Anti-slip wear-resistant modification method for lightweight rubber shoes

A technology of modification and rubber shoes, applied in the direction of wear-resistant fibers, footwear, applications, etc., can solve the problems of poor anti-skid and wear resistance, poor moisture absorption and air permeability, etc.

Inactive Publication Date: 2020-02-14
ANHUI GUANHONG PLASTIC IND
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of the commercially available lightweight rubber shoes have the defects of poor anti-skid wear resistance, poor moisture absorption and air permeability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A method for modifying anti-skid and wear resistance of lightweight rubber shoes, characterized in that it comprises the following steps, and the following raw materials are calculated in parts by weight:

[0027] (1) Surface pretreatment of aramid staple fibers: first impregnate 5 parts of aramid staple fibers with acetone, ultrasonically wash them at 40°C for 2 hours, then put them into a 10% sodium hydroxide solution and stir for 30 minutes, then Wash with deionized water until neutral, and dry in a blast drying oven at 60°C;

[0028] Put the citric acid-sodium citrate buffer solution with a pH of 5 into a water bath at 50°C for heating, pour 0.03 parts of xylanase into it and stir for 10 minutes, then add the aramid staple fiber obtained above for 5 hours, wash with water until neutral, Put it into a drying oven at 70°C for drying to obtain surface-pretreated aramid staple fibers;

[0029] Coating treatment of aramid staple fiber: Mix 5 parts of epoxy resin E51 and...

Embodiment 2

[0036] A method for modifying anti-skid and wear resistance of lightweight rubber shoes, characterized in that it comprises the following steps, and the following raw materials are calculated in parts by weight:

[0037] (1) Surface pretreatment of aramid staple fibers: First, impregnate 10 parts of aramid staple fibers with acetone, ultrasonically wash them at 50°C for 1 hour, then put them into a 10% sodium hydroxide solution and stir for 30 minutes, then Wash with deionized water until neutral, and dry in a blast drying oven at 80°C;

[0038] Heat the citric acid-sodium citrate buffer solution with a pH of 5 in a water bath at 55°C, pour 0.04 parts of xylanase into it and stir for 8 minutes, then add the aramid staple fiber obtained above for 5 hours, and then wash with water until neutral. Put it into a drying oven at 75°C for drying to obtain surface-pretreated aramid staple fibers;

[0039] Coating treatment of aramid staple fiber: mix 10 parts of epoxy resin E51 and 0....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses an anti-slip wear-resistant modification method for lightweight rubber shoes. The anti-slip wear-resistant modification method includes the steps that epoxy resin E51 and imidazole are mixed, acetone is added, stirring and dissolving are conducted, then surface-pretreated aramid short fibers are added, after infiltration, an acetone solution and part of cured epoxy resin are dried in an oven, and coated aramid short fibers are obtained; ethylene glycol and sodium tripolyphosphate are added into deionized water, even stirring is conducted, then pretreated modified coal ash and modified nano-calcium carbonate are added, and through high-speed dispersion wed modification, modified anti-slip aggregates are obtained; and nylon 6 is dried in an air dry oven, put into a rheometer to be molten, fully pretreated and plasticized, a rubber compound, the coated aramid short fibers and the modified anti-slip aggregates are added to be evenly mixed, during addition and discharging, nitrogen is introduced for protection, and then the lightweight rubber shoes are manufactured according to a conventional production method.

Description

technical field [0001] The invention belongs to the field of processing light rubber shoes, and in particular relates to a non-slip and wear-resistant modification method for lightweight rubber shoes. Background technique [0002] Plastic shoes, also known as all-plastic shoes, are shoes made of synthetic resin as the main raw material. Plastic shoes are divided into plastic sandals and plastic slippers according to their usage. Rubber shoes are a kind of shoes, with rubber as the sole or upper, water shoes generally also use rubber shoes, the earliest rubber shoes in my country are the famous "Jiefang brand rubber-soled shoes" or "Jiefang shoes", which are characterized by cheap price and simple production , comfortable and durable to wear, it is actually a good product in shoes. However, most of the commercially available lightweight rubber shoes have the defects of poor anti-skid wear resistance and poor moisture absorption and air permeability. [0003] In the present ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L77/02C08L7/00C08L77/10C08K13/06C08K9/04C08K9/02C08K7/26C08K3/26C08K3/22C08K5/09D06M11/38D06M15/55D06M13/352A43B1/10D06M101/36
CPCA43B1/10C08K2003/2296C08K2003/265C08L7/00C08L77/02C08L2205/16D06M11/38D06M13/352D06M15/55D06M2101/36D06M2200/35C08L77/10C08K13/06C08K9/04C08K9/02C08K7/26C08K3/26C08K3/22C08K5/09
Inventor 申乾成申辉黄振
Owner ANHUI GUANHONG PLASTIC IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap