Water-based two-component polyurethane paint for galvanized plates and preparation method of water-based two-component polyurethane paint

A two-component polyurethane and water-based isocyanate technology, applied in the field of coatings, can solve the problems of poor weather resistance and poor adhesion, and achieve the effects of good adhesion, good water resistance and excellent water resistance.

Active Publication Date: 2020-05-01
GUANGZHOU JOINTAS CHEM
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to overcome the problems of poor adhesion and poor weather resistance of the current galvanized sheet coating, one of the purposes of the present invention is to provide a water-based two-component polyurethane paint for galvanized sheets, and the second object of the present invention is to provide this Preparation method of water-based two-component polyurethane paint for galvanized sheet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based two-component polyurethane paint for galvanized plates and preparation method of water-based two-component polyurethane paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] This example is a water-based two-component polyurethane coating, including A component and B component, the mass ratio of A component and B component is 8:1, and the compositions of A component and B component are as follows:

[0045] Component A includes the following components in parts by mass: 53 parts of aqueous hydroxyacrylic acid dispersion, 0.8 part of wetting and dispersing agent, 1 part of defoamer, 0.5 part of pH regulator, 6 parts of cosolvent, 25 parts of pigment and filler, 1 part of leveling agent, 1 part of thickener, 1.5 parts of adhesion promoter and 10 parts of deionized water;

[0046] B component is water-based isocyanate curing agent.

[0047] The raw materials used are described as follows:

[0048] Waterborne hydroxyacrylic acid dispersion: Antkote 2035 hydroxyacrylic acid dispersion of Yantai Wanhua Group Co., Ltd.;

[0049] Curing agent: WL72-100 from Asahi Kasei, Japan;

[0050] Wetting and dispersing agent: Digo 750w wetting and dispersin...

Embodiment 2

[0064] This example is a water-based two-component polyurethane coating, which includes component A and component B. The mass ratio of component A to component B is 8.2:1. The compositions of component A and component B are as follows:

[0065] Component A includes the following components in parts by mass: 58 parts of aqueous hydroxyacrylic acid dispersion, 0.8 part of wetting and dispersing agent, 1 part of defoamer, 0.5 part of pH regulator, 5 parts of cosolvent, 25 parts of pigment and filler, 1 part of leveling agent, 0.8 parts of thickener, 1.5 parts of adhesion promoter and 6 parts of deionized water.

[0066] B component is water-based isocyanate curing agent.

[0067] The raw materials used are described as follows:

[0068] Waterborne hydroxyacrylic acid dispersion: Antkote 2035 hydroxyacrylic acid dispersion of Yantai Wanhua Group Co., Ltd.;

[0069] Curing agent: WL72-100 from Asahi Kasei, Japan;

[0070] Wetting and dispersing agent: Digo 750w wetting and dispe...

Embodiment 3

[0084] This example is a water-based two-component polyurethane coating, including A component and B component, the mass ratio of A component and B component is 7:1, and the compositions of A component and B component are as follows:

[0085] Component A, including the following components in parts by mass: 50 parts of water-based hydroxyacrylic acid dispersion, 0.8 parts of wetting and dispersing agent, 1 part of defoamer, 0.5 parts of pH regulator, 5 parts of cosolvent, 25 parts of pigments and fillers, 1 part of leveling agent, 1 part of thickener, 1.5 parts of adhesion promoter and 14 parts of deionized water.

[0086] B component is water-based isocyanate curing agent.

[0087] The raw materials used are described as follows:

[0088] Waterborne hydroxyacrylic acid dispersion: Antkote 2035 hydroxyacrylic acid dispersion of Yantai Wanhua Group Co., Ltd.;

[0089] Curing agent: WL72-100 from Asahi Kasei, Japan;

[0090] Wetting and dispersing agent: Digo 750w wetting and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Pencil hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses water-based two-component polyurethane paint for galvanized plates and a preparation method of the water-based two-component polyurethane paint. The water-based two-component polyurethane paint comprises a component A and a component B, wherein the mass ratio of the component A to the component B is (6.4-9.6):1; the component A comprises the following components: a water-based hydroxy acrylic acid dispersion, a wetting dispersant, an antifoaming agent, a pH regulator, a cosolvent, a pigment filler, a leveling agent, a thickener, an adhesion promoter and water; the wetting dispersant is a segmented copolymer aqueous solution containing pigment affinity groups; the adhesion promoter contains an active group capable of reacting with hydroxyl and / or carboxyl in the water-based hydroxyl acrylic acid dispersion; the component B is a water-based isocyanate curing agent. Meanwhile, the invention also discloses a preparation method of the water-based two-component polyurethane paint for the galvanized sheet. The waterborne polyurethane coating disclosed by the invention has the characteristics of being good in adhesive force to galvanized plates, outstanding in yellowing resistance and aging resistance and excellent in water resistance.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a water-based two-component polyurethane paint for galvanized sheets and a preparation method thereof. Background technique [0002] As a plate with good strength and flexibility, galvanized sheet is widely used in prefabricated houses, living boxes and other fields. Since the galvanized sheet itself has a galvanized layer, its anti-corrosion performance is better, but the residential box and the prefabricated house generally need to be sprayed with a layer of paint for the sake of beauty. The coating needs to have good adhesion to the galvanized layer. Excellent weather resistance and certain water resistance. Among them, the adhesion of the coating to the galvanized layer, especially the adhesion of the coating after soaking in water is particularly critical. The lack of adhesion makes the coating easy to fall off, which directly affects the service life of the board room. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D175/04C09D7/65C09D7/63C09D7/80C08G18/62
CPCC08G18/6216C08L2205/025C08L2205/035C09D175/04C09D7/63C09D7/65C09D7/80C08L75/04C08L101/00C08K5/5435
Inventor 王建川陈剑华陈卓崔晓帆余飞
Owner GUANGZHOU JOINTAS CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com