Special waterproof antibacterial adhesive for wood products and preparation method thereof

A technology for wood products and antibacterial glue, applied in the directions of adhesive additives, adhesive types, starch adhesives, etc. Long waterproof life, good inhibition, enhanced light resistance and long-term effects

Active Publication Date: 2020-04-10
肖可牧
View PDF12 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Both of the above two adhesives have certain adhesion and water resistance, but their corrosion resistance and waterproof performance are poor, and they cannot be antibacterial for a long time, and their service life is short.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Special waterproof antibacterial adhesive for wood products and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A special waterproof and antibacterial adhesive for wood products, made of raw materials in parts by weight as shown in Table 1. Wherein, the antibacterial agent is composed of 4,5-dichloro-2-n-octyl-4-isothiazolin-3-one, nano-titanium dioxide, nano-silver and a coupling agent. The anticorrosion agent is sodium diacetate. The waterproofing agent is sodium methyl siliconate.

[0024] The preparation method of the special waterproof and antibacterial adhesive for wood products comprises the following steps:

[0025] S1: After mixing glutinous rice flour, sweet potato starch, and 3 / 4 parts by weight of water, put it in a mixer at a temperature of 60°C and a speed of 100 r / min and stir for 20 minutes to obtain a mixed slurry 1;

[0026] S2: After the mixed slurry 1 drops to room temperature, add polyvinyl alcohol and the remaining 1 / 2 parts by weight of water to mix, and stir at room temperature at a speed of 200r / min for 30min to obtain the mixed slurry 2;

[0027] S3: ...

Embodiment 2

[0029]A special waterproof and antibacterial adhesive for wood products, made of raw materials in parts by weight as shown in Table 1. Wherein, the antibacterial agent is composed of 2-n-octyl-4-isothiazol-3 ketone, nano-titanium dioxide, nano-silver and a coupling agent. The anti-corrosion agent is butyl p-hydroxybenzoate. The waterproofing agent is polybutylene succinate.

[0030] The preparation method of the special waterproof and antibacterial adhesive for wood products comprises the following steps:

[0031] S1: After mixing glutinous rice flour, sweet potato starch, and 3 / 4 parts by weight of water, place it in a mixer at a temperature of 65° C. and stir at a speed of 150 r / min for 15 minutes to obtain a mixed slurry 1;

[0032] S2: After the mixed slurry 1 drops to room temperature, add polyvinyl alcohol and the remaining 1 / 2 parts by weight of water to mix, and stir at room temperature at a speed of 250r / min for 25min to obtain the mixed slurry 2;

[0033] S3: Mix ...

Embodiment 3

[0035] A special waterproof and antibacterial adhesive for wood products, made of raw materials in parts by weight as shown in Table 1. Wherein, the antibacterial agent is composed of n-butylbenzisothiazolinone, nano-titanium dioxide, nano-silver, and a coupling agent. The anticorrosion agent is sodium diacetate. The waterproofing agent is polybutylene succinate.

[0036] The preparation method of the special waterproof and antibacterial adhesive for wood products comprises the following steps:

[0037] S1: After mixing glutinous rice flour, sweet potato starch, and 3 / 4 parts by weight of water, place it in a mixer at a temperature of 70° C. and stir at a speed of 200 r / min for 10 minutes to obtain a mixed slurry 1;

[0038] S2: After the mixed slurry 1 drops to room temperature, add polyvinyl alcohol and the remaining 1 / 2 parts by weight of water to mix, and stir at room temperature at a speed of 300r / min for 20min to obtain the mixed slurry 2;

[0039] S3: Mix the anti-co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a special waterproof antibacterial adhesive for wooden products and a preparation method of the special waterproof antibacterial adhesive, and belongs to the technical field ofadhesive. The special waterproof antibacterial adhesive for wooden products is prepared from the following raw materials in parts by weight: 55 to 65 parts of glutinous rice flour, 20 to 28 parts of sweet potato starch, 10 to 15 parts of polyvinyl alcohol, 4 to 6 parts of an anti-corrosion agent, 2 to 3 parts of a waterproof agent, 2.7 to 3.5 parts of an antibacterial agent, 22 to 30 parts of a biological adhesive, and 360 to 380 parts of water. The special waterproof antibacterial adhesive is excellent in comprehensive performance, waterproof, corrosion-resistant, excellent in antibacterial effect and good in stability, and has a good inhibition effect on escherichia coli and staphylococcus aureus.

Description

technical field [0001] The invention relates to the technical field of adhesives, in particular to a special waterproof and antibacterial adhesive for wood products and a preparation method thereof. Background technique [0002] With the continuous improvement of people's living standards, the application of wood products is becoming more and more extensive. In the process of making wood products, a large amount of adhesive is needed. Through the adhesion and cohesion of the interface, two or more parts or Materials are joined together. At present, the commonly used adhesives on the market are mainly "tripolymer glue", which will release carcinogens and seriously affect the environment and human health. Subsequently, polyurethane adhesives appeared, which have the advantages of good flexibility and high tensile strength. However, during long-term use, this type of adhesive is affected by its own raw materials and the surrounding environment, which easily leads to bacterial ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J103/02C09J129/04C09J103/06C09J11/06C09J11/04C09J11/08
CPCC08K2003/0806C08K2003/2241C08K2201/011C08L2205/025C08L2205/035C09J11/04C09J11/06C09J11/08C09J103/02C08L3/02C08L29/04C08L3/06C08K13/02C08K5/47C08K3/22C08K3/08C08K5/098C08K5/5419C08L67/02C08K5/1345
Inventor 肖可牧
Owner 肖可牧
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap