A kind of high-efficiency laser marking material and preparation method thereof

A laser marking and high-efficiency technology, applied in the field of materials, can solve the problems of low marking speed, blurred marking, and inability to meet the needs of industrial production, and achieve the effect of improving the printing effect.

Active Publication Date: 2021-06-01
JIANGSU ZHONGTIAN TECH CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the process of laser printing, the existing black PE materials are prone to defects such as blurred marks, poor contrast, and slow marking speed when laser printing is used.
Especially in the printing of small-sized cables with small outer diameter and thin wall thickness, defects such as small marks, blurring, poor contrast, and low marking speed are prone to occur, which cannot meet the needs of industrial production.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-efficiency laser marking material and preparation method thereof
  • A kind of high-efficiency laser marking material and preparation method thereof
  • A kind of high-efficiency laser marking material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0038] The present invention also provides a method for preparing the above-mentioned high-efficiency laser marking material, comprising the following steps:

[0039] A) After mixing HDPE resin and LLDPE resin, add laser auxiliary agent, lubricant, antioxidant, light stabilizer and black masterbatch and mix to obtain a mixture;

[0040] B) extruding and granulating the mixed material to obtain a high-efficiency laser marking material.

[0041] In the present invention, the HDPE resin and the LLDPE resin are first mixed, and the present invention has no special limitation on the mixing method, and the mixing method known to those skilled in the art will suffice. In the present invention, preferably mix according to the following method:

[0042] Put the HDPE resin and LLDPE resin into the batch mixing equipment to reciprocate and mix up and down to obtain the batch mixed resin;

[0043] The batch-mixed resin is placed in a discharge bin, and then automatically weighed, and th...

Embodiment 1～4

[0058] 1. See Table 1 and Table 2 for formula type and dosage respectively

[0059] Table 1 type of formula

[0060]

[0061]

[0062] Note: HDPE resins in Table 1 include low-melt HDPE resins whose melt flow rate is not more than 1.0g / 10min, one or more blended materials selected from 7000F, FB1350, HDPE3363, HDPE00952 and HDPE041; high-melt index The melt flow rate of HDPE resin is not more than 10.0g / 10min, and it is selected from one or more blending materials of HDPE (FMA026), HDPE8008, HDPE (FMA025). The melt flow rate of LLDPE resin is not more than 1.0g / 10min, and it is selected from one or more blended materials of LLDPE7042, LLDPE (FB2230), LLDPE (FK1820). The laser engraving auxiliary agent in the laser auxiliary agent is Heqirun HZ-889A.

[0063] Table 2 formula dosage (unit: kg)

[0064] Example 1 Example 2 Example 3 Example 4 HDPE 60 40 80 75 LLDPE 40 60 20 25 Laser Auxiliary 0.1 0.4 0.5 0.8 lubricant 0....

Embodiment 5

[0088] Based on the formula and preparation method of Example 4, change the amount of raw materials or laser additives, and keep other conditions unchanged, prepare high-efficiency laser marking materials. The specific dosage of the formula is shown in Table 7

[0089] Table 7 formula dosage

[0090]

[0091] Note: In the example 4, 4-1, 4-2, 4-3 in Table 7, the laser auxiliary agent is selected from the mixture of Iriotec8835 and Iriotec8815 ​​with a mass ratio of 4:1; Example 4-4 does not add laser auxiliary agent ; Embodiment 4-5 selects the laser auxiliary agent as Heqi Run radium carving auxiliary agent HZ-889A;

[0092] The performance of the above-mentioned high-efficiency laser marking materials was tested, and the results are shown in Table 8

[0093] Table 8 Cabling performance of high-efficiency laser marking materials

[0094]

[0095] It can be seen from Table 8 that the mechanical properties of the product basically do not change much with the change of t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to view more

Abstract

The invention provides a high-efficiency laser marking material. In the formula system of the high-efficiency laser marking material provided by the invention, the addition amount of laser auxiliary agent and black color masterbatch plays a leading role in the printing effect. With the increase of additive content and the decrease of carbon black content, the mechanical properties of the material will not change much, but the printing effect will be significantly improved. In addition, the laser additive can help improve the black PE material to absorb the special wavelength emitted by the laser, so that the surface layer of the polymer is carbonized, and through foaming, it appears white, which is in sharp contrast with the black PE sheath.

Description

technical field [0001] The invention belongs to the technical field of materials, and in particular relates to a high-efficiency laser marking material and a preparation method thereof. Background technique [0002] In the cable industry, black PE material has been widely used. Black PE materials are generally marked by traditional ink spraying, printing wheel printing, etc., but there are certain limitations and it is difficult to meet production requirements. [0003] Compared with traditional printing methods, laser printing technology is energy-saving and environmentally friendly, with high applicability and clear marks. However, in the process of laser printing, the existing black PE materials are prone to defects such as blurred marks, poor contrast, and slow marking speed when laser printing is used. Especially in the printing of small-sized cables with small outer diameter and thin wall thickness, defects such as small marks, blurring, poor contrast, and low markin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/06C08L23/08C08L83/04C08K13/02C08K3/22C08K3/34C08K3/32C08K3/04B41M5/00B29C48/92
CPCC08L23/06C08L23/0815B41M5/0064B29C48/92C08L2205/025C08L2205/035C08L2207/062C08L2310/00C08K2003/2275C08K2003/328B29C2948/92704B29C2948/9259C08L83/04C08K13/02C08K3/22C08K3/34C08K3/32C08K3/04B29C48/0022B29C48/345B29C48/05B29C48/04B29C48/40B29C48/875B41M5/267B29B7/88B29B7/007B29B7/48B29B7/823B29B9/12B29B9/06B29K2023/065B29K2023/0625
Inventor 缪飞朱炯管成飞赵学广赵静
Owner JIANGSU ZHONGTIAN TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap