A method for smelting ultra-low manganese steel by using high manganese hot metal

A technology of ultra-low manganese steel and molten iron, applied in the field of iron and steel metallurgy

Active Publication Date: 2021-06-22
BAOTOU IRON & STEEL GRP
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In order to overcome the deficiency that the existing smelting process cannot use high-manganese molten iron with a manganese content higher than 0.40% to smelt ultra-low manganese steel, the present invention provides a method for smelting ultra-low manganese steel by using high-manganese molten iron, which is an original development LF furnace deep demanganization process, which can use high manganese molten iron as raw material to smelt molten steel with manganese content less than 0.02%.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for smelting ultra-low manganese steel by using high manganese hot metal
  • A method for smelting ultra-low manganese steel by using high manganese hot metal

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038]Using molten iron with a manganese content of 0.423% as the raw material, the double slag smelting process of the converter is used for smelting and demanganization. The low-temperature tapping of the converter link creates better thermodynamic conditions for further demanganization. The in-place temperature of the LF furnace is 1529°C. The Mn content in bit molten steel is 0.055%. During the LF smelting and refining process, 4269kg of lime and 329kg of modified formulations were added, and the cumulative heating was 31 minutes. The manganese content was 0.0165% when it was off-site. The specific parameters are shown in Table 1 below.

Embodiment 2

[0040] Using molten iron with a manganese content of 0.416% as the raw material, it is smelted using the double slag smelting process of the converter, and the steel is tapped at a low temperature in the converter link to create better thermodynamic conditions for further demanganization. The Mn content in molten steel is 0.049%. During the LF smelting and refining process, add 4442kg of lime, 346kg of reforming agent, heat for 33 minutes, and the manganese content is 0.0146% when off-site. The specific parameters are shown in Table 1 below.

Embodiment 3

[0042] Using molten iron with a manganese content of 0.457% as the raw material, the double slag smelting process of the converter is used for smelting, and the steel is tapped at a low temperature in the converter link to create better thermodynamic conditions for further demanganization. The Mn content in molten steel is 0.053%. During the LF smelting and refining process, add 3878kg of lime, 286kg of reforming agent, heat for 26 minutes, and the manganese content is 0.0136% when it is off-site. The specific parameters are shown in Table 1 below.

[0043] In the above three embodiments, the content of manganese in the molten iron exceeds 0.40%, and the content of manganese cannot be reduced to below 0.05% after demanganization in the converter. After further demanganization by the LF furnace, the manganese content of the molten steel further decreases, and finally reaches the smelting standard, which is lower than 0.02%. The specific process parameters and process effects ar...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for smelting ultra-low manganese steel by utilizing high manganese molten iron, which belongs to the field of iron and steel metallurgy. The method for smelting ultra-low manganese steel with high manganese molten iron provided by the present invention adopts double slag smelting process to remove manganese and other elements in most of the molten iron in the converter process, and adopts the process of low temperature tapping of converter and deep demanganization of LF refining furnace Further demanganization can stably control the manganese content in the molten steel below 0.02% under the condition that the molten iron fed into the furnace is a high-manganese molten iron with a manganese content higher than 0.40%, meeting the smelting needs of ultra-low manganese steel.

Description

technical field [0001] The invention belongs to the field of iron and steel metallurgy, and in particular relates to a method for smelting ultra-low manganese steel by utilizing high-manganese molten iron, in particular to a method for smelting ultra-low-manganese steel by utilizing high-manganese molten iron with a content greater than 0.40%. Background technique [0002] In order to meet the needs of today's market, high value-added special steel grades have very low requirements for Mn in molten steel, while the converter itself has limited demanganization capacity, and most steel mills have limited manganese content in molten iron due to the limitation of ore raw materials. At about 0.40%, when this molten iron is used to smelt ultra-low manganese steel (Mn≤0.02%), the minimum manganese content at the end of the converter is about 0.06%, which cannot meet the requirements of this type of steel. Under the above background, the technical problem of using high manganese hot...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C21C5/36C21C5/30C21C7/076C21C7/072
CPCC21C5/30C21C5/36C21C7/072C21C7/076Y02P10/20
Inventor 徐少华李志成徐涛赵鸣王俊刚韩浩田王进财
Owner BAOTOU IRON & STEEL GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com