A kind of modified asphalt and preparation method thereof

A technology of modified asphalt and asphalt slurry, which can be used in building components, building insulation materials, buildings, etc., and can solve problems such as poor stability of modified asphalt.

Active Publication Date: 2021-05-14
潮州市金鑫沥青混凝土有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the deficiencies of the prior art, the present invention provides a modified asphalt and its preparation method, which solves the problem of poor stability of the existing modified asphalt while realizing the modification

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of modified asphalt and preparation method thereof
  • A kind of modified asphalt and preparation method thereof
  • A kind of modified asphalt and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] In the present embodiment, the preparation method of modified asphalt is as follows:

[0030] 1) In parts by weight, weigh 100 parts of petroleum-based asphalt, 15 parts of polycarbosilane powder (softening point 90°C, mesh number 4), and 8 parts of KH792 silane coupling agent, and set aside;

[0031] 2) Heat the petroleum base asphalt to 160°C, keep it warm under slow stirring (40r / min) and wait for the next process;

[0032] 3) Add the weighed polycarbosilane powder to the petroleum base asphalt, first stir at a slow speed (40r / min) for 7 minutes, then stir at a medium speed (80r / min) for about 6 minutes until the polycarbosilane powder is evenly dispersed, and obtain mixture A , and wait for the next process under slow stirring (40r / min) state;

[0033] 4) Add the weighed KH792 silane coupling agent into the mixture A, stir at a slow speed for 7 minutes, then stir at a medium speed (80r / min) for about 6 minutes until the silane coupling agent is uniformly dispersed;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a modified asphalt and a preparation method thereof. In parts by weight, the modified asphalt comprises 10-20 parts of polycarbosilane, 5-10 parts of silane coupling agent and 90-100 parts of asphalt. In the present invention, polycarbosilane plus silane coupling agent can be well compatible with asphalt to form a stable homogeneous system without segregation and stratification, which is convenient for storage and transportation; the polycarbosilane precursor has a higher softening point, Good thermal stability and rheological properties can improve the temperature stability of modified asphalt; polycarbosilane has thermosetting properties, and as the temperature rises, it can further undergo cross-linking reaction to form a three-dimensional network structure, making the modified asphalt more effective. Good viscosity, anti-aging ability.

Description

technical field [0001] The invention relates to a modified asphalt and a preparation method thereof, in particular to a polycarbosilane modified asphalt and a preparation method thereof. Background technique [0002] In the past ten years, my country's highway construction has achieved rapid development. As of the end of 2017, the total mileage of national highways reached 4.7735 million kilometers, ranking first in the world. Compared with cement pavement, asphalt pavement has been widely used due to its smooth surface, no joints, comfortable driving, low vibration, low noise, wear resistance, no dust and easy cleaning, short construction period, and easy maintenance and repair. . With the development of our country's economy, the road traffic volume is increasing year by year, and the axle load of vehicles is getting heavier and heavier. The performance requirements of road asphalt are also getting higher and higher. The existing base asphalt has been difficult to meet th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L95/00C08L83/16C08K5/544
Inventor 李九苏黄志轩王潇潇沈增晖李杰张毅张振武尹红星孙玉申
Owner 潮州市金鑫沥青混凝土有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap