and preparation method thereof
  • A kind of in-situ synthesis aluminum carbide reinforced aluminum matrix composite material and preparation method thereof
  • A kind of in-situ synthesis aluminum carbide reinforced aluminum matrix composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] This embodiment provides a kind of in situ synthesis Al 4 C 3 Reinforced aluminum matrix composites, including aluminum powder and graphene powder, the volume fraction of graphene powder is 0.8%, and aluminum powder and graphene powder generate nanoscale Al with dispersed distribution through in-situ reaction 4 C 3 , nanoscale Al 4 C 3 It is distributed in the composite material in two forms, one of which is that the two ends of the rod-shaped shape grow into the two aluminum grains respectively, pinning two adjacent aluminum grains, and the other is that the rod-shaped length direction is along the grain Boundary arrangement can effectively prevent dislocation and grain boundary migration.

[0029] In-situ synthesis of Al in the foregoing examples 4 C 3 Reinforced aluminum matrix composites can be prepared by the following methods, including the following specific steps:

[0030] S1: Select aluminum powder with a ball diameter of 200 mesh and graphene powder wit...

Embodiment 2

[0035] This embodiment provides a kind of in situ synthesis Al 4 C 3 Reinforced aluminum matrix composites, including aluminum powder and graphene powder, the volume fraction of graphene powder is 1.5%, and aluminum powder and graphene powder generate nanoscale Al dispersedly distributed through in-situ reaction 4 C 3 , nanoscale Al 4 C 3 It is distributed in the composite material in two forms, one of which is that the two ends of the rod-shaped shape grow into the two aluminum grains respectively, pinning two adjacent aluminum grains, and the other is that the rod-shaped length direction is along the grain Boundary arrangement can effectively prevent dislocation and grain boundary migration.

[0036] In-situ synthesis of Al in the foregoing examples 4 C3 Reinforced aluminum matrix composites can be prepared by the following methods, including the following specific steps:

[0037] S1: Select aluminum powder with a ball diameter of 200 mesh and graphene powder with a sh...

Embodiment 3

[0045] This embodiment provides a kind of in situ synthesis Al 4 C 3 Reinforced aluminum matrix composites, including aluminum powder and graphene powder, the volume fraction of graphene powder is 2%, and aluminum powder and graphene powder generate nanoscale Al with dispersed distribution through in-situ reaction 4 C 3 , nanoscale Al 4 C 3 It is distributed in the composite material in two forms, one of which is that the two ends of the rod-shaped shape grow into the two aluminum grains respectively, pinning two adjacent aluminum grains, and the other is that the two ends of the rod-shaped shape grow along the crystal grains. Boundary arrangement can effectively prevent dislocation and grain boundary migration.

[0046] In-situ synthesis of Al in the foregoing examples 4 C 3 Reinforced aluminum matrix composites can be prepared by the following methods, including the following specific steps:

[0047] S1: Select aluminum powder with a spherical diameter of 1-2 μm and a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
hardnessaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides an in-situ synthesis of aluminum carbide-reinforced aluminum-based composite material and a preparation method thereof, comprising aluminum powder and graphene powder, wherein the aluminum powder and graphene powder generate dispersedly distributed Al with nanoscale through in-situ reaction 4 C 3 , nanoscale Al 4 C 3 It is distributed in the composite material in two forms, one of which is that the two ends of the rod-shaped shape grow into the two aluminum grains respectively, pinning two adjacent aluminum grains, and the other is that the two ends of the rod-shaped shape grow along the crystal grains. Boundary arrangement can effectively prevent dislocation and grain boundary migration. In one aspect of the present invention, nanoscale Al 4 C 3 Effectively pin the grain boundary migration of the Al matrix, retain the strength of the Al matrix, and at the same time, Al 4 C 3 As a hard reinforcing phase, the composite material has high room temperature strength and high-temperature mechanical properties due to the stress bearing and Orowan effect, and the composite material has broad application prospects in the fields of aerospace and other high-service temperature conditions.

Description

technical field [0001] The invention relates to the technical field of heat-resistant metal matrix composite materials, in particular to an in-situ synthesis of aluminum carbide Al 4 C 3 Reinforced aluminum matrix composite material and its preparation method. Background technique [0002] Heat-resistant aluminum alloys are widely used in the aerospace field due to their high strength and good heat resistance. However, when the working temperature exceeds 200°C, the coarsening of the main strengthening phase significantly reduces the mechanical properties, and it is difficult to meet the requirements of the new generation of aircraft, propellers and other structural components for the operating temperature. Therefore, the development has higher room temperature strength and better Aluminum alloys and aluminum matrix composites with excellent damage resistance, excellent heat resistance and thermal stability have become one of the current research hotspots of aluminum alloy...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/00C22C1/05C22C1/10B22F9/04B22F3/14B22F3/105B22F3/20B22F3/18
CPCB22F3/105B22F3/14B22F3/18B22F3/20B22F9/04B22F2003/1051B22F2009/043C22C1/055C22C21/00
Inventor 高海燕李敏张驰王朦朦吕海洋王宇飞王俊孙宝德
Owner SHANGHAI JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com