Adhesive for aldehyde-free plywood, and preparation method thereof, and plywood and preparation method thereof

An adhesive and plywood technology, which is applied in the field of prepared plywood and its preparation, can solve the problems of long opening time and slow viscosity growth rate, and achieve the effects of prolonging opening time, inhibiting viscosity growth and having remarkable catalytic effect.

Active Publication Date: 2020-03-10
WANHUA CHEM GRP CO LTD
View PDF14 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] There is a need for an adhesive system for formaldehyde-free plywood to solve the problem of formaldehyde release, and an adhesive system with a slow viscosity growth rate at room temperature, a long open time, and a moderate curing rate during hot pressing to prepare plywood

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Adhesive for aldehyde-free plywood, and preparation method thereof, and plywood and preparation method thereof
  • Adhesive for aldehyde-free plywood, and preparation method thereof, and plywood and preparation method thereof
  • Adhesive for aldehyde-free plywood, and preparation method thereof, and plywood and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Preparation of adhesives for formaldehyde-free plywood:

[0050] Step 1: Add 88 parts of deionized water and 12 parts of polyvinyl alcohol 1788 into the reaction kettle, stir at room temperature for 20 minutes, then raise the temperature to 90°C and keep it warm for 2 hours to completely dissolve the polyvinyl alcohol, then cool to room temperature stand-by;

[0051] Step 2: Dissolve 0.6 parts of copper phosphate in 12 parts of phosphoric acid.

[0052] The third step: the phosphoric acid solution of copper phosphate obtained in the second step and 0.5 parts of xanthan gum, 0.5 parts of methyl cellulose, 0.1 part of defoamer, 15 parts of flour and 30 parts of PMDI are added to the polyethylene obtained in the first step In the alcohol solution, continue to stir at room temperature until the mixture is uniform, and then the formaldehyde-free adhesive for plywood is obtained.

[0053] By testing the viscosity growth of the system, the opening time of the system can be m...

Embodiment 2

[0063] Example 2 Adjust polyvinyl alcohol to 7 parts of PVA2488, water to 93 parts, thickener to 0.4 parts of methylcellulose + 0.3 parts of xanthan gum, defoamer to 0.01 parts, phosphoric acid to 15 parts , the copper phosphate is adjusted to 0.8 parts, the flour is adjusted to 20 parts, the PMDI is adjusted to 35 parts, the hot pressing factor is adjusted to 1.5min / mm, and others are the same as in Example 1;

Embodiment 3

[0064]Example 3 The thickener is adjusted to 0.3 parts of methyl cellulose + 0.2 parts of xanthan gum, the defoamer is adjusted to 0.06 parts, phosphoric acid is adjusted to 10 parts, copper phosphate is adjusted to 0.5 parts, flour is adjusted to 30 parts, PMDI Adjusted to 25 parts, sizing amount adjusted to 200g / m 2 , other with embodiment 1;

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
freezing pointaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
alcoholysis degreeaaaaaaaaaa
Login to View More

Abstract

The invention discloses an adhesive for aldehyde-free plywood, and a preparation method thereof, a plywood prepared from the adhesive, and a preparation method thereof, wherein the adhesive is prepared from the following raw materials in parts by weight: 7-12 parts of polyvinyl alcohol, 0.5-1 part of a thickening agent, 0.01-0.1 part of a defoaming agent, 10-15 parts of phosphoric acid, 0.5-1 partof a copper salt, 15-30 parts of flour, 88-93 parts of deionized water and 25-35 parts of polyfunctional isocyanate. According to the invention, no formaldehyde is generated in adhesive production and plywood preparation, and the formaldehyde release amount of the obtained plywood is equivalent to the formaldehyde release amount of the raw material veneer, and the formaldehyde-free purpose is achieved; and by introducing phosphoric acid and a copper salt into the adhesive system, the viscosity increasing rate of the system at a normal temperature is slow, the opening time is long, the adhesive curing rate during hot pressing is moderate, and the production efficiency of the plate is high.

Description

technical field [0001] The invention relates to a formaldehyde-free adhesive system, in particular to an adhesive system used for preparing plywood, a plywood used for preparing the same and a preparation method thereof. Background technique [0002] Plywood is an important part of the wood-based panel industry. In 2016, China produced 177.56 million cubic meters of plywood, an increase of nearly 7.3% over the previous year, accounting for 59.1% of all wood-based panel production, with an output value of about 367.5 billion yuan. In the past 10 years, the average annual growth rate of plywood production in China has reached 20.6%, which is the fastest growing type of wood-based panels. In 2016, the General Administration of Quality Supervision, Inspection and Quarantine of the People's Republic of China organized the quality supervision and inspection of plywood products, and inspected three items including moisture content, bonding strength, and formaldehyde emission of ply...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J175/04C09J11/04C08G18/62C08G18/64C08G18/79C08G18/76B27D1/08
CPCC09J175/04C09J11/04C08G18/6484C08G18/6212C08G18/4081C08G18/7671C08G18/7614C08G18/794B27D1/08C08K2003/328C08K3/32
Inventor 孙卫华涂松李厚义王向硕张梓军孙鹏
Owner WANHUA CHEM GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com