Purification type recycled asphalt concrete and preparation process thereof

A technology of recycling asphalt and concrete, which is applied in the field of asphalt concrete processing, can solve the problems of flying dust and poor dust absorption of asphalt concrete, and achieve the effects of protecting the environment, improving dust absorption effect, and rough surface

Active Publication Date: 2019-04-19
SHANGHAI SHISHEN IND & TRADE CO LTD
View PDF7 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the problem in the prior art that asphalt concrete has poor dust-absorbing properties, the road paved with the asphalt concrete is prone to dust flying when vehicles pass by quickly. The first purpose of the present invention is to provide a purified recycled asphalt concrete , by making the purified recycled asphalt concrete have a good void and dust absorption effect to solve the above technical problems, it has a good adsorption effect on the dust on the road, can avoid dust flying, and is conducive to ensuring driving safety and environmental cleanliness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Purification type recycled asphalt concrete and preparation process thereof
  • Purification type recycled asphalt concrete and preparation process thereof
  • Purification type recycled asphalt concrete and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] Example 1: A purified recycled asphalt concrete, the components and their corresponding parts by weight are shown in Table 1, and were prepared through the following steps:

[0047] Step 1: Stir and dry new aggregates, diatomite, steel slag and porous ceramics in corresponding parts by weight in a drying barrel. The temperature is controlled at 100°C, the time is 40min, and the stirring speed is 900rpm to obtain a dry mixed material;

[0048] Step 2, put the dry mixture into the mixing tank, heat 60% by weight of SBS modified asphalt to 160°C, add it into the mixing tank evenly within 30s, and stir at a stirring speed of 1200rpm for 10min;

[0049] Step 3: Preheat the regenerated asphalt mixed old material to 80°C and add it together with the regeneration agent into the above mixing tank for stirring. The temperature in the mixing tank is maintained at 170°C, the stirring speed is 1200rpm, and the time is 25min. Then add the remaining SBS modified asphalt and conducti...

Embodiment 2-8

[0052] Example 2-8: A purification type recycled asphalt concrete, the difference from Example 1 is that each component and its corresponding parts by weight are shown in Table 1.

[0053] Each component and parts by weight thereof in table 1 embodiment 1-8

[0054]

[0055]

Embodiment 9

[0056] Example 9: A purified recycled asphalt concrete, the difference from Example 1 is that the new aggregate mainly consists of particle sizes ranging from 0 to 3mm, 3 to 5mm, 5 to 13mm, 13 to 20mm, and 20 to 25mm The limestone is composed of 1.5:2.5:7.5:1:3.5 in parts by weight.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a purification type recycled asphalt concrete and a preparation process thereof, and relates to the technical field of asphalt concrete processing. The problem is solved that dust flying easily occurs when vehicles drive on a highway paved with asphalt concrete because of the poor dust absorption property of the asphalt concrete. The purification type recycled asphalt concrete is prepared from, by weight, 70-80 parts of new aggregate, 4-6 parts of SBS modified asphalt, 0.2-0.3 part of mineral powder, 18-22 parts of a recycled asphalt mixture, 0.1-0.2 part of a regenerant, 2.5-4.5 parts of whisker filler, 6-8 parts of steel slag, 1.6-1.8 parts of porous ceramic, 1.2-1.6 parts of diatomite and 0.6-0.8 part of conductive carbon fibers. The purification type recycled asphalt concrete has a good adsorption effect on the dust on the highway, dust flying is avoided when vehicles rapidly drive on the highway, the safety of the vehicles in the driving process is ensured,and a certain environment protection effect is achieved.

Description

technical field [0001] The invention relates to the technical field of asphalt concrete processing, in particular to a purified recycled asphalt concrete and a preparation process thereof. Background technique [0002] Asphalt concrete, commonly known as asphalt concrete, is artificially selected with a certain gradation composition of mineral materials, crushed stone or crushed gravel, stone chips or sand, mineral powder, etc., and a certain proportion of road asphalt materials, mixed under strictly controlled conditions made mixture. [0003] A Chinese invention patent with application publication number CN108147728A discloses a rubber asphalt concrete and its preparation method. The raw material components of the rubber asphalt concrete include: 50-60 parts of mineral powder fly ash, 20-30 parts of stone chips, limestone 6-8 parts, 10-15 parts of cement, 5-10 parts of supramolecular rubber composite material, 6-10 parts of asphalt, 2-4 parts of glass fiber, 2-3 parts of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/26
CPCC04B26/26C04B2111/0075C04B2111/94C04B14/28C04B14/08C04B18/027C04B18/142C04B18/12C04B14/4612C04B14/386C04B2103/0068
Inventor 时兆武
Owner SHANGHAI SHISHEN IND & TRADE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com