Antibacterial foam dressing and preparation method thereof
A foam and foam stabilizer technology, which is applied in the fields of medical science, bandages, absorbent pads, etc., can solve the problems of difficult release and poisoning of metal particles, and achieve the effects of saving medical expenses, simple preparation method and large contact surface area.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0040] (1) Disperse 0.05g of copper powder with a particle size of 0.5μm in 100g of Bayhydur 305 and stir evenly to obtain component A;
[0041] (2) Water, 1,4 butanediol, K2800, B8110, 33LV mixed evenly to obtain component B;
[0042] (3) 100g A component and 100g B component are mixed with 6000rpm high-shear stirring speed in a dynamic mixer, and react to obtain C component;
[0043] (4) Quickly extrude component C onto the release paper to form a foam, adjust the thickness of the foam to 10mm, and then dry it at 105°C for 3 minutes to obtain an antibacterial foam dressing. The foaming density of the antibacterial foam dressing is 120kg / m 3 , The diameter of the open cell is 0.8mm.
Embodiment 2
[0045] (1) Disperse 3 g of zinc-copper alloy powder with a particle size of 10 μm and a copper content of 80% in 100 g of Bayhydur BL5140, and stir evenly to obtain component A;
[0046] (2) Water, ethylene glycol, K757, DC6070, Mix A-1 evenly to obtain component B;
[0047] (3) Mix 50g of component A with 100g of component B in a dynamic mixer at a high-shear stirring speed of 6000rpm, and react to obtain component C;
[0048] (4) Quickly extrude component C onto the release paper to form a foam, adjust the thickness of the foam to 10mm, and then dry it at 105°C for 5 minutes to obtain an antibacterial foam dressing. The foaming density of the antibacterial foam dressing is 50kg / m 3 , The diameter of the open cell is 3mm.
Embodiment 3
[0050] (2) Disperse 5g of zinc powder with a particle size of 60μm in 100g of WanCURE TP611 and stir evenly to obtain component A;
[0051] (2) Water, 1,6 hexanediol, Y-1900, PM-300, Mix AN-33 evenly to obtain component B;
[0052] (3) 100g A component and 50g B component are mixed with 6000rpm high-shear stirring speed in a dynamic mixer, and react to obtain C component;
[0053] (4) Quickly extrude component C onto the release paper to form a foam, adjust the thickness of the foam to 10mm, and then dry it at 105°C for 10 minutes to obtain an antibacterial foam dressing. The foaming density of the antibacterial foam dressing is 300kg / m 3 , The diameter of the open cell is 0.05mm.
PUM
Property | Measurement | Unit |
---|---|---|
density | aaaaa | aaaaa |
diameter | aaaaa | aaaaa |
viscosity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com