Blue light converter, blue light resistant adhesive, blue light resistant tape, and preparation method thereof

A conversion agent and anti-blue light technology, which is applied in chemical instruments and methods, adhesive additives, non-polymer adhesive additives, etc., can solve the problems of glue falling off from the substrate, poor visual effect, environmental pollution, etc., and achieve reduction The effect of improving polarity and adhesion

Active Publication Date: 2019-04-19
NINGBO SOKEN CHEM
View PDF10 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, blue light absorbers such as azo dyes have problems such as environmental pollution and unsatisfactory blue light absorption. There are many hybrid orbitals inside blue light conversion agents such as rare earth fluorescent materials, which easily absorb light of other colors, thereby affecting visual effects. There is a small amount of anti-blue light added. Not ideal, adding a large amount of light easily absorbs other colors, resulting in poor visual effects, and adding such a light transfer agent to the adhesive may easily cause poor adhesion and the glue will fall off from the substrate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Blue light converter, blue light resistant adhesive, blue light resistant tape, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] (1) 0.5 parts of europium carbonate, 3 parts of sodium lauryl sulfate, and 6 parts of 8-hydroxyquinoline were placed in a ball mill for ball milling for 1 hour, and finally vacuum-dried to obtain a blue light conversion agent;

[0036] (2) Add the blue light conversion agent prepared above to 30 parts of ethyl acetate and stir the solvent completely at 40°C, then add the solution to 100 parts of SK-1502D (manufactured by Soken Chemical Co., Ltd.), and stir the solvent for half an hour , and finally add 1.0 parts of cross-linking agent (L-45 (produced by Soken Chemical Co., Ltd.)) and stir for 20 minutes to obtain an anti-blue light adhesive;

[0037] (3) Apply the above-prepared anti-blue light adhesive composition evenly on the release film with a coating thickness of 20 μm, dry it in an 85°C drying oven for 2 minutes, then attach it to the PET black film, and roll it up , to obtain the first engineering product of the adhesive tape;

[0038] (4) Evenly coat the anti-...

Embodiment 2

[0040] (1) 1.0 parts of europium carbonate, 4 parts of sodium lauryl sulfate, and 8 parts of 8-hydroxyquinoline were placed in a ball mill for ball milling. The ball milling time was 1 hour, and finally vacuum-dried to obtain a blue light conversion agent;

[0041] (2) Add the blue light conversion agent prepared above to 20 parts of ethyl acetate and stir the solvent completely at 40°C, then add the solution to 100 parts of SK-1502D (manufactured by Soken Chemical Co., Ltd.), and stir the solvent for half an hour , and finally add 1.5 parts of cross-linking agent (L-45 (produced by Soken Chemical Co., Ltd.)) and stir for 20 minutes to obtain an anti-blue light adhesive.

[0042] (3) Apply the above-prepared anti-blue light adhesive composition evenly on the release film with a coating thickness of 20 μm, dry it in an 85°C drying oven for 2 minutes, then attach it to the PET black film, and roll it up , The first engineering product of the adhesive tape was obtained.

[0043]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a blue light converter, a blue light resistant adhesive, a blue light resistant tape, and a preparation method thereof. The blue light converter is composed of following raw materials in parts by weight: 0.5 to 1.0 part of rare earth compounds, 3 to 5 parts of alkyl compounds, and 6 to 10 parts of quinoline compounds. The preparation method of the blue light converter comprises following steps: adding rare earth compounds, alkyl compounds, and quinoline compounds into a ball mill according to the ratio mentioned above, ball-milling the raw materials, and finally carrying out vacuum drying to obtain the blue light converter. Compared with the prior art, rare earth compounds are modified by the alkyl compounds and quinoline compounds to prepare the novel blue light converter; and solved are the problems that a conventional blue light absorbent pollutes the environment, if the addition amount of a conventional blue light converter is small, the blue light conversion effect is not good, but if the addition amount of the conventional blue light converter is large, the performance of the converter is severely influenced. The invention further provides a high performance blue light resistant adhesive and a blue light resistant tape.

Description

technical field [0001] The invention relates to the technical field of light-shielding tapes, in particular to a blue light conversion agent, an anti-blue light adhesive, an anti-blue light tape and a preparation method thereof. Background technique [0002] The main function of the light-shielding tape is to fix the LCD screen and the backlight module. One of its main functions is to block the excess light leaking from the edge of the optical film. In the ultra-narrow bezel screen design, the width of the light-shielding tape is very narrow, resulting in Part of the light is refracted into the screen through the transparent adhesive layer, causing a bright line to appear on the edge of the screen, which affects the display effect. At the same time, the blue light in the excess light will cause damage to the eyes of the human body. [0003] At present, the anti-blue light materials on the market are mainly realized by adding blue light absorbers or blue light conversion agen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K11/06C07F5/00C09J133/08C09J11/04C09J11/06C09J7/30C09J7/25
CPCC09J7/255C09J7/30C09J11/04C09J11/06C09J133/08C09K11/06C07F5/00C09K2211/182C09J2467/006C09J2433/00C08K3/26C08K5/41C08K5/3437
Inventor 江健波纪照辉吴苗苗
Owner NINGBO SOKEN CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products