A kind of preparation method of black photonic glaze

A photonic and black technology, applied in the field of preparation of black photonic glaze, can solve the problems of complex preparation process, poor mechanical properties and high cost, and achieve the effects of simple process method, low cost and high saturation

Active Publication Date: 2020-11-24
JINGDEZHEN CERAMIC UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, in radiative cooling materials, photonic crystal layers are usually used to selectively transmit infrared radiation with a wavelength range of 8-13 μm, thereby achieving the effect of radiative cooling. However, the cost of this composite photonic crystal film is relatively high, and the preparation process is relatively complicated. , the mechanical properties are also poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of black photonic glaze
  • A kind of preparation method of black photonic glaze
  • A kind of preparation method of black photonic glaze

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A kind of preparation method of black photonic glaze, concrete steps are:

[0023] (1) According to the mass percentage of material composition: kaolin 7.0%, quartz 19.5%, SrCO 3 2.5%, TiO 2 12.5%, limestone 7.0%, BaCO 3 12.0%, albite 23.0%, ZnO 8.5%, Pb 3 o 4 3.5%, spodumene 4.5%;

[0024] (2) Put the raw materials in step (1) into a ball mill for 1 hour;

[0025] (3) Sieve the glaze slurry milled in step (2) to obtain a glaze slurry with a particle size of <45 μm, and the aging time is 24 hours;

[0026] (4) Applying the processed raw materials in step (3) to the surface of the green body;

[0027] (5) Dry the sample after glazing in step (4) at 60°C for 10 hours;

[0028] (6) Put the sample dried in step (5) into a high-temperature electric furnace for sintering, and then cool naturally with the furnace to obtain a bright black photonic glaze; the maximum temperature of the sintering process is 1100 ° C, the holding time is 90 minutes, and the ℃, the holdi...

Embodiment 2

[0030] A kind of preparation method of black photonic glaze, concrete steps are:

[0031] (1) According to the mass percentage of material composition: kaolin 8.5%, quartz 18.0%, SrCO 3 3.5%, TiO 2 11.0%, limestone 9.0%, BaCO 3 10.5%, albite 21.0%, ZnO 10.0%, Pb 3 o 4 4.5%, spodumene 4.0%;

[0032] (2) Put the raw materials in step (1) into a ball mill for 1 hour;

[0033] (3) Sieve the glaze slurry milled in step (2) to obtain a glaze slurry with a particle size of <45 μm, and the aging time is 24 hours;

[0034] (4) Applying the processed raw materials in step (3) to the surface of the green body;

[0035] (5) Dry the sample after glazing in step (4) at 60°C for 10 hours;

[0036] (6) Put the sample dried in step (5) into a high-temperature electric furnace for sintering, and then cool naturally with the furnace to obtain a bright black photonic glaze; ℃, the holding time is 30 minutes.

Embodiment 3

[0038] A kind of preparation method of black photonic glaze, concrete steps are:

[0039] (1) According to the mass percentage of material composition: kaolin 10.0%, quartz 16.5%, SrCO 3 4.0%, TiO 2 9.5%, limestone 11.5%, BaCO 3 8.5%, albite 19.5%, ZnO 11.5%, Pb 3 o 4 5.5%, spodumene 3.5%;

[0040] (2) Put the raw materials in step (1) into a ball mill for 1 hour;

[0041] (3) Sieve the glaze slurry milled in step (2) to obtain a glaze slurry with a particle size of <45 μm, and the aging time is 24 hours;

[0042] (4) Applying the processed raw materials in step (3) to the surface of the green body;

[0043] (5) Dry the sample after glazing in step (4) at 60°C for 10 hours;

[0044] (6) Put the sample dried in step (5) into a high-temperature electric furnace for sintering, and then cool naturally with the furnace to obtain a bright black photonic glaze; ℃, the holding time is 30 minutes.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of black photon glaze. The preparation method includes the steps that kaolin, quartz, SrCO3, TiO2, limestone, BaCO3, sodaclase, ZnO, Pb3O4 and spodumene powder are adopted as raw materials, burdening, ball-milling, screening, decaying, drying, glazing, sintering and cooling are carried out, and then the product is obtained. The black photon glaze prepared with the method with a solid-phase sintering method can absorb or consume incident light of almost all wavebands, thus, energy emitted to a blank structure is reduced, and the temperature of a blank is remarkably reduced. The method is simple in process, addition of heavy metal elements in tinting pigments is reduced, resource saving and environmental protection are benefited, the cost is low,large-scale production is easy, and therefore the preparation method has broad market prospects.

Description

technical field [0001] The invention belongs to photonic crystal-like structural color ceramic glazes, in particular to a method for preparing black photonic glazes. Background technique [0002] Photonic crystals refer to materials with photonic bandgap characteristics, which are periodically arranged on the optical scale. According to Bragg diffraction, a photonic bandgap of a certain size can be generated, and incident light with a corresponding wavelength size will be reflected and cannot continue to propagate. Macroscopic Expressed as a saturated bright structured color. Another feature of photonic crystal materials is selective transmission, which can selectively transmit incident light of a specific wavelength. For example, in radiative cooling materials, photonic crystal layers are usually used to selectively transmit infrared radiation with a wavelength range of 8-13 μm, thereby achieving the effect of radiative cooling. However, the cost of this composite photonic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C10/00C03C4/02C03C8/00C04B41/86
CPCC03C4/02C03C8/00C03C10/00C04B41/5023C04B41/86C04B41/4539C04B41/0072
Inventor 展红全吴传琦罗志云
Owner JINGDEZHEN CERAMIC UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com