Wood fireproof glue and manufacturing process of fireproof plate

A technology of fireproof glue and fireproof board, which is applied in the direction of manufacturing tools, wood processing appliances, and the joining of wooden veneers to achieve the effect of small heat generation, no residue, and increased coverage.

Active Publication Date: 2019-06-04
东莞市宏晟木业有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is to provide a kind of wood fireproof adhesive and pure solid wood glue that is not easy to fall off when bonded to wood, has good high temperature resistance, good wettability, good uniformity and high safety, based on the above-mentioned deficiencies in the prior art. Production, simple structure, fire-resistant and heat-insulating, adaptable to load, high strength, three-dimensional effect and fashion sense of fireproof board and the manufacturing process of fireproof board

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wood fireproof glue and manufacturing process of fireproof plate
  • Wood fireproof glue and manufacturing process of fireproof plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039]The invention provides a wood fireproof glue, which is made of magnesium chloride, polyvinyl alcohol, magnesium sulfate and water in a reaction kettle after being stirred and heated up so that the magnesium chloride and magnesium sulfate destroy the hydrogen bond of polyvinyl alcohol and react to form an intermediate material. The intermediate material It is formed due to the strong electronic interaction between the magnesium ions after magnesium chloride and magnesium sulfate are dissolved in water and the oxygen atoms in the hydroxyl groups on the polyvinyl alcohol molecular chain. The intermediate material is mixed with additives under the action of stirring to obtain the Described wood fireproof glue, wherein, the weight component of the raw material that prepares described intermediate material is magnesium chloride 35 parts, polyvinyl alcohol 8 parts, magnesium sulfate 3.5 parts, water 95 parts; Described auxiliary agent comprises the magnesium oxide 10 parts of wei...

Embodiment 2

[0049] The invention provides a wood fireproof glue, which is made of magnesium chloride, polyvinyl alcohol, magnesium sulfate and water in a reaction kettle after being stirred and heated up so that the magnesium chloride and magnesium sulfate destroy the hydrogen bond of polyvinyl alcohol and react to form an intermediate material. The intermediate material It is formed due to the strong electronic interaction between the magnesium ions after magnesium chloride and magnesium sulfate are dissolved in water and the oxygen atoms in the hydroxyl groups on the polyvinyl alcohol molecular chain. The intermediate material is mixed with additives under the action of stirring to obtain the Said wood fireproof glue, wherein, the weight component of the raw material that prepares described intermediate material is magnesium chloride 47 parts, polyvinyl alcohol 11 parts, magnesium sulfate 7 parts, water 110 parts; Described auxiliary agent comprises the magnesium oxide 15 parts of weight ...

Embodiment 3

[0059] The invention provides a wood fireproof glue, which is made of magnesium chloride, polyvinyl alcohol, magnesium sulfate and water in a reaction kettle after being stirred and heated up so that the magnesium chloride and magnesium sulfate destroy the hydrogen bond of polyvinyl alcohol and react to form an intermediate material. The intermediate material It is formed due to the strong electronic interaction between the magnesium ions after magnesium chloride and magnesium sulfate are dissolved in water and the oxygen atoms in the hydroxyl groups on the polyvinyl alcohol molecular chain. The intermediate material is mixed with additives under the action of stirring to obtain the The wood fireproof glue, wherein, the weight component of the raw material for preparing the intermediate material is 38 parts of magnesium chloride, 8.5 parts of polyvinyl alcohol, 4.0 parts of magnesium sulfate, and 98 parts of water; the auxiliary agent includes 12 parts of magnesium oxide by weig...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
peel strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses wood fireproof glue, which is prepared by the following steps: stirring and heating magnesium chloride, polyvinyl alcohol, magnesium sulfate and water in a reaction vessel, reacting to generate a fireproof glue intermediate material, adding an auxiliary agent into the intermediate material while stirring to prepare the wood fireproof glue. The invention also discloses a fireproof plate prepared from the wood fireproof glue and a manufacturing process thereof. The fireproof plate comprises a fireproof plate sandwich layer composed of multiple solid wood blocks which aresuccessively distributed from left to right. Upper and lower sides of the fireproof plate sandwich layer are respectively provided with a fireproof wood chip layer which is formed by crisscrossed lamination of multiple wood chips according to the wood grain. Between the fireproof wood chip layer and the fireproof plate sandwich layer, between two adjacent solid wood blocks and between two adjacentwood chips is coated with the wood fireproof glue. The fireproof plate is prepared by steps of wood turning, final trimming, coating with the wood fireproof glue, cold pressing, drying, sanding and hot pressing.

Description

technical field [0001] The invention relates to the technical field of wood products, in particular to a wood fireproof glue and a manufacturing process of a fireproof board. Background technique [0002] Fireproof board, also known as fireproof board, is a refractory building material for surface decoration. It has rich surface colors, textures and special physical properties. It is widely used in interior decoration, furniture, kitchen cabinets, laboratory countertops, exterior walls and other fields. [0003] Existing fireproof boards usually include a core layer and a fireproof layer. The fireproof layer wraps the core layer to make a fireproof board. In the prior art, the fireproof layer is a mineral wool board, glass wool board, cement board, perlite board, and fireproof gypsum board. , metal plates and other fire-resistant wood chips made of chemical materials, etc. The above-mentioned fire-resistant boards have the advantages of fire-resistant and heat-insulating, ad...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J129/04C09J11/04C09J11/06C09J11/08B27D1/04B27D1/08
Inventor 张良胡志刚
Owner 东莞市宏晟木业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com