Direct-coating water-based single-component ceramic tile renovating coating and preparation method thereof

A one-component, direct-coating technology, applied in the field of architectural coatings, it can solve the problems of poor adhesion, sagging, difficult adhesion of tiles, etc., and achieve the effects of improved dry and wet adhesion, simple application and low VOC content.

Inactive Publication Date: 2019-10-11
CARPOLY CHEM GRP
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of the problems in the prior art, the purpose of the present invention is to provide a direct-coating type water-based one-component ceramic tile renovation coating, which has excellent dry and wet adhesion and weather resistance, and can not only solve the problems of difficult adhesion and sag on the surface of ceramic tiles. problem, and it can also solve the problem of poor adhesion after soaking in rainwater

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Direct-coating water-based single-component ceramic tile renovating coating and preparation method thereof
  • Direct-coating water-based single-component ceramic tile renovating coating and preparation method thereof
  • Direct-coating water-based single-component ceramic tile renovating coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A kind of direct-coating type water-based one-component ceramic tile refurbishment coating comprises the following components by weight:

[0035]

[0036] (1) Add the dispersant to water, and disperse until uniform at a speed of 750 rpm;

[0037] (2) Add wetting agent, film-forming aid, antifreeze, defoamer, cellulose thickener and pH regulator in sequence, and disperse until uniform at a speed of 750 rpm;

[0038] (3) Add fillers and pigments, increase the speed to 1500 rpm, and disperse until uniform;

[0039] (4) Reduce the speed to 900 rpm, add antifungal agent, preservative, film former I, film former II, adhesion promoter and hydrophobic modified alkali-swellable thickener in sequence, and disperse until uniform, that is A direct-to-apply water-based one-component tile renovation paint.

Embodiment 2

[0041] A kind of direct-coating type water-based one-component ceramic tile refurbishment coating comprises the following components by weight:

[0042]

[0043]

[0044] (1) Add the dispersant to water, and disperse until uniform at a speed of 750 rpm;

[0045] (2) Add wetting agent, film-forming aid, antifreeze, defoamer, cellulose thickener and pH regulator in sequence, and disperse until uniform at a speed of 750 rpm;

[0046] (3) Add filler, increase the rotating speed to 1500 rpm, and disperse until uniform;

[0047] (4) Reduce the speed to 900 rpm, add antifungal agent, preservative, film former I, film former II, adhesion promoter and hydrophobic modified alkali-swellable thickener in sequence, and disperse until uniform, that is A direct-to-apply water-based one-component tile renovation paint.

Embodiment 3

[0049] A kind of direct-coating type water-based one-component ceramic tile refurbishment coating comprises the following components by weight:

[0050]

[0051]

[0052] The preparation method of the above-mentioned direct coating type water-based one-component ceramic tile renovation coating may further comprise the steps:

[0053] (1) Add the dispersant to water, and disperse until uniform at a speed of 750 rpm;

[0054] (2) Add wetting agent, film-forming aid, antifreeze, defoamer, cellulose thickener and pH regulator in sequence, and disperse until uniform at a speed of 750 rpm;

[0055] (3) Add filler, increase the rotating speed to 1500 rpm, and disperse until uniform;

[0056] (4) Reduce the speed to 900 rpm, add antifungal agent, preservative, film former I, film former II, adhesion promoter and hydrophobic modified alkali-swellable thickener in sequence, and disperse until uniform, that is A direct-to-apply water-based one-component tile renovation paint.

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of architectural coatings, and particularly relates to a direct-coating water-based single-component ceramic tile renovating coating and a preparation method thereof. The direct-coating water-based single-component ceramic tile renovating coating comprises the following components in parts by weight: 10-25 parts of a film forming material I, 25-35 partsof a film forming material II, 0-1 part of an adhesion promoter, 0-1 part of a wetting agent, 0-1 part of a dispersing agent, 0-1 part of a defoaming agent, 0-8 parts of a film forming assistant, 0-4parts of a thickening agent, 0-3 parts of an antifreezing agent, 0-1 part of a pH regulator, 0-1 part of a preservative, 0-1 part of a mildew inhibitor, 5-25 parts of a filler, 0-25 parts of a pigment and 20-25 parts of water. The direct-coating type water-based single-component ceramic tile renovating coating is a water-based system, has low VOC content and is environment-friendly; the direct-coating water-based single-component ceramic tile renovating coating has excellent performances of dry and wet adhesion, weather resistance and the like; and application is simple, the construction period can be shortened, and the construction cost can be reduced.

Description

technical field [0001] The invention belongs to the technical field of architectural coatings, in particular to a direct-coating type water-based one-component ceramic tile renovation coating and a preparation method thereof. Background technique [0002] Exterior wall tiles, mosaic tiles, etc. are commonly used decorative materials for building exterior walls. During use, with the passage of time, due to the influence of various external environmental conditions, these decorative materials are prone to problems such as loosening, falling off, getting old, and partially fading, which seriously affect their decorative effects. There are two main strategies for the renovation of exterior wall tiles, mosaic tiles, etc.: one is to not change the decorative style of the tile surface, such as first rolling the special renovation interface agent, and then rolling the topcoat or directly rolling two-component surface The other is to completely change the original decorative style, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/04C09D151/00C09D125/14C09D5/16C09D7/20C09D7/65
CPCC08K2003/2241C08L2201/08C08L2205/035C09D5/1662C09D5/1668C09D5/1687C09D7/20C09D125/14C09D133/04C09D151/00C08L25/14C08L83/04C08L1/284C08K5/103C08K5/053C08K3/22C08K13/02C08L33/04C08L51/00
Inventor 董海晖赵鹏昆张浩陈玉泉谭振华
Owner CARPOLY CHEM GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com