A kind of high-strength high-plastic single-phase inconel 625 nickel-based alloy and its preparation method

A nickel-based alloy, high plasticity technology, used in metal processing equipment, manufacturing tools, additive manufacturing, etc., can solve the problem of low strength of Inconel625 nickel-based alloy, achieve good plasticity, high yield strength and tensile strength, tensile strength, tensile strength Excellent strength

Active Publication Date: 2021-05-28
NANJING ENIGMA IND AUTOMATION TECH CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The preparation of Inconel 625 nickel-based alloy by this method has higher efficiency to a certain extent, but the strength of the prepared Inconel 625 nickel-based alloy is lower

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-strength high-plastic single-phase inconel 625 nickel-based alloy and its preparation method
  • A kind of high-strength high-plastic single-phase inconel 625 nickel-based alloy and its preparation method
  • A kind of high-strength high-plastic single-phase inconel 625 nickel-based alloy and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] The single-phase Inconel 625 nickel-based alloy with a coarse-grained columnar crystal structure is obtained by rapidly depositing and depositing layer by layer on the carbon steel substrate according to the set path under the protection of protective gas by using the method of arc-added material. The crystal structure has high strength and high plasticity. The chemical elements in the nickel-based alloy are measured by atomic percentage (at.%) as follows: Ni:>58.00%, Cr:20.00-23.00%, Mo:8.00-10.00%, Nb:3.15-4.15%, Fe:≤5.00 %, Co: ≤1.00%, Si: ≤0.50%, Mn: ≤0.50%, Ti: ≤0.40%, Al: ≤0.40%, Cu: ≤0.30%, C: ≤0.10%, S: ≤0.02%, P:≤0.02%, Ta:≤0.02%.

[0041] The arc process parameters are as follows: CMT MIG process is adopted, and the wire is NiCrMo-3 (625 nickel-based alloy) wire with a diameter of 1.2 mm. The printing adopts ArcMan 600 equipment, its process is DC CMT, and the arc additive software used is IungoPNT. The welding expert library version used in the experiment ...

Embodiment 2

[0045] The difference from Example 1 is:

[0046] Inconel 625 nickel-based alloy with columnar crystal single-phase structure with a high proportion of small-angle grain boundaries is obtained by rapidly depositing layer by layer on the carbon steel substrate according to the set path under the protection of protective gas by using arc additive technology. The columnar grain structure with angled grain boundaries has the characteristics of high strength and high plasticity. The arc process parameters are as follows: CMT MIG process is adopted, and the wire is NiCrMo-3 (625 nickel-based alloy) wire with a diameter of 1.2mm. The printing process adopts ArcMan 600 equipment, its process is DC CMT, and the arc additive software used is IungoPNT. The welding expert library version used in the experiment is 1693 (NIBAS625), the wire feeding speed is 4.6m / min, the arc length correction is 0, and the inductance correction is 0. Then, the obtained material was subjected to solution t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of arc-added metal materials, in particular to a high-strength and high-plastic single-phase Inconel 625 nickel-based alloy and a preparation method thereof. The invention discloses a high-strength and high-plasticity single-phase Inconel 625 nickel-based alloy, wherein the structure of the Inconel 625 nickel-based alloy is a single-phase columnar coarse-grained structure, and its grain size is 45-360 μm. In percentage terms, the grains have small-angle grain boundaries in a proportion of 15-33%. The invention also discloses a preparation method of the Inconel 625 nickel base alloy. The tensile strength of the Inconel 625 nickel-based alloy obtained according to this method is 720-730MPa, the yield strength is 390-415MPa, and the elongation is 54-63%. Compared with the traditional cast 625 nickel-based alloy, it significantly improves the strength and plasticity.

Description

technical field [0001] The invention relates to the technical field of arc-added metal materials, in particular to a high-strength and high-plastic single-phase Inconel 625 nickel-based alloy and a preparation method thereof. Background technique [0002] Inconel 625 nickel-based alloy has excellent comprehensive mechanical properties, good oxidation resistance and corrosion resistance, and is widely used in industrial fields such as aerospace and machinery manufacturing. The traditional preparation process of Inconel 625 nickel-based alloy parts mainly includes isomaterial manufacturing (casting, rolling, etc.) technology and subtractive manufacturing (turning, milling, etc.) technology, etc. Inconel 625 nickel-based alloy prepared by traditional technology has a relatively excellent comprehensive Mechanical properties, but the process is cumbersome and the production efficiency is low. At the same time, it is difficult to process components with complex shapes and the prod...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C19/05B22F10/22B22F10/36B23K9/167B23K9/133B23K9/32B33Y10/00B33Y70/00
CPCB23K9/133B23K9/167B23K9/32B33Y10/00B33Y70/00C22C19/055
Inventor 程远袁玉荣
Owner NANJING ENIGMA IND AUTOMATION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap