A kind of progressive expansion liquid expansion agent and preparation method thereof

A technology for liquid expansion and powder mixing, which is applied in the field of building materials, can solve the problems of shrinkage and cracking of concrete, large amount of finely ground fly ash and slag powder, and troublesome concrete, so as to avoid excessive local expansion stress. , good penetration performance, the effect of improving strength

Active Publication Date: 2021-09-03
HUBEI UNIV OF TECH
View PDF16 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, fiber-mixed concrete is cumbersome and costly, and the amount of finely ground fly ash and slag powder is large, which requires high cost and cannot completely solve the shrinkage and cracking of concrete.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of progressive expansion liquid expansion agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 2

[0055] A method for preparing a step-by-step expansion liquid expansion agent, the total mass of raw materials is 100 parts, the solid content is about 10%, and it is mainly prepared from the following components:

[0056] 700 ℃ nano magnesium oxide powder: 1.0 part

[0057] 900℃ nano magnesium oxide powder: 0.8 part

[0058] 1100℃ nano magnesium oxide powder: 0.5 part

[0059] Butanol: 0.2 parts

[0060] Dimethicone: 0.3 parts

[0061] Span 80: 0.3 servings

[0062] Polypropylene alcohol 400: 0.6 part

[0063] Dodecyl polyoxyethylene ether: 2.6 parts

[0064] Propylene Glycol Methyl Ether: 2.6 parts

[0065] Polyacrylamide: 1.2 parts

[0066] Step 1: Weigh 1.0 part of 700 ℃ nanometer magnesium oxide powder, 0.8 part of 900 ℃ nanometer magnesium oxide powder, 0.5 part of 1100 ℃ nanometer magnesium oxide powder, 0.2 part of butanol, 0.3 part of dimethyl silicone oil, 0.3 part of simethicone Disk 80 and 90 parts of water were placed in the reaction kettle, the temperatur...

Embodiment 3

[0070] A method for preparing a step-by-step expansion liquid expansion agent, the total mass of raw materials is 100 parts, the solid content is about 10%, and it is mainly prepared from the following components:

[0071] 700 ℃ nano magnesium oxide powder: 1.4 parts

[0072] 900℃ nano magnesium oxide powder: 0.8 part

[0073] 1100℃ nano magnesium oxide powder: 0.5 part

[0074] Butanol: 0.3 parts

[0075] Dimethicone: 0.2 parts

[0076] Span 80: 0.4 servings

[0077] Polypropylene alcohol 400: 0.7 parts

[0078] Dodecyl polyoxyethylene ether: 2.5 parts

[0079] Propylene Glycol Methyl Ether: 2.5 parts

[0080] Polyacrylamide: 1.0 parts

[0081] Step 1: Weigh 1.4 parts of 700 ℃ nanometer magnesium oxide powder, 0.8 part of 900 ℃ nanometer magnesium oxide powder, 0.5 part of 1100 ℃ nanometer magnesium oxide powder, 0.3 part of butanol, 0.2 part of dimethyl silicone oil, 0.4 part of Disk 80 and 90 parts of water were placed in the reaction kettle, the temperature of the ...

Embodiment 4

[0085] A method for preparing a step-by-step expansion liquid expansion agent, the total mass of raw materials is 100 parts, the solid content is about 10%, and it is mainly prepared from the following components:

[0086] 700 ℃ nano magnesium oxide powder: 1.3 parts

[0087] 900 ℃ nano magnesium oxide powder: 0.9 part

[0088] 1100℃ nano magnesium oxide powder: 0.8 part

[0089] Butanol: 0.3 parts

[0090] Dimethicone: 0.2 parts

[0091] Span 80: 0.4 servings

[0092] Polypropylene alcohol 400: 0.8 parts

[0093] Dodecyl polyoxyethylene ether: 2.4 parts

[0094] Propylene Glycol Methyl Ether: 2.4 parts

[0095] Polyacrylamide: 0.8 parts

[0096] Step 1: Weigh 1.3 parts of 700 ℃ nanometer magnesium oxide powder, 0.9 part of 900 ℃ nanometer magnesium oxide powder, 0.8 part of 1100 ℃ nanometer magnesium oxide powder, 0.3 part of butanol, 0.2 part of dimethyl silicone oil, 0.4 part of simethicone Disk 80 and 90 parts of water were placed in the reaction kettle, the temper...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a step-by-step expansion liquid expansion agent and a preparation method thereof. The liquid expansion agent is prepared by the following steps: Step 1: Weigh the mixture of nano-magnesium oxide powder, butanol, Span 80 and water at 30 Stir at a constant temperature of ~40°C for 1 hour; step 2: heat up to 50~70°C, add polyacryl alcohol 400, simethicone and shrinkage reducing components in sequence, and stir for 1~2 hours; step 3: add polyacrylamide, stir for 1 hour ~2h, aging at constant temperature for 1h, and cooling to room temperature to obtain a step-by-step expansion liquid expansion agent. The expansion component in the liquid expansion agent of the present invention is formed by modifying and mixing magnesium oxide powder fired at different temperatures of 700°C, 900°C and 1100°C. The magnesium oxide powder is mixed and ground to the nanometer level, and fired in three different The hydration time of magnesium oxide powder at different temperatures can achieve the effect of gradual expansion; compounding with shrinkage reducing components can significantly increase the volume expansion of concrete, reduce the volume shrinkage of concrete, and improve the crack resistance and impermeability of concrete.

Description

technical field [0001] The invention belongs to the technical field of building materials, and relates to an expansion agent, in particular to a liquid expansion agent with a high expansion rate and a preparation method thereof. Background technique [0002] During the pouring and hardening process of cement-based cementitious materials, volume shrinkage will be caused by chemical shrinkage, cold shrinkage and dry shrinkage, and even cracking of the material will occur in severe cases. Add fiber, pulverized fly ash or slag powder and expansion agent into concrete to solve the shrinkage and cracking problems of concrete. However, fiber-mixed concrete is cumbersome and costly, and the amount of finely ground fly ash and slag powder is large, which requires high cost and cannot completely solve the shrinkage and cracking of concrete. However, expansion agent is a kind of chemical additive. When mixed into concrete, when the concrete sets and hardens, it expands and blocks capi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B24/42
CPCC04B40/0046C04B2103/0068C04B14/304C04B24/00C04B24/42C04B24/08C04B24/26C04B24/32C04B24/023C04B24/2652
Inventor 柯凯姚恒
Owner HUBEI UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products