A kind of electrospinning rotary spinneret and using method thereof

An electrospinning and spinning device technology, applied in the field of electrospinning rotary spinning device, can solve the problems of high brittleness of nanofibers, limited application performance and scope, etc., achieve uniform force on inner wall, improve material utilization, increase The effect of high pressure

Active Publication Date: 2021-09-28
NANTONG UNIVERSITY
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the nanofibers prepared by electrospinning technology are relatively brittle, which limits their application performance and scope.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of electrospinning rotary spinneret and using method thereof
  • A kind of electrospinning rotary spinneret and using method thereof
  • A kind of electrospinning rotary spinneret and using method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0033] In this embodiment, the electrospinning rotary spinning device, such as figure 1 As shown, it includes a micro injection pump 7 , a syringe 6 , a bearing sleeve 5 , a bearing 4 , a needle 2 , a receiving plate 1 and a high voltage power supply 11 .

[0034] Injection tube 6 is arranged on microinjection pump 7 by clamp, as Figure 4 As shown, the bearing sleeve 5 has a stepped inner cavity, which includes a bearing connection cavity 51, a transition cavity 52 and an injection tube connection cavity 53 arranged in sequence. The inner diameter of the bearing connection cavity 51 is larger than the injection tube connection cavity. The inner diameter of the cavity 53, the transition cavity 52 is an inner cavity formed by the smooth transition from the bearing connection cavity 51 to the injection tube connection cavity 53, and the smooth transition protrudes outward, and the bearing sleeve 5 is used to connect the bearing 4 and the injection tube 6 , the inside of which i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an electrospinning rotary spinning device and a method of using the same, comprising a micro-injection pump, an injection tube, a bearing sleeve, a bearing, a needle, a receiving plate and a high-voltage power supply. The advantages of the present invention lie in: the electrospinning rotary spinneret device and its using method of the present invention, the tail of the needle head is connected with a bearing, the bearing rotational frictional resistance is small, and the bearing is easy to be replaced after wear; the needle tube in the device is divided into equal volumes. Several layers, each layer of spinning solution is under the same pressure to ensure the uniformity of spinning; the speed of the needle is controlled by the motor, and the speed can be adjusted according to the characteristics of different polymers, so as to change the degree of spinning of the fibers and improve the product quality. quality.

Description

technical field [0001] The invention belongs to the technical field of electrospinning, in particular to an electrospinning rotary spinneret and a using method thereof. Background technique [0002] Electrospinning has become one of the main ways to prepare nanofiber materials due to its simple manufacturing equipment, low spinning cost, variety of spinnable materials and controllable process. Electrospinning technology can directly and continuously prepare polymer nanofibers. It has the advantages of low equipment and experimental costs, convenient, simple and flexible operation, and high fiber yield. The fiber membrane prepared by electrospinning technology has high porosity, Network structure with large specific surface area. [0003] The potential application value of nanofibers provides a new development space for the development of its preparation technology, and also puts forward new requirements. However, nanofibers prepared by electrospinning technology are relati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D01D5/00
CPCD01D5/0061D01D5/0069D01D5/0076
Inventor 倪红军沈威钢朱昱吕帅帅汪兴兴黄明宇李志扬
Owner NANTONG UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap